IPC분류정보
| 국가/구분 |
United States(US) Patent
등록
|
| 국제특허분류(IPC7판) |
|
| 출원번호 |
UP-0551728
(2004-04-23)
|
| 등록번호 |
US-7528087
(2009-07-01)
|
| 국제출원번호 |
PCT/US04/012740
(2004-04-23)
|
| §371/§102 date |
20051003
(20051003)
|
| 국제공개번호 |
WO04/096729
(2004-11-11)
|
|
발명자
/ 주소 |
- Saha, Chandan
- Allen, Sharon
- Han, Chan
- Nilsson, Robert T.
- Prunier, Jr., Arthur R.
- Pyzik, Aleksander J.
- Wallin, Sten A.
- Ziebarth, Robin
- Gallagher, Timothy J.
|
| 출원인 / 주소 |
- Dow Global Technologies, Inc.
|
| 인용정보 |
피인용 횟수 :
4 인용 특허 :
24 |
초록
▼
A porous mullite composition is made by Forming a mixture of one or more precursor compounds having the elements present in mullite (e.g., clay, alumina, silica) and a property enhancing compound. The property enhancing compound is a compound having an element selected from the group consisting of M
A porous mullite composition is made by Forming a mixture of one or more precursor compounds having the elements present in mullite (e.g., clay, alumina, silica) and a property enhancing compound. The property enhancing compound is a compound having an element selected from the group consisting of Mg, Ca, Fe, Na, K, Ce, Pr, Nd, Sm, Eu, Gd, Th, Dy, Ho, Er, Tm, Yb, Lu, B, Y, Sc, La and combination thereof. The mixture is shaped and to form a porous green shape which is heated under an atmosphere having a fluorine containing gas to a temperature sufficient to form a mullite composition comprised substantially of acicular mullite grains that are essentially chemically bound.
대표청구항
▼
What is claimed is: 1. A method for preparing a porous acicular mullite composition having an improved thermal shock factor, the method comprising, a) forming a mixture of one or more precursor compounds having the elements present in mullite and a property enhancing compound comprising talc, b) sh
What is claimed is: 1. A method for preparing a porous acicular mullite composition having an improved thermal shock factor, the method comprising, a) forming a mixture of one or more precursor compounds having the elements present in mullite and a property enhancing compound comprising talc, b) shaping the mixture into a porous green shape, c) heating the porous green shape of step (b) under an atmosphere having a fluorine containing gas and to a temperature sufficient to form a mullite composition comprised substantially of acicular mullite grains that are essentially chemically bound, wherein an element of the property enhancing compound is incorporated into a glassy grain interface phase of the porous acicular mullite composition. 2. The method of claim 1 wherein the property enhancing compound is talc. 3. A method for preparing a porous acicular mullite composition having an improved thermal shock factor, the method comprising, a) forming a mixture of one or more precursor compounds having the elements present in mullite and a property enhancing compound, the property enhancing compound containing an element selected from the group consisting of Mg, Ca, Fe, Na, K, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, B, Y, Sc, La and combination thereof. b) shaping the mixture into a porous green shape, c) heating the porous green shape of step (b) under an atmosphere having a fluorine containing gas and to a temperature sufficient to form a mullite composition is comprised substantially of acicular mullite grains that are essentially chemically bound and said mullite composition has a ratio of Nd/Mg from about 0.1 to about 10 by weight. 4. A method for preparing a porous acicular mullite composition having an improved thermal shock factor, the method comprising, a) forming a mixture of one or more precursor compounds having the elements present in mullite and a property enhancing compound, the property enhancing compound containing an element selected from the group consisting of Mg, Ca, Fe, Na, K, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, B, Y, Sc, La and combination thereof. b) shaping the mixture into a porous green shape, c) heating the porous green shape of step (b) under an atmosphere having a fluorine containing gas and to a temperature sufficient to form a mullite composition comprised substantially of acicular mullite grains that are essentially chemically bound and said mullite composition has a ratio of Fe/Mg from about 0.5 to about 1.5 by weight the Fe and Mg being present as oxides. 5. The method of claim 4, wherein the Fe and Mg are present in an amorphous oxide glassy phase. 6. The method of claim 3, wherein an element of the property enhancing compound is incorporated into a glassy grain interface phase of the porous acicular mullite composition. 7. The method of claim 4, wherein an element of the property enhancing compound is incorporated into a glassy grain interface phase of the porous acicular mullite composition.