초록 ▼

In a process of fabricating a stent composed primarily of niobium alloyed with a trace amount of zirconium, tantalum, or titanium for hardening, the stent is annealed under vacuum in a substantially oxygen-free environment. The vacuum is preferably maintained at pressure less than 10-4 millibars, ox

In a process of fabricating a stent composed primarily of niobium alloyed with a trace amount of zirconium, tantalum, or titanium for hardening, the stent is annealed under vacuum in a substantially oxygen-free environment. The vacuum is preferably maintained at pressure less than 10-4 millibars, oxygen-content less than about 80 parts per million, and the annealing temperature exceeds 400° C. for at least one hour, and is preferably kept in a range from about 1100-1200° C. for several hours. This may be followed by applying a surface layer of oxide, such as iridium oxide, with a thickness of 299-300 nm to the stent.

대표청구항 ▼

What is claimed is: 1. A process for fabricating a stent comprising: producing a stent from a tube composed principally of niobium with a trace of additional metal for alloy formation and reinforcement, the production of the stent including a step of annealing the tube under vacuum in a substantial

What is claimed is: 1. A process for fabricating a stent comprising: producing a stent from a tube composed principally of niobium with a trace of additional metal for alloy formation and reinforcement, the production of the stent including a step of annealing the tube under vacuum in a substantially oxygen-free environment, wherein producing the stent comprises mechanical and chemical finishing of the tube, wherein the stent comprises a network of interconnected struts. 2. The process of claim 1, wherein the trace metal is selected from a group including zirconium, tantalum and titanium, and said trace is less than approximately 5%. 3. The process of claim 1, wherein said vacuum is in a range from about 10-4 to about 10-6 millibars of pressure, with less than about 80 parts per million (ppm) of O2. 4. The process of claim 3, wherein said step of annealing is performed at a temperature greater than 400° C., for at least one hour. 5. The process of claim 3, wherein said annealing is performed at a temperature in a range of about 1100-1200° C., for several hours. 6. A process for fabricating a stent comprising: producing a stent from a tube composed principally of niobium with a trace of additional metal for alloy formation and reinforcement, the production of the stent including a step of annealing the tube under vacuum in a substantially oxygen-free environment and a post-annealing step of at least partially coating the stent surface with a material to inhibit closure of a central lumen at a site of stent implant in a body, wherein said coating material is titanium nitrate. 7. A process for fabricating a stent comprising: producing a stent from a tube composed principally of niobium with a trace of additional metal for alloy formation and reinforcement, the production of the stent including a step of annealing the tube under vacuum in a substantially oxygen-free environment, wherein the process includes keeping the stent wrapped in a material having affinity for oxygen during the production of the stent under vacuum to reduce oxygen entry into the stent tubing, wherein the stent comprises a network of interconnected struts. 8. A process for fabricating a stent comprising: producing a stent from a tube composed principally of niobium with a trace of additional metal for alloy formation and reinforcement, the production of the stent including a step of annealing the tube under vacuum in a substantially oxygen-free environment, wherein the stent comprises a network of interconnected struts, wherein producing the stent comprises laser cutting of the tube.