초록 ▼

A process for producing a cable, such as, for medium-tension or high-tension power transmission or distribution, having at least one coating layer made of a thermoplastic polymer material. The process includes at least the following steps: (a) extruding a thermoplastic material of at least one therm

A process for producing a cable, such as, for medium-tension or high-tension power transmission or distribution, having at least one coating layer made of a thermoplastic polymer material. The process includes at least the following steps: (a) extruding a thermoplastic material of at least one thermoplastic polymer and at least one dielectric liquid; (b) passing the thermoplastic material through at least one static mixer; and (c) depositing and shaping the thermoplastic material around a conductor belonging to the cable so as to obtain a layer of thermoplastic coating on the conductor.

대표청구항 ▼

What is claimed is: 1. A process for producing a cable provided with at least one thermoplastic coating comprising: providing at least one thermoplastic polymer and at least one dielectric liquid; feeding said at least one thermoplastic polymer into at least one extruder; conveying said at least on

What is claimed is: 1. A process for producing a cable provided with at least one thermoplastic coating comprising: providing at least one thermoplastic polymer and at least one dielectric liquid; feeding said at least one thermoplastic polymer into at least one extruder; conveying said at least one thermoplastic polymer through said at least one extruder; plasticizing said at least one thermoplastic polymer traveling through said at least one extruder; adding said at least one dielectric liquid to said at least one thermoplastic polymer in a zone of said at least one extruder, wherein said at least one thermoplastic polymer is in a molten state, to form a thermoplastic material, wherein said at least one dielectric liquid is distributed substantially uniformly within said at least one thermoplastic polymer; passing said thermoplastic material through at least one static mixer; and extruding said thermoplastic material around a conductor so as to obtain a layer of thermoplastic coating on said conductor. 2. The process according to claim 1, wherein said dielectric liquid is also added to said at least one thermoplastic polymer in the solid state. 3. The process according to claim 1, wherein said dielectric liquid is added in at least two separate points of said zone of said at least one extruder. 4. The process according to claim 2, wherein said dielectric liquid is added to said at least one thermoplastic polymer during said feeding sub-step. 5. The process according to claim 2, wherein said dielectric liquid is added to said at least one thermoplastic polymer before said feeding sub-step. 6. The process according to claim 2, wherein said dielectric liquid is added in at least one zone of said at least one extruder in which said at least one thermoplastic polymer is in the solid state. 7. The process according to claim 1, further comprising filtering said thermoplastic material prior to said step of passing said thermoplastic material through at least one static mixer. 8. The process according to claim 1, further comprising filtering said thermoplastic material after said step of passing said thermoplastic material through at least one static mixer. 9. The process according to claim 1, wherein said at least one thermoplastic coating is a layer of electrical insulation. 10. The process according to claim 1, wherein said at least one thermoplastic coating is a semiconductive layer. 11. The process according to claim 1, wherein said thermoplastic material comprises at least one polyolefin. 12. The process according to claim 11, wherein said polyolefin has an elastic flexural modulus, measured according to ASTM standard D790 at ambient temperature, of between 30 and 1400 MPa. 13. The process according to claim 12, wherein said elastic flexural modulus is between 60 and 1000 MPa. 14. The process according to claim 11, wherein said polyolefin has a melt flow index (MFI), measured at 230° C. under a 21.6 N load according to ASTM standard D1238/L, of between 0.05 and 10.0 dg/min. 15. The process according to claim 14, wherein said melt flow index is between 0.5 and 5.0 dg/min. 16. The process according to claim 11, wherein said polyolefin is: a) a high-density polyethylene (HDPE) with a density of between 0.93 g/cm3 and 0.96 g/cm3; or b) a propylene homopolymer or a copolymer of propylene with at least one olefinic comonomer chosen from ethylene and an α-olefin other than propylene, said homopolymer or copolymer having a melting point greater than or equal to 140° C. and a heat of fusion of from 30 to 100 J/g. 17. The process according claim 1, wherein said dielectric liquid is an aromatic oil, an aliphatic oil, or an aliphatic and aromatic oil with a dielectric constant (measured at 25° C. according to IEC standard 247) of not greater than 8. 18. The process according to claim 17, wherein said dielectric constant is less than 3.5. 19. The process according to claim 17, wherein said dielectric liquid is: (i) an alkylaryl hydrocarbon containing at least two, non-fused aromatic rings and having a ratio between the number of aryl carbon atoms and the total number of carbon atoms of greater than or equal to 0.6; (ii) a diphenyl ether, which is unsubstituted or substituted with at least one linear or branched aliphatic, aromatic or mixed aliphatic and aromatic hydrocarbon radical, containing from 1 to 30 carbon atoms, or (iii) a mixture of (i) and (ii). 20. The process according to claim 1, further comprising adding an epoxy resin to said dielectric liquid before said extruding step. 21. The process according to claim 20, wherein said epoxy resin is added in an amount of not greater than 1% by weight relative to the weight of said dielectric liquid. 22. The process according to claim 1, wherein the weight ratio between said dielectric liquid and said at least one thermoplastic polymer is between 1:99 and 25:75. 23. The process according to claim 22, wherein said weight ratio is between 2:98 and 20:80. 24. The process according to claim 23, wherein said weight ratio is between 3:97 and 15:85.