To provide a hardly colored curable composition having an excellent storage stability while maintaining fast curing properties. A curable composition which comprises a polymer (P) having a polyoxyalkylene chain and a group of the following formula (1) and a compound (S) having a mercapto group and a
To provide a hardly colored curable composition having an excellent storage stability while maintaining fast curing properties. A curable composition which comprises a polymer (P) having a polyoxyalkylene chain and a group of the following formula (1) and a compound (S) having a mercapto group and a group of the following formula (2), and which contains from 0.01 to 0.50 part by mass of the compound (S) per 100 parts by mass of the polymer (P): —Si(—X1)3 (1) —Si(—X2)m(—Y2)3-m (2) wherein symbols have the following meanings: X1 and X2: each independently a C1-6 alkoxy group, Y2: a C1-6 alkyl group, and m: 1, 2 or 3.
대표청구항▼
What is claimed is: 1. A curable composition which comprises a polymer (P) having polyoxyalkylene formed by ring-opening polymerization of a C2-6 alkylene oxide and a group of the following formula (1), and a compound (S) having the following formula (S1), and which contains from 0.01 to 0.50 part
What is claimed is: 1. A curable composition which comprises a polymer (P) having polyoxyalkylene formed by ring-opening polymerization of a C2-6 alkylene oxide and a group of the following formula (1), and a compound (S) having the following formula (S1), and which contains from 0.01 to 0.50 part by mass of the compound (S) per 100 parts by mass of the polymer (P): —Si(—X1)3 (1) Si(—X2)m(—Y2)3-m(-QM-SH) (S1) wherein symbols have the following meanings: X1 and X2: each independently a C1-6 alkoxy group, Y2: a C1-6 alkyl group, m: 1, 2 or 3, and QM: a C1-20 divalent organic group, and wherein the polymer (P) has a number average molecular weight (Mn) of from 5,000 to 30,000 and a molecular weight distribution (Mw/Mn) of at most 3.0. 2. The curable composition according to claim 1, wherein the polymer (P) is a polymer (P1) obtained by an urethane-forming reaction of a polymer (pP) having a polyoxyalkylene chain and a hydroxy group, with a compound (U) having a group of the following formula (1) and an isocyanate group, and in the urethane-forming reaction, the ratio of the total number of isocyanate groups in the compound (U) to the total number of hydroxy groups in the polymer (pP) is from 0.80 to 1.50: —Si(—X1)3 (1) wherein symbol has the following meaning: X1: a C1-6 alkoxy group. 3. The curable composition according to claim 2, wherein the compound (U) is a compound of the following formula (U1): Si(—X1)3(-QU-NCO) (U1) wherein symbols have the following meanings: X1: a C1-6 alkoxy group, and QU: a C1-20 divalent organic group. 4. The curable composition according to claim 1, which further contains a compound of the following formula (V): Si(—X3)n(—Y3)4-n (V) wherein symbols have the following meanings: X3: a C1-6 alkoxy group, Y3: a C1-6 hydrocarbon group, and n: 1, 2, 3 or 4. 5. An adhesive or sealing material using the curable composition as defined in claim 1. 6. The curable composition according to claim 1, wherein said ring-opening polymerization is in the presence of a double metal cyanide complex. 7. The curable composition according to claim 1, wherein compound (S) is present in a maximum amount of 0.06 part by mass of the compound (S) per 100 parts by mass of the polymer (P). 8. A curable composition which comprises a polymer (P) having polyoxyalkylene formed by ring-opening polymerization of a C2-6 alkylene oxide and a group of the following formula (1), a compound (S) having the following formula (S1), and an antioxidant (T), and which contains from 0.01 to 0.50 part by mass of the compound (S) and from 0.01 to 10 parts by mass of the antioxidant (T), per 100 parts by mass of the polymer (P): —Si(—X1)3 (1) Si(—X2)m(—Y2)3-m(-Qm-SH) (S1) wherein symbols have the following meanings: X1 and X2: each independently a C1-6 alkoxy group, Y2: a C1-6 alkyl group, m:1, 2 or 3, and QM: a C1-20 divalent organic group, and wherein the polymer (P) has a number average molecular weight (Mn) of from 5,000 to 30,000 and a molecular weight distribution (Mw/Mn) of at most 3.0. 9. The curable composition according to claim 8, which has a chromaticity of less than 100. 10. The curable composition according to claim 8, wherein said ring-opening polymerization is in the presence of a double metal cyanide complex. 11. The curable composition according to claim 8, wherein compound (S) is present in a maximum amount of 0.06 part by mass of the compound (S) per 100 parts by mass of the polymer (P). 12. A curable composition which is a curable composition obtained by adding and mixing an antioxidant (T) to a polymer (P) having polyoxyalkylene formed by ring-opening polymerization of a C2-6 alkylene oxide and the group of the following formula (1), and then adding and mixing a compound (S) having the following formula (S1) thereto, and which contains from 0.01 to 0.50 part by mass of the compound (S) and from 0.01 to 10 parts by mass of the antioxidant (T), per 100 parts by mass of the polymer (P): —Si(—X1)3 (1) Si(—X2)m(—Y2)3-m(-QM-SH) (S1) wherein symbols have the following meanings: X1 and X2: each independently a C1-6 alkoxy group, Y2: a C1-6 alkyl group, m: 1, 2 or 3, and QM: a C1-20 divalent organic group, and wherein the polymer (P) has a number average molecular weight (Mn) of from 5,000 to 30,000 and a molecular weight distribution (Mw/Mn) of at most 3.0. 13. The curable composition according to claim 12, which has a chromaticity of less than 100. 14. The curable composition according to claim 12, wherein said ring-opening polymerization is in the presence of a double metal cyanide complex. 15. The curable composition according to claim 12, wherein compound (S) is present in a maximum amount of 0.06 part by mass of the compound (S) per 100 parts by mass of the polymer (P).
Chu Hsien-Kun (Midland MI) Kamis Russell P. (Midland MI) Klosowski Jerome M. (Bay City MI) Lower Loren D. (Midland MI), Silicone sealants having reduced color.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.