초록 ▼

Although nanoparticles capable of providing an extremely large active surface area have highly marked advantages, when a PEFC electrode utilizing nanoparticles is used for a prolonged period of time, the catalyst nanoparticles on carrier of the PEFC electrode because of the nano-size thereof migrate

Although nanoparticles capable of providing an extremely large active surface area have highly marked advantages, when a PEFC electrode utilizing nanoparticles is used for a prolonged period of time, the catalyst nanoparticles on carrier of the PEFC electrode because of the nano-size thereof migrate and aggregate together to result in a rapid loss of activity. Thus, there is a demand for inhibition of the above aggregation so as to prevent any drop of catalytic activity. According to the present invention the aggregation of nanoparticles can be inhibited by catalyst nanoparticles containing Pt wherein a porous matter containing an inorganic oxide is disposed on the surface of the catalyst nanoparticles. When use is made of nanoparticles whose surface has undergone specific modification, excellent activity can be realized. Therefore, there are provided surface-modified nanoparticles and catalyst and further a PEFC electrode utilizing these nanoparticles.

대표청구항 ▼

The invention claimed is: 1. Surface-modified metal nanoparticles comprising platinum group metal-containing nanoparticles of an alloy of Pt and Ru that have been treated with a silane coupling agent and having, on the surface thereof, a porous substance comprising an inorganic oxide. 2. Nanopart

The invention claimed is: 1. Surface-modified metal nanoparticles comprising platinum group metal-containing nanoparticles of an alloy of Pt and Ru that have been treated with a silane coupling agent and having, on the surface thereof, a porous substance comprising an inorganic oxide. 2. Nanoparticles according to claim 1 wherein said surface-modified metal nanoparticles show an oxidative catalytic activity against hydrogen and methanol. 3. Nanoparticles according to claim 1 wherein said platinum group metal-containing nanoparticles have an average particle diameter not greater than 10 nm. 4. Nanoparticles according to claim 1 wherein said platinum group metal-containing nanoparticles have an average particle diameter of about 2-10 nm. 5. Nanoparticles according to claim 1 wherein said inorganic oxide is SiO2. 6. A catalyst comprising nanoparticles as claimed in claim 1 supported on a carrier or support. 7. A nanoparticle-containing catalyst according to claim 6 wherein the catalyst is a catalyst for a polymer electrolyte fuel cell (PEFC) electrode. 8. A fuel cell electrode comprising nanoparticles as claimed in claim 1 used as a catalyst for the electrode. 9. A fuel cell comprising a fuel cell electrode as claimed in claim 8. 10. The surface-modified metal nanoparticles as claimed in claim 1, wherein the porous substance comprising the inorganic oxide formed on the surface of the platinum group metal-containing nanoparticles has a pore diameter large enough to permit methanol to diffuse to the platinum group metal-containing nanoparticles and small enough to prevent a surface of the platinum group metal-containing nanoparticles exposed through the pores from contacting one another. 11. The surface-modified metal nanoparticles as claimed in claim 1, wherein the porous substance comprising said inorganic oxide formed on the surface of the platinum group metal-containing nanoparticles has a thickness of about 0.5 to 2 nm. 12. A method of producing surface-modified metal nanoparticles which comprises: (1) the step of treating platinum group metal-containing nanoparticles of an alloy of Pt and Ru with a silane coupling agent to provide silane coupling agent-treated nanoparticles, and (2) the step of forming a porous substance comprising an inorganic oxide in the presence of the silane coupling agent-treated nanoparticles, in that order to obtain surface-modified metal nanoparticles comprising the platinum group metal-containing nanoparticles with a porous substance comprising said inorganic oxide as formed on the surface thereof. 13. A method of producing surface-modified metal nanoparticles according to claim 12 wherein said surface-modified metal nanoparticles show a oxidative catalytic activity against hydrogen and methanol. 14. A method of producing surface-modified metal nanoparticles according to claim 12 wherein said coupling agent is a silane coupling agent. 15. The surface-modified metal nanoparticles produced by the method of claim 12. 16. The surface-modified metal nanoparticles as claimed in claim 15, wherein the porous substance comprising said inorganic oxide formed on the surface of the platinum group metal-containing nanoparticles has a pore diameter large enough to permit methanol to diffuse to the platinum group metal-containing nanoparticles and small enough to prevent a surface of the platinum group metal-containing nanoparticles exposed through the pores from contacting one another. 17. The surface-modified metal nanoparticles as claimed in claim 15, wherein the porous substance comprising said inorganic oxide formed on the surface of the platinum group metal-containing nanoparticles has a thickness of about 0.5 to 2 nm. 18. A method of producing surface-modified metal nanoparticles which comprises: (1) the step of forming nanoparticles by subjecting a platinum group metal ion-containing solution to containing Pt and Ru to reduction treatment, (2) the step of treating the nanoparticles with a silane coupling agent to provide a silane coupling agent treated nanoparticles, and (3) the step of forming a porous substance comprising an inorganic oxide in the presence of the silane coupling agent-treated nanoparticles, in that order to obtain surface-modified metal nanoparticles comprising the platinum group metal-containing nanoparticles of an alloy of Pt and Ru with a porous substance comprising said inorganic oxide as formed on the surface thereof and showing an oxidative catalytic activity against hydrogen and methanol. 19. The surface-modified metal nanoparticles produced by the method of claim 18. 20. The surface-modified metal nanoparticles according to claim 19, wherein the porous substance comprising said inorganic oxide formed on the surface of the platinum group metal-containing nanoparticles has a pore diameter large enough to permit methanol to diffuse to the platinum group metal-containing nanoparticles and small enough to prevent a surface of the platinum group metal-containing nanoparticles exposed through the pores from contacting one another. 21. The surface-modified metal nanoparticles as claimed in claim 19, wherein the porous substance comprising said inorganic oxide formed on the surface of the platinum group metal-containing nanoparticles has a thickness of about 0.5 to 2 nm.