초록 ▼

The present invention provides polarized electrodes that ensure a satisfactory packing ratio of activated carbon particles and conductive particulates and favorable contact between these and an electrolyte, and demonstrate high capacitance. The present invention relates to the following electrode ma

The present invention provides polarized electrodes that ensure a satisfactory packing ratio of activated carbon particles and conductive particulates and favorable contact between these and an electrolyte, and demonstrate high capacitance. The present invention relates to the following electrode materials for polarized electrodes: (1) electrode materials for polarized electrodes containing a rubber-based emulsion, activated carbon particles, conductive particulates, and a surfactant; and (2) electrode materials for polarized electrodes containing a dispersion of polytetrafluoroethylene, activated carbon particles, conductive particulates, and a surfactant, wherein the solid content is 25% by weight or more.

대표청구항 ▼

The invention claimed is: 1. A method for preparing an electrode material for a polarized electrode, the method comprising: a first step of dispersing conductive particles and a surfactant in water; a subsequent second step of dispersing activated carbon particles, different from the conductive par

The invention claimed is: 1. A method for preparing an electrode material for a polarized electrode, the method comprising: a first step of dispersing conductive particles and a surfactant in water; a subsequent second step of dispersing activated carbon particles, different from the conductive particles, in the dispersion obtained in the first step; and a third step of mixing a binder comprising a rubber containing emulsion or a dispersion of polytetrafluoroethylene in the dispersion obtained in the second step. 2. A preparation method according to claim 1, wherein at least two types of activated carbon particles with different mean particle diameters are used. 3. A preparation method according to claim 2, wherein the at least two types of activated carbon particles are dispersed in the dispersion in the second step in the order such that the type of activated carbon particles with the smallest mean particle diameter is dispersed first, and then a) the other type of activated carbon particles is dispersed or b) the other types of activated carbon particles are dispersed in order of their increasing mean particle diameter. 4. A method according to claim 1, wherein the conductive particles have a mean particle diameter of 0.01-20 μm. 5. A method according to claim 2, wherein the next smallest activated carbon particles have a mean particle diameter which is three times that of the smallest activated carbon particles. 6. A method according to claim 1, wherein the mixed dispersion obtained in the third step is flowable and has a solid content of 25% by weight or more. 7. A method according to claim 1, further comprising a fourth step of applying the mixed dispersion obtained in the third step on a substrate, followed by drying. 8. The method of claim 1, further comprising a fourth step of drying the electrode material to substantially remove the water, thereby generating voids between at least a portion of the binder and the activated carbon.