초록

The magnetic head slider material of the present invention is constituted by a sintered body containing 100 parts by weight of alumina, 20 to 150 parts by weight of titanium carbide and silicon carbide in total, and 0.2 to 9 parts by weight of carbon.

대표청구항 ▼

What is claimed is: 1. A magnetic head slider material constituted by a sintered body containing 100 parts by weight of alumina, 20 to 150 parts by weight of titanium carbide and silicon carbide in total, and 0.2 to 9 parts by weight of carbon. 2. The magnetic head slider material according to cl

What is claimed is: 1. A magnetic head slider material constituted by a sintered body containing 100 parts by weight of alumina, 20 to 150 parts by weight of titanium carbide and silicon carbide in total, and 0.2 to 9 parts by weight of carbon. 2. The magnetic head slider material according to claim 1, wherein the sintered body contains 0.3 to 6 parts by weight of carbon with respect to 100 parts by weight of alumina. 3. The magnetic head slider material according to claim 1, wherein the sintered body contains 0.5 to 3 parts by weight of carbon with respect to 100 parts by weight of alumina. 4. The magnetic head slider material according to claim 1, wherein the sintered body contains 10 to 90 parts by weight of silicon carbide with respect to 100 parts by weight of alumina. 5. The magnetic head slider material according to claim 1, wherein the sintered body contains at least 35 parts by weight of titanium carbide with respect to 100 parts by weight of alumina. 6. A magnetic head slider comprising a substrate made of a sintered body; and a laminate, formed on the substrate, including a thin-film magnetic head; wherein the sintered body contains 100 parts by weight of alumina, 20 to 150 parts by weight of titanium carbide and silicon carbide in total, and 0.2 to 9 parts by weight of carbon. 7. The magnetic head slider according to claim 6, wherein the sintered body contains 0.3 to 6 parts by weight of carbon with respect to 100 parts by weight of alumina. 8. The magnetic head slider according to claim 6, wherein the sintered body contains 0.5 to 3 parts by weight of carbon with respect to 100 parts by weight of alumina. 9. The magnetic head slider according to claim 6, wherein the sintered body contains 10 to 90 parts by weight of silicon carbide with respect to 100 parts by weight of alumina. 10. The magnetic head slider according to claim 6, wherein the sintered body contains at least 35 parts by weight of titanium carbide with respect to 100 parts by weight of alumina. 11. A method of manufacturing a magnetic head slider material, the method comprising the steps of: preparing a molded body containing 100 parts by weight of alumina, 20 to 150 parts by weight of titanium carbide and silicon carbide in total, and 0.2 to 9 parts by weight of carbon; and sintering the molded body in a non-oxidizing atmosphere. 12. The method of manufacturing a magnetic head slider material according to claim 11, wherein the step of preparing the molded body mixes a powder containing alumina, a powder containing titanium carbide, a powder containing silicon carbide, and a powder containing carbon so as to yield a mixed powder, and molds the mixed powder. 13. The method of manufacturing a magnetic head slider material according to claim 11, wherein the step of preparing the molded body mixes a powder containing alumina, a powder containing titanium carbide, a powder containing silicon carbide, and an organic matter so as to yield a mixture, heat-treats the mixture in the non-oxidizing atmosphere so as to carbonize the organic matter in the mixture and yield a mixed powder, and molds the mixed powder. 14. The method of manufacturing a magnetic head slider material according to claim 11, wherein the step of preparing the molded body mixes a powder containing alumina, a powder containing titanium carbide, and an organic matter so as to yield a mixture, molds the mixture, and heat-treats the molded mixture in the non-oxidizing atmosphere so as to carbonize the organic matter in the mixture.