A composition for surface treatment of aluminium, aluminum alloys, magnesium or magnesium alloys and the treating solutions being diluted to the desired concentration are defined. The composition contains (1) compound A containing at least one metal element selected from the group consisting of Hf(I
A composition for surface treatment of aluminium, aluminum alloys, magnesium or magnesium alloys and the treating solutions being diluted to the desired concentration are defined. The composition contains (1) compound A containing at least one metal element selected from the group consisting of Hf(IV), Ti(IV) and Zr(IV), (2) a fluorine-containing compound of sufficient amount to make fluorine exist in the composition in an amount of at least 5 times the molarity of the total molarity of the metal contained in the above-mentioned compound A, (3) at least one metal ion B selected from the group of alkaline earth metals, (4) at least one metal ion C selected from the group consisting of Al, Zn, Mg, Mn and Cu, and (5) nitric ion and the mol concentration of compound A is 0.1-50 mmol/L as the metal element of Hf(IV), Ti(IV) and Zr(IV). A metal treated with the treating method of the present invention solution has an excellent resistance to various corrosive environments.
대표청구항▼
What is claimed is: 1. A method for pretreatment of a metal material containing at least one metal selected from the group consisting of aluminum, aluminum alloys, magnesium and magnesium alloys comprising the steps of: providing a treating solution for surface treatment comprising components (1) t
What is claimed is: 1. A method for pretreatment of a metal material containing at least one metal selected from the group consisting of aluminum, aluminum alloys, magnesium and magnesium alloys comprising the steps of: providing a treating solution for surface treatment comprising components (1) to (6), (1) 0.1 to 50 mmol/L of a compound A containing at least one metal selected from the group consisting of Hf(IV), Ti(IV) and Zr(IV) as said metal contained in compound A, (2) a fluorine-containing compound of a sufficient amount to cause etching of the surface of the aluminum, aluminum alloys, magnesium or magnesium alloys and to make fluorine exist in the treating solution in an amount of at least 7 times the molarity of the total molarity of the metal contained in compound A, (3) at least one metal ion B selected from the group consisting of Ca, Sr and Ba, (4) at least one metal ion C selected from the group consisting of Zn, Mg, Mn and Cu, (5) nitric ion, and (6) at least one compound selected from the group consisting of HClO3, HBrO3, HNO2, HMnO4, HVO3, H2WO4, and an oxygen acid salt thereof; contacting a surface of the metal material with the treating solution for no more than 180 seconds, the treating solution having a pH of from 3 to 6, a temperature of from 30-70° C. and free fluorine ion concentration of less than 500 ppm; etching the surface of the metal material with the treating solution; and depositing a surface-treated film layer of the metal contained in compound A of from more than 10-72 mg/m2. 2. The method of claim 1, wherein the total concentration of metal ion B is from 1 to 500 ppm. 3. The method of claim 1, wherein the total concentration of metal ion C is from 1 to 5000 ppm. 4. The method of claim 1, wherein the concentration of nitric ion is from 1000 to 30000 ppm. 5. The method of claim 1, wherein the concentration of the at least one compound selected from the group consisting of HClO3, HBrO3, HNO2, HMnO4, HVO3, H2WO4, and an oxygen and salt thereof, is from 10 to 5000 ppm. 6. The method of claim 1, wherein the treating solution consists essentially of components (1) to (6). 7. The method of claim 1, wherein the treating solution has a pH of from 4 to 6. 8. The method of claim 1, wherein the treating solution has a pH of from 5 to 6. 9. The method of claim 1, wherein the treating solution has a pH of 6. 10. The method of claim 1, wherein component (6) is at least one compound selected from the group consisting of HMnO4, HVO3, H2WO4, and an oxygen acid salt thereof. 11. The method of claim 1, wherein the concentration of the at least one compound selected from the group consisting of HClO3, HBrO3, HNO2, HMnO4, HVO3, H2WO4, and an oxygen acid salt thereof, is from 10 to 200 ppm.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (10)
Frelin Frank J. (Norristown PA) Kelly Timm L. (Oreland PA) Malloy Anthony J. (Willow Grove PA), Coating solution for metal surfaces.
Shan, Dayong; Song, Yingwei; Han, Enhou; Chen, Rongshi; Ke, Wei, Chromate-free conversion film solution and the method of applying the solution to magnesium alloys.
Sudour, Michel; Wozniak, Aline; Maintier, Philippe, Zirconium pretreatment compositions containing molybdenum, associated methods for treating metal substrates, and related coated metal substrates.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.