초록 ▼

A lightweight structural concrete with screw-ability and nail-ability similar to wood is composed of a non-structural and ultra lightweight aggregate such as expanded perlite or a combination of expanded perlite and polystyrene beads of a particular size distribution and volume amount, entrained air

A lightweight structural concrete with screw-ability and nail-ability similar to wood is composed of a non-structural and ultra lightweight aggregate such as expanded perlite or a combination of expanded perlite and polystyrene beads of a particular size distribution and volume amount, entrained air cells of another specific size distribution and volume amount, and dense cementitious composition of a cement binder, a fine grade structural filler no larger than concrete sand grade, a pozzolan, and optional micro-fibers for reinforcement. This structural concrete matrix is optimized to hold 13 gauge T-nails and bugle head wood screws with thread ranging from 8 to 11 threads per inch and diameter of 0.10″ to 0.137″. The resulting concrete will have consistent screw-ability and nail-ability similar to that of wood.

대표청구항 ▼

1. A high strength lightweight concrete having a compression strength greater than 2500 psi, comprising: (a) 1.05 to 1.75 parts by volume of Portland cement or shrinkage-compensating cement;(b) 0.40 to 1.25 parts by volume of pozzolan;(c) 1.15 to 1.85 parts by volume of fine sand with a particle siz

1. A high strength lightweight concrete having a compression strength greater than 2500 psi, comprising: (a) 1.05 to 1.75 parts by volume of Portland cement or shrinkage-compensating cement;(b) 0.40 to 1.25 parts by volume of pozzolan;(c) 1.15 to 1.85 parts by volume of fine sand with a particle size distribution means meeting at least an ASTM C33 specification;(d) an amount of expanded lightweight aggregate of expanded perlite, expanded polystyrene or expanded vermiculite, or any combination thereof effective to achieve between 6% to 22% volume of a total concrete volume, and a particle size distribution mean between 1 mm to 3.5 mm with at least 75% of the amount of particles falling within 0.6 mm from a center of the particle size distribution mean;(e) 0.65 to 1.20 parts by volume of water effective to achieve a water to cement (W/C) ratio in the range of 0.27 to 0.60;(f) an amount of super-plasticizer effective to produce a target slump; and(g) an amount of air entrainment admixture effective to produce 5% to 20% entrained air cells with a cell size distribution mean no larger than 70% of the particle size distribution mean of the expanded lightweight aggregate in the concrete. 2. The high strength lightweight concrete according to claim 1, further comprising an amount of synthetic fiber effective to occupy up to 3.00% volume of the total concrete volume with a minimum tensile strength of 49,000 psi and a length between 5 mm to 18 mm. 3. The high strength lightweight concrete according to claim 1, further comprising a waterproof admixture effective to reduce both the water permeability of the concrete. 4. The high strength lightweight concrete according to claim 1, wherein a ratio of the expanded perlite or expanded vermiculite to the expanded polystyrene bead is adjustable to absorb water out of the wet concrete mix, before the concrete sets. 5. The high strength lightweight concrete according to claim 1, wherein the entrained air cells in the concrete can be substituted by any expanded lightweight aggregate of the same size as the entrained air cells. 6. The high strength lightweight concrete according to claim 1, wherein the expanded perlite or expanded vermiculite is water-absorbent and the expanded polystyrene bead is not water-absorbent, and wherein a ratio of the expanded perlite or the expanded vermiculite to the expanded polystyrene bead is adjustable to control an amount of water absorbed out of the concrete mix prior to setting. 7. The high strength lightweight concrete according to claim 1, wherein the pozzolan is one of Class F fly ash, Class C fly ash, silica fume and blast furnace slag. 8. A lightweight concrete having compression strength greater than 2500 psi comprising: (a) 1.05 to 1.75 parts by volume of one of Portland cement, magnesium based cement and a combination of Portland cement and magnesium based cement;(b) 0.00 to 1.25 parts by volume of one of Class F fly ash, Class C fly ash, silica fume and furnace slag;(c) 1.15 to 1.85 parts by volume of fine sand with a particle size distribution meeting at least an ASTM C33 specification;(d) an amount of expanded lightweight aggregate of expanded perlite, expanded polystyrene or expanded vermiculite, or any combination thereof effective to achieve between 6% to 22% volume of a total concrete volume, a particle size distribution mean between 1 mm and 3.5 mm with at least 75% of particles falling within 0.60 mm from a center of the particle size distribution mean;(e) 0.65 to 1.20 parts by volume of water effective to achieve a water to cement (W/C) ratio in the range of 0.27 to 0.60;(f) an amount of super-plasticizer effective to produce a target slump; and(g) an amount of entrainment admixture effective to produce 5% to 20% entrained air cells with a cell size distribution mean no larger than 70% of the particle size distribution mean of the expanded lightweight aggregate in the concrete. 9. The lightweight concrete according to claim 8, further comprising: an amount of synthetic fiber effective to occupy up to 3.00% volume of the total concrete volume with a minimum tensile strength of 49,000 psi and a length between 5 mm to 18 mm; andan amount of waterproof admixture effective to reduce the water permeability of the concrete. 10. The lightweight concrete according to claim 8, wherein a ratio of the expanded perlite or the expanded vermiculite relative to the expanded polystyrene bead is adjustable to absorb water amount out of the wet concrete before the concrete sets. 11. The lightweight concrete according to claim 8, wherein the entrained air cells in the concrete can be partially substituted by any lightweight aggregate having a compression strength less than 2500 psi or any expanded polystyrene bead having the same size as the entrained air cells. 12. The lightweight concrete according to claim 8, wherein the expanded perlite or the expanded vermiculite is water-absorbent and the expanded polystyrene bead is not water-absorbent, and wherein a ratio of the expanded perlite or the expanded vermiculite to the expanded polystyrene bead is adjustable to control an amount of water absorbed out of the concrete mix prior to setting.