초록 ▼

New nonwoven fibrous webs are taught which comprise a collected mass of a) directly formed fibers disposed within the web in a C-shaped cross-sectional configuration and b) staple fibers having a crimp of at least 15% dispersed among the directly formed fibers in an amount of at least 5% the weight

New nonwoven fibrous webs are taught which comprise a collected mass of a) directly formed fibers disposed within the web in a C-shaped cross-sectional configuration and b) staple fibers having a crimp of at least 15% dispersed among the directly formed fibers in an amount of at least 5% the weight of the directly formed fibers. The web is lofty but free of macrovoids. Preferably, the web has a filling ratio of at least 50 and a light transmittance variation of about 2% or less. Typically, fibers within the web are bonded together at points of fiber intersection, preferably with autogenous bonds, to provide a compression-resistant matrix. The webs are especially useful as acoustic and thermal insulation.

대표청구항 ▼

What is claimed is: 1. A nonwoven fibrous web comprising a collected mass of directly formed fibers disposed within the web in a C-shaped configuration, and staple fibers having a crimp of at least 15% randomly and thoroughly dispersed among the directly formed fibers in an amount at least 5% the w

What is claimed is: 1. A nonwoven fibrous web comprising a collected mass of directly formed fibers disposed within the web in a C-shaped configuration, and staple fibers having a crimp of at least 15% randomly and thoroughly dispersed among the directly formed fibers in an amount at least 5% the weight of the directly formed fibers to form a continuous, lofty and resilient web structure free of macrovoids. 2. A web of claim 1 having an initial filling ratio of at least 50. 3. A web of claim 1 having an initial filling ratio of at least 75. 4. A web of claim 1 having an initial filling ratio of at least 100. 5. A web of claim I having a light transmittance variation of about 2% or less. 6. A web of claim 1 having a light transmittance variation of about 1% or less. 7. A web of claim 1 having a light transmittance variation of about 0.5% or less. 8. A web of claim 1 in which fibers within the web are bonded together at points of fiber intersection to provide a compression-resistant matrix. 9. A web of claim 8 in which the bonds are autogenous bonds. 10. A web of claim 1 in which the directly formed fibers have an average geometric diameter of about 15 micrometers or less. 11. A web of claim 1 in which the directly formed fibers have an average geometric diameter of about 10 micrometers or less. 12. A web of claim 1 in which the staple fibers are present in an amount at least 10% the weight of the directly formed fibers. 13. A web of claim 1 in which the staple fibers are present in an amount at least 20% the weight of the directly formed fibers. 14. A web of claim 1 in which the directly formed fibers comprise meltblown fibers. 15. A web of claim 1 in which the directly formed fibers comprise polyethylene terephthalate fibers that exhibit a double melting peak on a DSC plot, one peak being representative of a first molecular portion within the fiber that is in non-chain-extended form, and the other peak being representative of a second molecular portion within the fiber that is in chain-extended form and has a melting point elevated over that of the non-chain-extended form. 16. A web of claim 1 in which the directly formed fibers comprise meltspun fibers. 17. A fibrous web of claim 1 having a thickness of at least about 0.5 centimeter, a density of less than about 50 kg/m3, and an acoustical specific airflow resistance of at least 100 mks rayl. 18. A web of claim 1 joined to a supporting sheet. 19. A nonwoven fibrous web comprising a collected mass of directly formed fibers disposed within the web in a C-shaped configuration, and crimped staple fibers having a crimp of at least 15% randomly and thoroughly dispersed among the directly formed fibers in an amount at least 10% the weight of the directly formed fibers to form a continuous, lofty and resilient web structure free of macrovoids, the web having a filling ratio of at least 75 and a light transmittance variation of about 1% or less. 20. A web of claim 19 having a filling ratio of at least 100. 21. A web of claim 19 having a light transmittance variation of about 0.5% or less. 22. A fibrous web of claim 19 in which the directly formed fibers have an average geometric diameter of about 15 micrometers or less. 23. A fibrous web of claim 19 in which the directly formed fibers comprise meltblown microfibers. 24. A fibrous web of claim 19 in which the directly formed fibers comprise molecularly oriented meltspun fibers.