초록 ▼

A plating layer 18 of Ni or the like is formed around the outer peripheral face 14 of a wire tool 10, and super abrasive grains 16 are electrodeposited so as to be embedded in the plating layer 18. A coating layer 20 is formed on the surface of the super abrasive grains 16 to increase efficiency dur

A plating layer 18 of Ni or the like is formed around the outer peripheral face 14 of a wire tool 10, and super abrasive grains 16 are electrodeposited so as to be embedded in the plating layer 18. A coating layer 20 is formed on the surface of the super abrasive grains 16 to increase efficiency during electrodeposition. The thickness of the coating layer 20 formed on the super abrasive grains 16 is less than 0.1 μm, and preferably not more than 0.05 μm. The coating layer 20 is thin enough that its mass is less than 10% of the mass of the super abrasive grain 16. Accordingly, the super abrasive grains 16 are electrodeposited in a single layer around the outer peripheral face 14 of the core wire 12. As a result, the super abrasive grains 16 do not readily come off the core wire 12, which means that the wire tool will have a longer life. Also, since there is no need to remove any excess super abrasive grains after their electrodeposition, manufacturing costs can be cut and less work is entailed.

대표청구항 ▼

The invention claimed is: 1. An electrodeposited wire tool, having a plurality of super abrasive grains fixed by electrodeposition to an outer peripheral face of a long thin object, wherein the super abrasive grains are fixed by only a plated layer electrodeposited to the outer peripheral face of t

The invention claimed is: 1. An electrodeposited wire tool, having a plurality of super abrasive grains fixed by electrodeposition to an outer peripheral face of a long thin object, wherein the super abrasive grains are fixed by only a plated layer electrodeposited to the outer peripheral face of the long thin object, wherein an entire surface of the super abrasive grains is covered with a coating layer containing a material selected from among TiC and SiC, and the thickness of the coating layer on the surface of the super abrasive grains is less than 0.1 μm. 2. An electrodeposited wire tool, having a plurality of super abrasive grains fixed by electrodeposition to an outer peripheral face of a long thin object, wherein the super abrasive grains are fixed by only a plated layer electrodeposited to an outer peripheral face of the long thin object, wherein an entire surface of the super abrasive grains is covered with a coating layer containing a material selected from among TiC and SiC, and the mass of the coating layer on the surface of the super abrasive grain is less than 10% of the mass of the super abrasive grain. 3. An electrodeposited wire tool according to claim 1, wherein the super abrasive grains are fixed to the outer peripheral face of the long thin object in a single layer. 4. An electrodeposited wire tool according to claim 2, wherein the super abrasive grains are fixed to the outer peripheral face of the long thin object in a single layer. 5. An electrodeposited wire tool according to claim 1, wherein the average grain size of the super abrasive grains is from 1 to 60 μm. 6. An electrodeposited wire tool according to claim 2, wherein the average grain size of the super abrasive grains is from 1 to 60 μm. 7. An electrodeposited wire tool according to claim 1, wherein all of the super abrasive grains are covered with the coating layer. 8. An electrodeposited wire tool according to claim 2, wherein all of the super abrasive grains are covered with the coating layer. 9. An electrodeposited wire tool according to claim 1, wherein the thickness of the coating layer is less than 0.05 μm. 10. An electrodeposited wire tool according to claim 2, wherein the mass of the coating layer is less than 5% of the mass of the super abrasive grains. 11. An electrodeposited wire tool, having a plurality of super abrasive grains fixed by electrodeposition to an outer peripheral face of a wire, wherein the super abrasive grains are fixed by only a plated layer electrodeposited to the outer peripheral face of the wire; an entire surface of the super abrasive grains is covered with a coating layer containing a material selected from among TiC and SiC; the thickness of the coating layer on the super abrasive grains is less than 0.1 μm; the average grain size of the super abrasive grains is from 1 to 60 μm; and the super abrasive grains are fixed to the outer peripheral face of the wire in a single layer. 12. An electrodeposited wire tool, having a plurality of super abrasive grains fixed by electrodeposition to an outer peripheral face of a wire, wherein the super abrasive grains are fixed by only a plated layer electrodeposited to the outer peripheral face of the wire; an entire surface of the super abrasive grains is covered with a coating layer containing a material selected from among TiC and SiC; the mass of the coating layer on the super abrasive grains is less than 10% of the mass of the super abrasive grain; the average grain size of the super abrasive grains is from 1 to 60 μm; and the super abrasive grains are fixed to the outer peripheral face of the wire in a single layer.