초록 ▼

This invention relates to: a molding material comprising a bundle of continuous reinforcing fibers (A), a polyarylene sulfide prepolymer (B) comprising at least 50% by weight of cyclic polyarylene sulfide and having the weight average molecular weight of less than 10,000 or polyarylene sulfide (B&#x

This invention relates to: a molding material comprising a bundle of continuous reinforcing fibers (A), a polyarylene sulfide prepolymer (B) comprising at least 50% by weight of cyclic polyarylene sulfide and having the weight average molecular weight of less than 10,000 or polyarylene sulfide (B′) having the weight average molecular weight of 10,000 or greater and the degree of dispersion of 2.5 or lower, and thermoplastic resin (C); a prepreg comprising a resin composition comprising the polyarylene sulfide prepolymer (B) impregnated into a reinforcing fiber; and a method for producing a fiber-reinforced molding substrate comprising step (I) of continuously feeding a bundle of continuous reinforcing fibers, step (II) of combining cyclic polyarylene sulfide with the reinforcing fiber bundle, step (III) of heating the composite obtained in step (II) to subject the cyclic polyarylene sulfide to ring-opening polymerization to convert into polyarylene sulfide, and step (IV) of cooling the composite obtained in step (III) and withdrawing the same.

대표청구항 ▼

The invention claimed is: 1. A molding material comprising: (i) 1 to 50% by weight of a bundle of continuous reinforcing fibers (A); (ii) 0.1 to 10% by weight of a polyarylene sulfide prepolymer (B) comprising at least 50% by weight of cyclic polyarylene sulfide and having a weight average molecula

The invention claimed is: 1. A molding material comprising: (i) 1 to 50% by weight of a bundle of continuous reinforcing fibers (A); (ii) 0.1 to 10% by weight of a polyarylene sulfide prepolymer (B) comprising at least 50% by weight of cyclic polyarylene sulfide and having a weight average molecular weight of less than 10,000 or polyarylene sulfide (B′) having a weight average molecular weight of 10,000 or greater and having a degree of dispersion represented by weight average molecular weight/number average molecular weight of 2.5 or smaller; and (iii) 40 to 98.9% by weight of a thermoplastic resin (C), wherein component (C) is adhered to a composite of component (A) and component (B) or (B′). 2. The molding material according to claim 1, wherein the melting point of component (B) is 100° C. to 250° C. 3. The molding material according to claim 1, wherein a decrease in the weight of component (B′) when heated satisfies the condition represented by the equation below: ΔWr=(W1−W2)/W1×100≦0.18(%) wherein Δ Wr represents a percentage of weight decrease (%), which is determined based on the weight of a sample (W2) at 330° C. relative to the weight of a sample (W1) at 100° C. when performing thermogravimetric analysis under an ordinary pressure and in a non-oxidizing atmosphere from 50° C. to an arbitrary temperature of 330° C. or higher at a temperature increase rate of 20° C/min. 4. The molding material according to claim 1, wherein component (A) comprises at least 10,000 carbon fiber monofilaments. 5. The molding material according to claim 1, wherein component (ii) is component (B), and component (C) is at least one component selected from among polyamide resin, polyester resin, and polyphenylene sulfide resin. 6. The molding material according to claim 1, wherein component (ii) is component (B′), and component (C) is at least one component selected from among polyamide resin, polyetherimide resin, polyamide imide resin, polyether ether ketone resin, and polyphenylene sulfide resin. 7. The molding material according to claim 1, wherein component (A) is arranged substantially parallel to the direction of a shaft center and the length of component (A) is substantially the same as that of the molding material. 8. The molding material according to claim 7, wherein the composite of component (A) and component (B) or (B′) has a core structure and component (C) surrounds the composite to form a core-in-sheath structure. 9. The molding material according to claim 8, wherein the form of the molding material is a long-fiber pellet. 10. The molding material according to claim 1, wherein the length of the molding material is 1 mm to 50 mm.