초록 ▼

A process for removing epoxides from a process stream over a wide range of temperature and relative humidity, comprising the step of contacting the process stream with a filtration media comprising an acid form of a mesoporous zeolite produced from pentasil zeolite treated with a caustic agent, for

A process for removing epoxides from a process stream over a wide range of temperature and relative humidity, comprising the step of contacting the process stream with a filtration media comprising an acid form of a mesoporous zeolite produced from pentasil zeolite treated with a caustic agent, for a sufficient time to remove the epoxides therefrom.

대표청구항 ▼

What is claimed is: 1. A process for removing epoxides from a process stream over a wide range of temperature and relative humidity, comprising the step of contacting the process stream with a filtration media comprising an acid form of a mesoporous zeolite produced from pentasil zeolite having an

What is claimed is: 1. A process for removing epoxides from a process stream over a wide range of temperature and relative humidity, comprising the step of contacting the process stream with a filtration media comprising an acid form of a mesoporous zeolite produced from pentasil zeolite having an SiO2/Al2O3 ratio from about 20 to less than about 200 treated with a strong base, for a sufficient time to remove the epoxides therefrom. 2. The process of claim 1, wherein the temperature of the process stream is from about −25° F. to 120° F. 3. The process of claim 1, wherein the relative humidity of the process stream is from about 5% to about 95%. 4. The process of claim 1, wherein the pentasil zeolite is selected from the group consisting of ZSM-5, ZSM-8, ZSM-11 and combinations thereof. 5. The process of claim 1, wherein the mesoporous zeolite further comprises a compound impregnated therein selected from the group consisting of sulfates, fluorides, chlorides, nitrates, metal salts, acids and precursors thereof, and combinations thereof. 6. The process of claim 5, wherein the acid is selected from the group consisting of sulfuric acid, hydrochloric acid, ammonium bisulfate, ammonium chloride, ammonium fluoride, ammonium nitrate, citric acid, formic acid, and combinations thereof. 7. The process of claim 1, wherein the mesoporous zeolite comprises pores having a diameter size in the range of from about 2 nm to 50 nm. 8. The process of claim 1, wherein the mesoporous zeolite comprises, a surface area of at least 375 m2/g. 9. The process of claim 1, wherein the mesoporous zeolite comprises a pore volume of at least 0.220 cm3/g. 10. The process of claim 1, wherein the strong base caustic agent is present in a solution at a concentration of from about 0.001N to 10.0N. 11. The process of claim 10, wherein the concentration is from about 0.1N to 1.0N. 12. The process of claim 1, wherein the strong base is a hydroxide. 13. The process of claim 12, wherein the hydroxide is selected from the group consisting of potassium hydroxide, barium hydroxide, cesium hydroxide, sodium hydroxide, strontium hydroxide, calcium hydroxide, lithium hydroxide, rubidium hydroxide, and combinations thereof. 14. The process of claim 1, wherein the zeolite-based filtration media is in a form selected from the group consisting of a particle, a bead, an extrusion or combinations thereof. 15. The process of claim 1, wherein the pentasil zeolite is ZSM-5. 16. The process of claim 1, wherein the pentasil zeolite has a SiO2/Al2O3 ratio from about 30 to about 90. 17. A process for removing epoxides, amines and/or aldehydes from a process stream over a wide range of temperature and relative humidity, comprising the step of contacting the process stream with a filtration media comprising an acid form of a mesoporous zeolite produced from pentasil zeolite having an SiO2/Al2O3 ratio from about 20 to less than about 200 treated with a strong base, for a sufficient time to remove the epoxides, amines and/or aldehydes therefrom, wherein said mesoporous zeolite further comprises a compound impregnated therein selected from the group consisting of sulfates, fluorides, chlorides, nitrates, metal salts, acids and precursors thereof, and combinations thereof. 18. The process of claim 16, wherein the acid is selected from the group consisting of sulfuric acid, hydrochloric acid, ammonium bisulfate, ammonium chloride, ammonium fluoride, ammonium nitrate, citric acid, formic acid, and combinations thereof. 19. The process of claim 17, wherein the mesoporous zeolite comprises pores having a diameter size in the range of from about 2 nm to 50 nm. 20. The process of claim 17, wherein the mesoporous zeolite comprises a surface area of at least 375 m2/g. 21. The process of claim 17, wherein the mesoporous zeolite comprises a pore volume of at least 0.220 cm3/g. 22. The process of claim 17, wherein the strong base is present in a solution at a concentration of from about 0.001N to 10.0N. 23. The process of claim 17, wherein the strong base is a hydroxide. 24. The process of claim 23, wherein the hydroxide is selected from the group consisting of potassium hydroxide, barium hydroxide, cesium hydroxide, sodium hydroxide, strontium hydroxide, calcium hydroxide, lithium hydroxide, rubidium hydroxide, and combinations thereof. 25. The process of claim 17, wherein the zeolite-based filtration media is in a form selected from the group consisting of a particle, a bead, an extrusion or combinations thereof.