초록 ▼

Tubular metal articles such as pipe and cylinder liners are produced by centrifugal casting on a permanent metal mold coated by refractory glass on the active surface. A coating suspension mix is evenly distributed onto the mold to form a uniform layer of insulation on the surface of the mold. The m

Tubular metal articles such as pipe and cylinder liners are produced by centrifugal casting on a permanent metal mold coated by refractory glass on the active surface. A coating suspension mix is evenly distributed onto the mold to form a uniform layer of insulation on the surface of the mold. The material for the coating comprises of essentially a waterborne suspension mix of glass particles. The suspension is given time to dry on the surface of the mold. The glass particles dispersed in the suspension are both non-crystalline and nonporous. The glass particles in the suspension and forming the coating are not dissolved and do not chemically attract the polar water molecule or cause it to bond to the surface of glass in the suspension or to the mold active surface. Articles cast as such are smooth surfaced and require only limited machining. The coating provides thermal protection to the mold, but more importantly, the water in the suspension vaporizes quickly on a warm mold because the water is not attracted or bonded to the refractory glass particles.

대표청구항 ▼

1. A process for manufacturing a metal casting free from pinholes and other blowout gas defects comprising, providing a mold, said mold having an active surface,heating and maintaining said mold to a temperature between 250° F.-600° F., prior to introducing a molten metal at an elevated temperature

1. A process for manufacturing a metal casting free from pinholes and other blowout gas defects comprising, providing a mold, said mold having an active surface,heating and maintaining said mold to a temperature between 250° F.-600° F., prior to introducing a molten metal at an elevated temperature into said mold, a coating suspension mix is applied onto said active surface of said mold,said coating suspension mix having dispersed therein a quantity of refractory glass that constitutes from 10.0% to 55.0% by weight of the coating suspension mix,said refractory glass being inert at said elevated temperature of said molten metal to be cast and having a brittle state at said elevated temperature of said molten metal,said suspension mix having a carrier liquid for suspending said quantity of refractory glass, wherein said carrier liquid and said refractory glass combined constitute at least 95.0% by weight of the suspension mix,wherein said refractory glass is nonporous to said carrier liquid and said carrier liquid is vaporizable at a temperature from 250° F. to 600° F.,drying said carrier liquid on said heated mold for at least five minutes in duration whereby said carrier liquid is vaporized and no further water vaporizes or are other gases generated, after said five minutes a thermal insulating coating remains on said mold active surface, said thermal insulating coating is inert and nonreactive to said molten metal. 2. A process according to claim 1, wherein said application of said suspension mix onto the active surface of the mold is in the form of a thin smooth layer, said thin smooth layer upon said drying forms a dry thermal insulating coating having a thickness of 0.01 inch to 0.04 inches on said active surface. 3. A process according to claim 2, wherein said molten metal temperature is at least 1,200° F. 4. A process according to claim 1, wherein said mold is a centrifugal casting mold. 5. A process according to claim 1, wherein said suspension mix is applied by spraying. 6. A process according to claim 1, wherein said molten metal is molten iron, said process further comprising pouring said molten iron into said centrifugal casting mold.