초록

Algae-resistant roofing granules are formed by extruding a mixture of mineral particles and a binder to form porous granule bodies, and algaecide is distributed in the pores. Release of the algaecide is controlled by the structure of the granules.

대표청구항 ▼

We claim: 1. A process for producing algae-resistant roofing granules, the process comprising: (a) preparing porous, inert base particles from a mixture including stone dust and a binder; (b) providing at least one inorganic algaecide on or within the base particles to form algaecide-bearing partic

We claim: 1. A process for producing algae-resistant roofing granules, the process comprising: (a) preparing porous, inert base particles from a mixture including stone dust and a binder; (b) providing at least one inorganic algaecide on or within the base particles to form algaecide-bearing particles; (c) insolubilizing the binder. 2. A process according to claim 1 wherein the mixture is formed into base particles by a forming process selected from press molding, cast molding, injection molding, extrusion, spray granulation, gel casting, pelletizing, compaction and agglomeration. 3. A process according to claim 1 wherein the at least one inorganic algaecide is provided on the base particle by coating the base particle with the at least one inorganic algaecide. 4. A process according to claim 1 wherein the at least one inorganic algaecide is selected from the group consisting of copper materials, zinc materials, and mixtures thereof. 5. A process according to claim 4 wherein the inorganic algaecides are cuprous oxide and zinc oxide. 6. A process according to claim 1 wherein the binder comprises an aluminosilicate material, and the base particles are fired in a kiln at a temperature of from 800 degrees C. to 1200 degrees C. to insolubilize the binder. 7. A process according to claim 6 wherein the at least one inorganic algaecide is provided in the base particles after the base particles are fired, an algaecide-forming compound being dissolved in a fluid to form a solution, the solution being drawn into the pores in the base particles by capillary action to form solution-laden particles, the solution-laden particles being subsequently treated to convert the algaecide-forming compound to an inorganic algaecide. 8. A process according to claim 7 wherein the algaecide-forming compound is a soluble copper salt, and the solution-laden particles are subsequently treated by heating the particles to convert the soluble copper salt to cuprous oxide. 9. A process according to claim 6 wherein the at least one inorganic algaecide is provided in the base particles after the base particles are fired, an algaecide-forming compound being mixed with a binder and a fluid to form a slurry, the slurry being drawn into the pores in the base particles by capillary action to form slurry-laden particles, the slurry-laden particles being subsequently treated to convert the algaecide-forming compound to an inorganic algaecide. 10. A process according to claim 9 wherein the algaecide-forming compound is a soluble copper salt, and the slurry-laden particles are subsequently treated by heating the particles to convert the soluble copper salt to cuprous oxide. 11. A process according to claim 1 further comprising coating the algaecide-bearing particles with a colorant composition. 12. A process according to claim 11 wherein the colorant composition includes a fusible binder, and further comprising heating the colorant-coated algaecide-bearing particles to fuse the binder. 13. A process according to claim 1 wherein the roofing granules have a porosity of between about 3 percent and 30 percent by volume. 14. A process according to claim 1 wherein the mixture includes from about 10 percent to 40 percent by weight binder. 15. Roofing granules prepared according to the process of claim 1. 16. A process for producing algae-resistant roofing granules, the process comprising: (a) preparing porous, inert base particles from a mixture including stone dust and from about 10 percent to 40 percent by weight of a binder comprising an aluminosilicate material; (b) providing at least one inorganic algaecide within the base particles to form algaecide-bearing particles; (c) insolubilizing the binder by firing the base particles in a kiln at a temperature of from 800 degrees C. to 1200 degrees C.; the roofing granules having a porosity of between about 3 percent and 30 percent by volume. 17. Roofing granules prepared according to the process of claim 16. 18. A process according to claim 1 wherein the porosity of the inert base particles is controlled by selection of the shape of the stone dust. 19. A process according to claim 1 wherein the porosity of the inert base particles is controlled by selection of the particle size distribution of the stone dust. 20. A process according to claim 16 wherein the porosity of the inert base particles is controlled by selection of the shape of the stone dust. 21. A process according to claim 16 wherein the porosity of the inert base particles is controlled by selection of the particle size distribution of the stone dust. 22. A process according to claim 16 wherein the porosity of the inert base particles is controlled by adjusting the ratio of stone dust and aluminosilicate material.