Process for manufacturing high density boron carbide
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
C01B-035/00
C01B-025/08
C01B-031/36
C01B-031/00
출원번호
US-0630711
(2005-06-17)
등록번호
US-8110165
(2012-02-07)
우선권정보
IL-162676 (2004-06-22)
국제출원번호
PCT/IL2005/000645
(2005-06-17)
§371/§102 date
20071218
(20071218)
국제공개번호
WO2005/123626
(2005-12-29)
발명자
/ 주소
Bar-Ziv, Shimshon
Hachamo, Yehoshua
Gorni, David
Ophir, Zohar
Gutman, Itamar
Frey, Joseph
Nisenholz, Zvi
출원인 / 주소
Rafael-Armament Development
대리인 / 주소
Ohlandt, Greeley, Ruggiero & Perle, LLP
인용정보
피인용 횟수 :
1인용 특허 :
4
초록▼
A process for manufacturing high density boron carbide by pressureless sintering, enabling to create sintered products of complex shapes and high strength. The process comprises mixing raw boron carbide powder with carbon precursor, such as a polysaccharide, compacting the mixture to create an objec
A process for manufacturing high density boron carbide by pressureless sintering, enabling to create sintered products of complex shapes and high strength. The process comprises mixing raw boron carbide powder with carbon precursor, such as a polysaccharide, compacting the mixture to create an object of the desired shape, and finally carbonizing and sintering the object at higher temperatures.
대표청구항▼
1. A process for manufacturing boron carbide objects comprising the steps of: (a) pre-washing a raw boron carbide powder with an organic solvent selected from the group consisting of isopropyl alcohol, ethyl alcohol, methyl alcohol, acetone, and a combination thereof, said pre-washing including mixi
1. A process for manufacturing boron carbide objects comprising the steps of: (a) pre-washing a raw boron carbide powder with an organic solvent selected from the group consisting of isopropyl alcohol, ethyl alcohol, methyl alcohol, acetone, and a combination thereof, said pre-washing including mixing for about 24 hours, followed by drying the washed boron carbide;(b) mixing the washed boron carbide powder with a carbon precursor selected from the group consisting of phenolic resin, aqueous solution of a polysaccharide, and mixture of two or more saccharides;(c) drying the mixture;(d) granulating the dried mixture;(e) compacting the granulated dried mixture to form a shaped object by applying a pressure thereto;(f) carbonizing the shaped body in an inert atmosphere, by dwelling at a high temperature for a predetermined period of time; and(g) sintering the carbonized shaped body at a temperature between 2300° C. and about 2350° C. in an inert atmosphere for a time period of not less than about 30 min. 2. The process according to claim 1, wherein the polysaccharide is maltodextrin. 3. The process according to claim 1, wherein the drying is carried out by spray drying. 4. The process of claim 1, wherein the pressure is applied uniaxially. 5. The process of claim 1, wherein the pressure is applied isostatically. 6. The process of claim 1, wherein the compacting is carried out with heating. 7. The process of claim 6, wherein the compaction is carried out at a temperature of between about 130° C. and about 170° C. 8. The process of claim 1, wherein compaction is carried out until the density of the compacted shaped body reaches between about 1.36 to about 1.60 g/cc. 9. The process of claim 1, wherein the carbonization step is carried out in a nitrogen atmosphere. 10. The process of claim 1, wherein the carbonization step is carried out in an argon atmosphere. 11. The process of claim 1, wherein the carbonization step is carried out at a controlled heating rate, which is between about 25° C./hr to about 100° C./hr. 12. The process of claim 1, wherein the sintering is carried out in an argon atmosphere. 13. The process of claim 1, wherein the sintering is carried out for a time period of about 120 minutes. 14. The process of claim 1, wherein the sintering is performed while the shaped body is constrained between shaped graphite dies having essentially a geometry to match a desired final geometry of said shaped body. 15. The process of claim 14, wherein the graphite dies have a non-flat, multi-curved shape. 16. Shaped, high-density boron carbide objects made by a process for manufacturing boron carbide objects comprising the steps of: (a) pre-washing a raw boron carbide powder with an organic solvent selected from the group consisting of isopropyl alcohol, ethyl alcohol, methyl alcohol, acetone, and a combination thereof, said pre-washing including mixing for about 24 hours, followed by drying the washed boron carbide;(b) mixing the washed boron carbide powder with a carbon precursor selected from the group consisting of phenolic resin, aqueous solution of a polysaccharide, and mixture of two or more saccharides;(c) drying the mixture;(d) granulating the dried mixture;(e) compacting the granulated dried mixture to form a shaped object by applying a pressure thereto;(f) carbonizing the shaped body in an inert atmosphere, by dwelling at a high temperature for a predetermined period of time; and(g) sintering the carbonized shaped body at a temperature between 2300° C. and about 2350° C. in an inert atmosphere for a time period of not less than about 30 min.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (4)
Sigl Lorenz (Lechaschau ATX) Thaler Hubert (Kempten DEX) Schwetz Karl-Alexander (Sulzberg DEX), Process for producing bodies based on boron carbide by pressureless sintering.
Schwetz Karl A. (Sulzberg ATX) Vogt Georg (Kempten-Sankt Mang DEX), Process for the production of dense sintered shaped articles of polycrystalline boron carbide by pressureless sintering.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.