초록 ▼

A method for producing a bottle-shaped container that is highly thermally resistant and shows an excellent shaping/shape-keeping property in a short period of time is provided. The method for producing the bottle-shaped container mainly made of polyethylene terephthalate comprises the steps of: firs

A method for producing a bottle-shaped container that is highly thermally resistant and shows an excellent shaping/shape-keeping property in a short period of time is provided. The method for producing the bottle-shaped container mainly made of polyethylene terephthalate comprises the steps of: first biaxially-oriented blow-molding a preform mainly made of polyethylene terephthalate in a first metal mold, to form a primary intermediate molded article; causing thermal contraction of the primary intermediate molded aritcle by heating the primary intermediate molded article, to form a secondary intermediate molded article; and second blow-molding the secondary intermediate molded article in a second metal mold, to form the bottle-shaped container, characterized in that in the second biaxially-oriented blow-molding step, fluid is blown into the secondary intermediate molded article to expand the secondary intermediate article, and then further fluid is blown into and circulated in the expanded article to cool the expanded article.

대표청구항 ▼

What is claimed is: 1. A method for producing a bottle-shaped container mainly made of polyethylene terephthalate, comprising the steps of: first biaxially-oriented blow-molding a preform mainly made of polyethylene terephthalate in a first metal mold, to form a primary intermediate molded article,

What is claimed is: 1. A method for producing a bottle-shaped container mainly made of polyethylene terephthalate, comprising the steps of: first biaxially-oriented blow-molding a preform mainly made of polyethylene terephthalate in a first metal mold, to form a primary intermediate molded article, causing thermal contraction of the primary intermediate molded article by heating the primary intermediate molded article, to form a secondary intermediate molded article, and second blow-molding the secondary intermediate molded article in a second metal mold, to form the bottle-shaped container, characterized in that in the second biaxially-oriented blow-molding step, fluid under high pressure is blown into the secondary intermediate molded article to expand the secondary intermediate article, and then further fluid is blown into and circulated in the expanded article to cool the expanded article, so as to minimize the high pressure blow time. 2. The method according to claim 1, wherein said first biaxially-oriented blow-molding is realized by blowing fluid under high pressure into the preform so as to minimize the high pressure blow time. 3. The method according to claim 1, wherein said high pressure blow time is a period of time suitable for providing a good shaping/shape-keeping property. 4. The method according to claim 1, wherein said high pressure blow time is a period of time suitable for providing a good shaping/shape-keeping property. 5. The method according to claim 1, wherein high pressure is greater than 20 Mpa. 6. The method according to claim 1, wherein high pressure is greater than 25.3 Mpa. 7. A method for producing a bottle-shaped container mainly made of polyethylene terephthalate, comprising the steps of: first biaxially-oriented blow-molding a preform mainly made of polyethylene terephthalate in a first metal mold, to form a primary intermediate molded article, causing thermal contraction of the primary intermediate molded article by heating the primary intermediate molded article, to form a secondary intermediate molded article, and second blow-molding the secondary intermediate molded article in a second metal mold, to form the bottle-shaped container, characterized in that in the second biaxially-oriented blow-molding step, fluid is blown into the secondary intermediate molded article to expand the secondary intermediate article, and further fluid is blown into and circulated in the expanded article; wherein said first biaxially-oriented blow-molding is realized by blowing fluid under high pressure into the preform so as to minimize the high pressure blow time. 8. The method according to claim 7, wherein said high pressure blow time is a period of time suitable for providing a good shaping/shape-keeping property. 9. The method according to claim 7, wherein high pressure is greater than 20 MPa. 10. The method according to claim 1, wherein high pressure is greater than 25.3 MPa.