A reclaimed ceramic starting material is produced from scrap generated in a method for producing a cordierite ceramic body. The scrap is an unnecessary part generated in a cutting step of cutting a dried ceramic molded article into a predetermined length or a defective dried ceramic molded article g

A reclaimed ceramic starting material is produced from scrap generated in a method for producing a cordierite ceramic body. The scrap is an unnecessary part generated in a cutting step of cutting a dried ceramic molded article into a predetermined length or a defective dried ceramic molded article generated in a drying step of drying an extruded ceramic material. The scrap is crushed. From a powder obtaind by crushing, at least particles smaller than the predetermined size are removed to produce a reclaimed powder having a particle size within a predetermined size range. The reclaimed powder is used as a reclaimed ceramic starting material. Instead of crushing, the scrap may be fired at a temperature where a contained binder can burn away to obtain a reclaimed powder. The reclaimed ceramic starting material ensures no deterioration in the quality of a cordierite ceramic body produced therefrom.

대표청구항 ▼

The invention claimed is: 1. A method for producing a cordierite ceramic body, comprising: a mixing step of mixing a ceramic starting material comprising a ceramic virgin starting material and reclaimed powder and a binder to produce a mixed starting material, a humidifying step of adding a humidif

The invention claimed is: 1. A method for producing a cordierite ceramic body, comprising: a mixing step of mixing a ceramic starting material comprising a ceramic virgin starting material and reclaimed powder and a binder to produce a mixed starting material, a humidifying step of adding a humidifying liquid to the mixed starting material to produce a humidified starting material, a molding step of kneading and extruding the humidified starting material to mold a ceramic molded article, a drying step of drying the ceramic molded article, a cutting step of cutting off an unnecessary part of the ceramic molded article after drying and thereby machining the ceramic molded article into a predetermined length, and a calcining step of calcining the ceramic molded article having the predetermined length to produce a ceramic calcined body, wherein the method further comprises a reclaiming step of crushing to a powder the unnecessary part generated in the cutting step and then classifying the crushed powder to remove particles having a particle size less than 1 mm to produce a reclaimed powder composed of particles having a size range of 1 mm to 5 mm, and the reclaimed powder is used at least as a part of the ceramic starting material in the mixing step. 2. A method for producing a cordierite ceramic body according to claim 1, wherein in the mixing step, the content of the reclaimed powder in the ceramic starting material is from 1 to 30 parts by weight based on 100 parts by weight of the virgin starting material. 3. A method for producing a cordierite ceramic body according to claim 1, wherein the cordierite ceramic body has a honeycomb structure.