초록 ▼

A method of producing a tire including mixing in a non-productive phase at least one elastomer with a polyamide having a melting temperature of less than 180° C. The polyamide is allowed to heat to at least its melting temperature. During the productive phase, at least one curing agent is added to t

A method of producing a tire including mixing in a non-productive phase at least one elastomer with a polyamide having a melting temperature of less than 180° C. The polyamide is allowed to heat to at least its melting temperature. During the productive phase, at least one curing agent is added to the elastomeric composition. The curing agent may be a sulfur containing curing agent and/or a non-sulfur containing curing agent. The elastomeric composition may optionally include a crystalline EPDM elastomer. The resulting compositions may then be formed into a tire component which may be built into a tire and cured.

대표청구항 ▼

1. A method of producing an elastomeric composition comprising: mixing in a non-productive phase 100 parts by weight of at least one elastomer with from 5 to 100 parts by weight, per 100 parts by weight of elastomer (phr) of a polyamide having a melting temperature of less than 120° C. and a crystal

1. A method of producing an elastomeric composition comprising: mixing in a non-productive phase 100 parts by weight of at least one elastomer with from 5 to 100 parts by weight, per 100 parts by weight of elastomer (phr) of a polyamide having a melting temperature of less than 120° C. and a crystalline EPDM elastomer;allowing the temperature of the low melting temperature polyamide to reach at least its melting temperature; andadding in a productive phase to the product of the non-productive phase at least one non-sulfur containing curing agent, wherein the non-sulfur containing curing agent is selected from the group consisting of hexamethoxymethylmelamine, hexamethylene-tetramine, N-N′-m phenylenedimaleimide, and combinations thereof. 2. The method of claim 1 wherein the concentration of polyamide ranges from about 5 phr to about 30 phr. 3. The method of claim 1 wherein the concentration of polyamide ranges from about 55 phr to about 80 phr. 4. The method of claim 1 wherein at least one of a carbon black, an oil, a resin, a fatty acid, a silica, a silica coupler, a wax, an antioxidant, a resin, a stearic acid, nano-clay, resorcinol, or a zinc oxide is added to the composition of the non-productive phase. 5. The method of claim 1 wherein the non-productive stage comprises mixing the elastomer with the carbon black to form a master batch, and mixing the nano-clay with the polyamide, then mixing the nano-clay/polyamide mixture with the master batch. 6. The method of claim 1 wherein the elastomeric composition is formed into a tire component. 7. The method of claim 6 wherein the tire component is selected from the group consisting of sidewall, apex, treadbase, Extended Mobility Tire insert (“EMT insert”), wedge, gum strip, and wire coat. 8. The method of claim 6 further comprising building a tire with the tire component. 9. The method of claim 1 wherein the concentration of crystalline EPDM elastomer ranges from about 1 phr to about 30 phr. 10. The method of claim 9 wherein the concentration of polyamide ranges from about 1 phr to about 30 phr. 11. The method of claim 9 wherein the concentration of polyamide ranges from about 30 phr to about 80 phr. 12. The method of claim 9 wherein the elastomeric composition is formed into a tire component. 13. The method of claim 12 wherein the tire component is selected from the group consisting of sidewall, apex, treadbase, EMT insert, wedge, gum strip, and wire coat. 14. The method of claim 12 further comprising building a tire with the tire component. 15. A tire built comprising the elastomeric composition produced by the method of claim 1. 16. A tire built comprising the elastomeric composition produced by the method of claim 9.