Optical strain gauge comprising a fiber Bragg grating
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
G01B-011/16
G02B-006/00
출원번호
US-0265974
(2010-04-22)
등록번호
US-8405822
(2013-03-26)
우선권정보
DE-10 2009 018 206 (2009-04-22)
국제출원번호
PCT/DE2010/000460
(2010-04-22)
§371/§102 date
20120517
(20120517)
국제공개번호
WO2010/121605
(2010-10-28)
발명자
/ 주소
Günther, Bernd
Ruppin, Hagen
Haase, Karl-Heinz
Kipp, Tobias
Kreuzer, Manfred
Maul, Jochen
Schulz, Rudolf
출원인 / 주소
Hottinger Baldwin Messtechnik GmbH
대리인 / 주소
Henry M Feiereisen LLC
인용정보
피인용 횟수 :
4인용 특허 :
7
초록▼
The invention relates to an optical strain gauge using a glass fiber (1) comprising a Bragg grating (2). The glass fiber is coated with a sheath (3) of polyether ether ketone with an admixture of at least 10 weight percent and a maximum of 40 weight percent of an inorganic filler, with a particle si
The invention relates to an optical strain gauge using a glass fiber (1) comprising a Bragg grating (2). The glass fiber is coated with a sheath (3) of polyether ether ketone with an admixture of at least 10 weight percent and a maximum of 40 weight percent of an inorganic filler, with a particle size of between 0.08 μm and 12 μm. The outer diameter of the sheath (3) is between 0.2 mm and 1.2 mm. The ratio D/d between the outer diameter D of the sheath (3) and the diameter d of the glass fiber (1) is between 2 and 6. A pressure of the sheath (3) on the glass fiber (1) is such that essentially no relative movement can occur between the glass fiber (1) and the sheath (3).
대표청구항▼
1. Optical strain gauge comprising a glass fiber, which is provided with a Bragg grating, and a sheath, wherein the sheath comprises the following composition: a mixture of poly-ether ether ketone and an inorganic filler in an admixture of at least 10 percent by weight and maximum 40 percent by weig
1. Optical strain gauge comprising a glass fiber, which is provided with a Bragg grating, and a sheath, wherein the sheath comprises the following composition: a mixture of poly-ether ether ketone and an inorganic filler in an admixture of at least 10 percent by weight and maximum 40 percent by weight, with a particle size of 0.08 μm to 12 μm,the outside diameter of the sheath is 0.2 mm to 1.2 mm,the ratio D/d between the outside diameter D of the sheath and the diameter d of the glass fiber is 2 to 6, anda pressure of the sheath on the glass fiber is such that no relative movement between the glass fiber and the sheath can occur. 2. Optical strain gauge according to claim 1, wherein the pressure of the sheath on the glass fiber is at least 120 N/mm2. 3. Optical strain gauge according to claim 1, wherein the glass fiber comprises a glass core having a coating of ORMOCER□. 4. Optical strain gauge according to claim 1, wherein the inorganic filler is a silicate. 5. Optical strain gauge according to claim 1, wherein the inorganic filler is a laminated silicate. 6. Optical strain gauge according to claim 1, wherein the inorganic filler is talcum, chalk, calcium carbonate, barium sulfate, boron nitride, silicon dioxide or bentonite. 7. Optical strain gauge according to claim 1, wherein the admixture of the inorganic filler is at least 25 percent by weight and maximum 40 percent by weight. 8. Optical strain gauge according to claim 1, wherein the admixture of the inorganic filler is at least 27 percent by weight and maximum 33 percent by weight. 9. Optical strain gauge according to claim 1, wherein the particle size is at least 0.1 μm and maximum 10 μm. 10. Method of making an optical strain, which comprises the following steps: providing (S1, S2) of a glass fiber with a Bragg grating andextruding (S3) of a sheath onto the glass fiber, whereinthe sheath comprises the following composition: a mixture of poly-ether ether ketone and an inorganic filler in an admixture of at least 10 percent by weight and maximum 40 percent by weight, with a particle size of 0.08 μm to 12 μm,the outside diameter of the sheath is 0.2 mm to 1.2 mm, the ratio D/d between the outside diameter D of the sheath and the diameter d of the glass fiber is 2 to 6, andafter termination of the process, a pressure of the sheath on the glass fiber is such that no relative movement between the glass fiber and the sheath can occur. 11. Method according to claim 10, wherein parameters of extrusion are chosen so that, after termination of the process, the pressure of the sheath on the glass fiber is at least 120 N/mm2. 12. Method according to claim 10, wherein the step of providing a glass fiber comprises the step (S1) of providing a glass core having the Bragg grating and the step (S2) of applying a coating of ORMOCER□ onto the glass core. 13. Method according to claim 10, wherein the inorganic filler is a silicate. 14. Method according to claim 10, wherein the inorganic filler is a laminated silicate. 15. Method according to claim 10, wherein the inorganic filler is talcum, chalk, calcium carbonate, barium sulfate, boron nitride, silicon dioxide or bentonite.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (7)
Peter A. Quigley ; Stephen C. Nolet, Composite spoolable tube with sensor.
Jens Engholm Pedersen DK; Martijn Beukema DK; Christian Vestergaard Poulsen DK; Lars Erik Eskildsen DK, Temperature stabilization of optical waveguides.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.