초록 ▼

A catalyst composition is provided for use on a diesel particulate filter which facilitates the oxidation of soot from diesel engine exhaust and which generates low NO2 emissions during regeneration of the filter. The catalyst composition includes a catalytic metal comprising a platinum group metal

A catalyst composition is provided for use on a diesel particulate filter which facilitates the oxidation of soot from diesel engine exhaust and which generates low NO2 emissions during regeneration of the filter. The catalyst composition includes a catalytic metal comprising a platinum group metal selected from Pt, Pd, Pt—Pd, or combinations thereof, an active metal oxide component containing Cu and La; and an oxide component selected from oxides of Co, Fe, or combinations thereof. The catalyst composition includes a support selected from alumina, silica, zirconia, or combinations thereof. The catalyst composition may be provided on a diesel particulate filter by impregnating the filter with an alumina, silica or zirconia sol solution modified with glycerol and/or saccharose, impregnating the filter with a stabilizing solution, and impregnating the filter with a solution containing the catalyst metal precursor(s), the active metal oxide precursor(s) and the Co or Fe oxide(s). The resulting catalyst coated diesel particulate filter provides effective soot oxidation, exhibits good thermal stability, has a high BET surface area, exhibits minimal backpressure, and produces low NO2 emissions during filter regeneration.

대표청구항 ▼

What is claimed is: 1. A catalyst composition for use on a diesel particulate filter for facilitating soot oxidation comprising: a catalytic metal comprising a platinum group metal selected from the group consisting of Pt, Pd, Pt—Pd, and combinations thereof; an active metal oxide component

What is claimed is: 1. A catalyst composition for use on a diesel particulate filter for facilitating soot oxidation comprising: a catalytic metal comprising a platinum group metal selected from the group consisting of Pt, Pd, Pt—Pd, and combinations thereof; an active metal oxide component comprising CuO—La2CuO4; and an oxide component selected from the group consisting of oxides of Co, Fe, and combinations thereof. 2. The catalyst composition of claim 1 wherein said platinum group metal loading is between about 5 to about 15 g/ft3. 3. The catalyst composition of claim 1 wherein said catalytic metal comprises palladium only. 4. The catalyst composition of claim 1 wherein said Co oxide component comprises Co3O4. 5. The catalyst composition of claim 1 wherein said Fe oxide component comprises Fe2O3. 6. The catalyst composition of claim 1 further including a support selected from the group consisting of alumina, silica, zirconia, and combinations thereof. 7. The catalyst composition of claim 6 wherein said support has been stabilized with an element selected from the group consisting of lanthanum, zirconium, aluminum, and combinations thereof. 8. The catalyst composition of claim 1 wherein said platinum group metal loading in said catalyst composition is less than about 20 g/ft3. 9. A diesel exhaust gas treatment system comprising: a diesel particulate filter for receiving diesel exhaust gas from a diesel engine; and a catalyst composition coated on said filter; said catalyst composition comprising a catalytic metal comprising a platinum group metal selected from the group consisting of Pt, Pd, Pt—Pd, and combinations thereof; an active metal oxide comprising CuO—La2CuO4; and an oxide component selected from Co, Fe, or combinations thereof. 10. The diesel exhaust gas treatment system of claim 9 wherein said platinum group metal loading in said catalyst composition is less than about 20 g/ft3. 11. The diesel exhaust treatment system of claim 9 wherein said platinum group metal loading is between about 5 and about 15 g/ft3. 12. The diesel exhaust treatment system of claim 9 wherein said catalyst composition further includes a support selected from the group consisting of alumina, silica and zirconia, and combinations thereof. 13. The diesel exhaust treatment system of claim 9 wherein catalyst composition facilitates oxidation of soot trapped on said filter at a temperature between about 550 and 600° C. 14. The diesel exhaust treatment system of claim 9 wherein said catalyst composition facilitates oxidation of 60 to 100% of soot trapped on said filter. 15. The diesel exhaust treatment system of claim 9 wherein during regeneration of said diesel particulate filter containing said catalyst composition, the amount of NO2 is reduced to between about 0.40 to 0.70 from its initial level upstream of said filter. 16. The diesel exhaust treatment system of claim 15 wherein during regeneration of said diesel particulate filter containing said catalyst composition, the amount of NO2 is reduced to about 0.60. 17. The diesel exhaust treatment system of claim 15 wherein during regeneration of said diesel particulate filter containing said catalyst composition, the amount of NO2 is reduced to about 0.40.