초록 ▼

The present invention provides methods and materials for use in applying a coating on a surface of a magnesium component. The method includes the steps of: accelerating a coating powder to a velocity of between about 500 to about 1200 meters/second, wherein the coating powder comprises a material se

The present invention provides methods and materials for use in applying a coating on a surface of a magnesium component. The method includes the steps of: accelerating a coating powder to a velocity of between about 500 to about 1200 meters/second, wherein the coating powder comprises a material selected from the group consisting of aluminum, aluminum alloys, titanium, titanium alloys, and composites; directing the coating powder through a convergent-divergent nozzle onto the surface of the magnesium component; and forming a coating on the surface of the magnesium component so as to substantially cover the surface of the magnesium component. The coating thickness may be between approximately 0.1 to approximately 1.0 mm.

대표청구항 ▼

What is claimed is: 1. A method of applying a coating on a surface of a magnesium component, the method comprising the steps of: accelerating a coating powder to a velocity of between about 500 to about 1200 meters/second and directing the coating powder through a convergent-divergent nozzle onto t

What is claimed is: 1. A method of applying a coating on a surface of a magnesium component, the method comprising the steps of: accelerating a coating powder to a velocity of between about 500 to about 1200 meters/second and directing the coating powder through a convergent-divergent nozzle onto the surface of the magnesium component to form a layer of aluminum thereover; and depositing additional coating materials over the layer of aluminum by accelerating the additional coating materials to a velocity of between about 500 to about 1200 meters/second and directing the additional coating materials through the convergent-divergent nozzle over the layer of aluminum forming a laminate on the surface of the magnesium component so as to substantially cover the surface of the magnesium component, the laminate having an outer layer of titanium. 2. The method according to claim 1 wherein the coating is up to approximately 20 mm in thickness. 3. The method according to claim 1 further comprising the step of heating the coating powder to a temperature of between about 250�� F. and about 750�� F. 4. The method according to claim 1 farther comprising the step of providing coating powder at a powder feed rate of about 0.01 to about 20 grams/second-cm2, before the step of accelerating. 5. The method according to claim 1 farther comprising the step of preparing the surface of the magnesium component by an operation comprising a method selected from the group consisting of grinding, degreasing, and grit blasting. 6. The method according to claim 1 wherein the step of accelerating a coating powder further comprises accelerating a coating powder with a gas comprising helium. 7. A method for coating a surface of a magnesium component comprising the steps of: providing a magnesium component with a surface; inspecting the magnesium component for suitability for cold spraying; preparing the surface of the magnesium component; and applying a coating onto the surface of the magnesium component by cold spraying so as to substantially cover the surface of the magnesium component with the coating, the coating comprising a laminate including a layer of aluminum over the magnesium component and an outer layer of titanium over the layer of aluminum. 8. The method according to claim 7 wherein the step of applying a coating onto the surface of the magnesium component produces a coated component, and further comprising heat treating the coated component wherein the step of heat treating the coated component comprises heating the coated component at approximately 600�� F. to approximately 725�� F. for approximately 0.5 to approximately 2 hours, cooling the coated component, and then heating the coated component to approximately 250�� F. to approximately 425�� F. for approximately 4 to approximately 16 hours. 9. The method according to claim 7 further comprising inspecting the coated component by x-ray inspection or FPI inspection. 10. A method of applying a coating on a surface of a magnesium component, the method comprising the steps of: accelerating a coating powder to a velocity of between about 500 to about 1200 meters/second and directing the coating powder through a convergent-divergent nozzle onto the surface of the magnesium component to form a layer of aluminum thereover; and depositing additional coating materials over the layer of aluminum by accelerating the additional coating materials to a velocity of between about 500 to about 1200 meters/second and directing the additional coating materials through the convergent-divergent nozzle over the layer of aluminum forming a laminate on the surface of the magnesium component so as to substantially cover the surface of the magnesium component, the laminate having an outer layer of a material selected from the group consisting of titanium, titanium alloys, iron, iron alloys, copper, copper alloys, nickel, nickel alloys, and composites. 11. The method according to claim 10 wherein the coating is up to approximately 20 mm in thickness. 12. The method according to claim 10 further comprising the step of heating the coating powder to a temperature of between about 250�� F. and about 750�� F.