초록 ▼

A method of forming a ceramic matrix composite (CMC) article (30) or a composite article (60) that minimizes the risk of delaminations while simultaneously maintaining a desired degree of porosity in the material. A pressure P applied against a surface of the article during a sintering process is co

A method of forming a ceramic matrix composite (CMC) article (30) or a composite article (60) that minimizes the risk of delaminations while simultaneously maintaining a desired degree of porosity in the material. A pressure P applied against a surface of the article during a sintering process is controlled to be high enough to resist a separation force between the plies (66) of the CMC material (62) caused by anisotropic shrinkage of the material and/or to resist a separation force caused by differential shrinkage between the CMC material and an adjoined monolithic ceramic material (64). The pressure is also controlled to be low enough to avoid undue consolidation of the materials and to provide a desired degree of porosity in the sintered article. The pressure may be applied by delta-alpha tooling, and it may be varied verses the time of the sintering heating and/or across the article surface.

대표청구항 ▼

The invention claimed is: 1. A method of manufacturing a ceramic matrix composite article, the method comprising: forming a ceramic matrix composite article by stacking a plurality of plies of oxide-oxide ceramic matrix composite material, surfaces of adjacent plies making contact to define a combi

The invention claimed is: 1. A method of manufacturing a ceramic matrix composite article, the method comprising: forming a ceramic matrix composite article by stacking a plurality of plies of oxide-oxide ceramic matrix composite material, surfaces of adjacent plies making contact to define a combined thru-thickness dimension; heating the article to a sintering temperature while applying a thru-thickness pressure against the article; controlling the pressure during the heating to a level sufficiently high to oppose a separation force developed between adjacent plies by anisotropic shrinkage of the plies in order to maintain contact between respective contacting surfaces; and controlling the pressure during the heating to a level sufficiently low within a range of greater than 50 psig to less than 750 psig to maintain a desired level of porosity within the article. 2. The method of claim 1, further comprising controlling the pressure during the heating to a value generating a thru-thickness force at least equal to the separation force and no more than 10 times the separation force. 3. The method of claim 1, further comprising controlling the pressure to a value generating a thru-thickness force in the range of 3-7 times the separation force. 4. The method of claim 1, further comprising controlling the pressure during the heating to a level sufficiently low to maintain porosity within a range of 10-30%. 5. The method of claim 1, further comprising controlling the pressure during the heating to a level sufficiently low to maintain porosity within a range of 15-25%. 6. The method of claim 1, further comprising controlling the pressure during the heating to within a range of greater than 50 psig to less than 750 psig. 7. The method of claim 1, further comprising controlling the pressure during the heating to within a range of greater than 100 psig to less than 500 psig. 8. The method of claim 1, further comprising controlling the pressure during the heating to within a range of greater than 200 psig to less than 500 psig. 9. The method of claim 1, further comprising: forming the plies of alumino-silicate fibers in an alumina-containing matrix; and controlling the pressure during the heating to a range of values that is effective to produce a sintered ceramic matrix composite article exhibiting interlaminar tensile strength of greater than 7 MPa while maintaining in-plane tensile strength of at least 140 MPa. 10. The method of claim 1, further comprising applying the pressure by: positioning the article at least partially within portions of a first tooling member exhibiting a first coefficient of thermal expansion; disposing a second tooling member exhibiting a second coefficient of thermal expansion higher than the first coefficient of thermal expansion between the first tooling member and the article; and heating the article, the first tooling member and the second tooling member together to cause relatively greater expansion of the second tooling member compared to expansion of the first tooling member, thereby exerting the thru-thickness pressure against the article. 11. The method of claim 1, further comprising varying the pressure verses time during the heating. 12. The method of claim 1, further comprising varying the pressure across a surface of the article. 13. A method of manufacturing a composite article, the method comprising: adjoining a surface of a ceramic matrix composite material to a surface of a monolithic ceramic material to form a composite article; applying pressure to urge the adjoined surfaces together while heating the composite article to a sintering temperature to bond the ceramic matrix composite material to the monolithic ceramic material along the adjoined surfaces; applying the pressure to a level sufficiently high to overcome a separation force tending to separate the adjoining surfaces resulting from differential shrinkage between the ceramic matrix composite material and the monolithic ceramic material; limiting the pressure to a level sufficiently low to maintain a desired level of porosity within at least one of the ceramic matrix composite material and the monolithic ceramic material; and controlling the pressure to be responsive to actual shrinkage of the composite article. 14. The method of claim 13, further comprising controlling the pressure during the heating to a value generating a force at least equal to the separation force and no more than 10 times the separation force. 15. The method of claim 13, further comprising controlling the pressure during the heating to a level sufficiently low to maintain porosity within the at least one of the ceramic matrix composite material and the monolithic ceramic material to within a range of 10-30%. 16. The method of claim 13, further comprising controlling the pressure during the heating to within a range of greater than 50 psig to less than 750 psig. 17. The method of claim 13, wherein the ceramic matrix composite material comprises multiple plies of reinforcing fabric disposed in matrix material, and wherein the adjoined surfaces comprise a non-planar region, and further comprising: applying the pressure to a level sufficiently high to overcome a first separation force tending to separate the adjoining surfaces and to overcome a second separation force tending to separate adjoining plies of the ceramic matrix composite material and effective to prevent delamination in the non-planar region; and limiting the pressure to a level sufficiently low to maintain a desired level of porosity within the ceramic matrix composite material of at least 10%.