Meta-and para-aramid pulp and processes of making same
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
D21H-013/26
D21H-013/00
출원번호
US-0877860
(2004-06-25)
등록번호
US-7455750
(2008-11-25)
발명자
/ 주소
Conley,Jill A.
Lundblad,Lenard Oscar
Merriman,Edmund A.
출원인 / 주소
E.I. du Pont de Nemours and Company
인용정보
피인용 횟수 :
5인용 특허 :
11
초록▼
The present invention relates to meta-and para-aramid pulp for use as reinforcement material in products such as seals and friction materials. The pulp comprises (a) fibril free meta-aramid particles, (b) irregularly shaped, para-aramid fibrous structures, and (c) water, whereby the para-aramid fib
The present invention relates to meta-and para-aramid pulp for use as reinforcement material in products such as seals and friction materials. The pulp comprises (a) fibril free meta-aramid particles, (b) irregularly shaped, para-aramid fibrous structures, and (c) water, whereby the para-aramid fibrous structures contact and are wrapped partially around at least some of the meta-aramid particles. The invention further relates to processes for making such aramid pulp.
대표청구항▼
What is claimed is: 1. A process for making a meta-and para-aramid pulp for use as reinforcement material, comprising: (a) combining pulp ingredients including: (1) pieces of fibrous meta-aramid material, wherein the fibrous meta-aramid material is uncalendered paper having a thickness of 2 to 40 m
What is claimed is: 1. A process for making a meta-and para-aramid pulp for use as reinforcement material, comprising: (a) combining pulp ingredients including: (1) pieces of fibrous meta-aramid material, wherein the fibrous meta-aramid material is uncalendered paper having a thickness of 2 to 40 mils and a density of 0.1 to 0.4 g/cm3, being 10 to 90 wt % of the total solids in the ingredients, and having an average maximum dimension of no more than 50 mm; (2) para-aramid fiber being 10 to 90 wt % of the total solids in the ingredients, and having an average length of no more than 10 cm; and (3) water being 95 to 99 wt % of the total ingredients; (b) mixing the ingredients to a substantially uniform slurry; (c) co-refining the slurry by simultaneously: (1) breaking apart the fibrous meta-aramid material pieces, and cutting and/or masticating the meta-aramid material, into fibril free, fibrous and non fibrous, meta-aramid particles; (2) fibrillating, cutting and masticating the para-aramid fiber to irregularly shaped fibrillated fibrous structures; and (3) dispersing all solids such that the refined slurry is substantially uniform; and (d) removing water from the refined slurry to no more than 60 total wt % water, thereby producing a meta-and para-aramid pulp with the para-aramid fibrous structures contacting and wrapped partially around at least some of the meta-aramid particles. 2. The process of claim 1, wherein the fibrous meta-aramid material comprises pieces of fibrous meta-aramid paper which comprise paper components including: (i) meta-aramid fiber being 10 to 90 wt % of the paper, and having a length of 2 to 25 mm; and (ii) non granular, fibrous or film-like, meta-aramid fibrids being 90 to 10 wt % of the paper, and having an average maximum dimension of 0.2 to 1 mm, an aspect ratio of 5:1 to 10:1, and a thickness of no more than 2 microns. 3. The process of claim 1, wherein the ingredients further comprise: substantially or completely fibril-free, granular, para-aramid particles being no more than 50 wt % of the total solids in the ingredients, and having an average maximum dimension of 50 to 2000 microns; and in the refining step, masticating at least some of the para-aramid particles into smaller, rounder, substantially fibril-free, particles, whereby in the produced meta-and para-aramid pulp, the para-aramid fibrous structures contact and are wrapped partially around at least some of the rounder, substantially fibril-free, para-aramid particles. 4. A process for making a meta-and para-aramid pulp for use as reinforcement material, comprising: (a) combining ingredients including water and a first material of the group: (1) pieces of fibrous meta-aramid material, wherein the fibrous meta-aramid material is uncalendered paper having a thickness of 2 to 40 mils and a density of 0.1 to 0.4 g/cm3, being 10 to 90 wt % of the total solids in the pulp, and having an average maximum dimension of no more than 50 mm; and (2) para-aramid fiber being 10 to 90 wt % of the total solids in the pulps, and having an average length of no more than 10 cm; (b) mixing the ingredients to a substantially uniform suspension; (c) refining the mixed suspension by: (1) breaking apart at least some of the fibrous meta-aramid material pieces, and cutting and/or masticating at least some of the meta-aramid material, into fibril free, meta-aramid particles; or (2) fibrillating, cutting and masticating at least some of the para-aramid fiber to irregularly shaped fibrillated fibrous structures; (d) combining ingredients including the refined suspension, the second material of the group of (a) (1 and 2), and water, if necessary, to increase the water concentration to 95-99 wt % of the total ingredients; (e) mixing the ingredients, if necessary, to form a substantially uniform slurry; (f) co-refining the slurry by simultaneously: (1) breaking apart at least some of the fibrous meta-aramid material pieces and/or cutting and/or masticating at least some of the meta-aramid material, such that all or substantially all of the fibrous meta-aramid material pieces are converted into fibril free, meta-aramid particles; and (2) fibrillating, cutting and masticating at least some of the para-aramid fiber such that all or substantially all of the para-aramid fiber is converted to irregularly shaped fibrillated fibrous structures; and (3) dispersing all solids such that the refined slurry is substantially uniform; and (g) removing water from the refined slurry to no more than 60 total wt % water, thereby producing a meta-and para-aramid pulp with the para-aramid fibrous structures contacting and wrapped partially around at least some of the meta-aramid particles. 5. The process of claim 4, wherein the fibrous meta-aramid material comprises pieces of fibrous meta-aramid paper which comprise paper components including: (i) meta-aramid fiber being 5 to 97 wt % of the paper, and having a linear density of 1 to 10 dtex and a length of 2 to 25 mm; and (ii) non granular, fibrous or film-like, meta-aramid fibrids being 95 to 3 wt % of the paper, and having an average maximum dimension of 0.2 to 1 mm, an aspect ratio of 5:1 to 10:1, and a thickness of no more than 1 micron. 6. The process of claim 4, wherein the ingredients further comprise: substantially or completely fibril-free, granular, para-aramid particles being no more than 50 wt % of the total solids in the ingredients, and having an average maximum dimension of 50 to 2000 microns; and in either the first or second refining step, masticating at least some of the para-aramid particles into smaller, rounder, substantially fibril-free, particles, whereby in the produced meta-and para-aramid pulp, the para-aramid fibrous structures contact and are wrapped partially around at least some of the rounder, substantially fibril-free, para-aramid particles.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (11)
Ramachandran Seshadri ; Allen Ronnie Aaron, Aramid dispersions and aramid sheets of increased uniformity.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.