초록 ▼

A method of manufacturing endodontic files involves a chemical milling process to yield endodontic files having a desired taper and/or degree of sharpness. The process involves the steps of (a) forming helical cutting edges in the cutting portion of the metallic rod; and (b) chemically milling the c

A method of manufacturing endodontic files involves a chemical milling process to yield endodontic files having a desired taper and/or degree of sharpness. The process involves the steps of (a) forming helical cutting edges in the cutting portion of the metallic rod; and (b) chemically milling the cutting portion of the rod so as to sharpen and/or taper the cutting portion. The rod may be formed of any desirable metallic material, for example stainless steel or a nickel-titanium alloy. The cutting edges may be formed by torsioning, cutting, grinding, machining, laser micromachining, or grit blasting.

대표청구항 ▼

What is claimed is: 1. A method of manufacturing an endodontic instrument for use in performing an endodontic procedure, comprising: (a) providing an intermediate instrument comprised of a metal and having a cutting portion; (b) providing a chemical milling composition that chemically strips metal

What is claimed is: 1. A method of manufacturing an endodontic instrument for use in performing an endodontic procedure, comprising: (a) providing an intermediate instrument comprised of a metal and having a cutting portion; (b) providing a chemical milling composition that chemically strips metal from a surface of a metallic substrate as result of chemical action of the chemical milling composition; and (c) chemically milling at least a portion of said cutting portion by contacting at least a portion of said cutting portion with said chemical milling composition so as to chemically strip metal from an entire surface of the portion of said cutting portion in contact with said chemical milling composition so as to yield an endodontic instrument having a desired taper and/or cutting edges having a desired degree of sharpness and/or a more contiguous surface with fewer microfissures or cracks. 2. The method as recited in claim 1, wherein (c) is performed by progressively inserting and/or withdrawing said cutting portion into and/or from said chemical milling composition at a predetermined rate. 3. The method as recited in claim 2, further comprising soaking at least said cutting portion in said chemical milling composition for a predetermined soak time of between about 1 minute and about 60 minutes. 4. The method as recited in claim 2, wherein said cutting portion of said rod is inserted into and/or withdrawn from said chemical milling composition at a rate of between about 0.1 mm per minute and about 6 mm per minute. 5. The method as recited in claim 2, wherein said cutting portion of said rod is inserted into and/or withdrawn from said chemical milling composition at a rate of between about 0.5 mm per minute and about 3 mm per minute. 6. The method as recited in claim 2, wherein said cutting portion of said rod is inserted into and/or withdrawn from said chemical milling composition at a rate of between about 0.8 mm per minute and about 1.2 mm per minute. 7. The method as recited in claim 1, wherein said chemical milling composition is acidic. 8. The method as recited in claim 7, wherein said chemical milling composition comprises hydrofluoric acid, nitric acid, water, and a wetting agent. 9. The method as recited in claim 1, wherein at least a portion of said cutting portion is formed by machining or grinding a metallic rod so as to form said cutting edges in said cutting portion. 10. The method as recited in claim 1, wherein at least a portion of said cutting portion is formed by at least one of cutting, grinding, laser micromachining, machining, or grit blasting. 11. The method as recited in claim 1, wherein at least a portion of said cutting portion is formed by torsioning a metallic rod having a polygonal cross section so as to form helical cutting edges in said cutting portion. 12. The method as recited in claim 1, wherein (c) produces a cutting portion taper of between about 0.02 mm/mm and about 0.06 mm/mm. 13. The method as recited in claim 1, wherein (c) sharpens said cuffing edges as they are chemically milled. 14. The method as recited in claim 1, wherein (c) does not result in significant tapering of said endodontic instrument. 15. The method as recited in claim 1, wherein said intermediate instrument having a cutting portion is tapered prior to (c). 16. The method as recited in claim 1, wherein (c) further comprises passing an electric current through at least one of said intermediate instrument or said chemical milling composition. 17. The method as recited in claim 1, wherein (c) comprises chemically milling a plurality of intermediate instruments simultaneously. 18. A method of manufacturing an endodontic instrument adapted for use in performing an endodontic procedure, comprising: (a) providing a metallic rod; (b) forming said rod into an intermediate endodontic instrument having a cutting portion comprised of at least one helical cutting edge; and (c) chemically milling at least a portion of said cutting portion of said intermediate endodontic instrument by contacting at least a portion of said cutting portion with a chemical milling composition in order to chemically strip metal from an entire surface of the portion of said cutting portion in contact with said chemical milling composition so as to sharpen said at least one helical cutting edge and/or taper said cutting portion and/or remove microfissures or cracks in said cutting portion. 19. The method as recited in claim 18, wherein said rod is formed of a nickel-titanium alloy. 20. A method of manufacturing an endodontic instrument adapted for use in performing an endodontic procedure, comprising: (a) providing a metallic rod having a polygonal cross section; (b) torsioning, grinding and/or machining said rod so as to form an intermediate endodontic instrument having a cutting portion comprised of at least one helical cutting edge in said cutting portion; and (c) chemically milling at least a portion of said cutting portion of said intermediate endodontic instrument by contacting at least a portion of said cuffing portion with a chemical milling composition in order to chemically strip metal from an entire surface of the portion of said cutting portion in contact with said chemical milling composition so as to sharpen said at least one helical cutting edge and/or taper said cutting portion and/or remove microfissures or cracks in said cutting portion.