A microporous polypropylene film where film formability is improved in accordance with a β-crystal technique which allows microporous films to be continuously manufactured at low cost is disclosed. In addition, a microporous polypropylene film of which the specific gravity is further reduced is prov
A microporous polypropylene film where film formability is improved in accordance with a β-crystal technique which allows microporous films to be continuously manufactured at low cost is disclosed. In addition, a microporous polypropylene film of which the specific gravity is further reduced is provided. Furthermore, a microporous polypropylene film with a significantly high permeability is provided. In addition, manufacturing methods for these microporous polypropylene films are provided.
대표청구항▼
1. A microporous polypropylene film consisting essentially of not less than 97 wt % polypropylene with respect to a total amount of monomers of all polymers in the film, said polypropylene comprising polypropylene having a Trouton ratio of not less than 30, said film having 1) β-crystal activity, 2)
1. A microporous polypropylene film consisting essentially of not less than 97 wt % polypropylene with respect to a total amount of monomers of all polymers in the film, said polypropylene comprising polypropylene having a Trouton ratio of not less than 30, said film having 1) β-crystal activity, 2) a specific gravity of 0.2 to 0.4, 3) a liquid paraffin permeating time of 0.1 seconds/25 μm to 60 seconds/25 μm, 4) a heat shrinkage ratio at 105° C. in a longitudinal direction of the film of no greater than 5%, 5) a Trouton ratio of not less than 6 and 6) a Gurley air permeability of 50 sec/100 ml to 300 sec/100 ml. 2. A microporous polypropylene film consisting essentially of not less than 97 wt % polypropylene with respect to a total amount of monomers of all polymers in the film, said film having a Trouton ratio of not less than 6, said film having β-crystal activity, a specific gravity of 0.2 to 0.4, a liquid paraffin permeating time of 0.1 seconds/25 μm to 60 seconds/25 μm, a heat shrinkage ratio at 105° C. in a longitudinal direction of the film of no greater than 5% and a Gurley air permeability of 50 sec/100 ml to 300 sec/100 ml. 3. A microporous polypropylene film consisting essentially of not less than 97 wt % polypropylene with respect to a total amount of monomers of all polymers in the film, said polypropylene having a long chain branch in a main chain, said film having β-crystal activity, a specific gravity of 0.2 to 0.4, a liquid paraffin permeating time of 0.1 seconds/25 μm to 60 seconds/25 μm and a heat shrinkage ratio at 105° C. in a longitudinal direction of the film of no greater than 5%. 4. The microporous polypropylene film according to claim 3, wherein a Gurley air permeability is 10 sec/100 ml to 300 sec/100 ml. 5. The microporous polypropylene film according to any of claims 1 to 3, wherein the temperature of crystallizing from the melt (Tmc) of the film is 120° C. to 135° C. 6. A microporous polypropylene film consisting essentially of not less than 97 wt % polypropylene with respect to a total amount of monomers of all polymers in the film, said polypropylene comprising polypropylene, wherein the relationship between melt strength (MS) and melt flow rate (MFR), measured at 230° C., of the polypropylene is represented by formula (1), said film having β-crystal activity, a porosity of 60% to 85%, a liquid paraffin permeating time of 0.1 seconds/25 μm to 60 seconds/25 μm and a heat shrinkage ratio at 105° C. in a longitudinal direction of the film of no greater than 5% log(MS)>−0.61 log (MFR)+0.82 (1). 7. A microporous polypropylene film consisting essentially of not less than 97 wt % polypropylene with respect to a total amount of monomers of all polymers in the film, wherein melt strength (MS) of the film is less than 5 cN measured at 230° C., and a relationship between the MS and melt flow rate (MFR) of the film is represented by formula (2), and said film having β-crystal activity, a porosity of 60% to 85%, a liquid paraffin permeating time of 0.1 seconds/25 μm to 60 seconds/25 μm and a heat shrinkage ratio at 105° C. in a longitudinal direction of the film of no greater than 5% log(MS)>−0.9 log (MFR)+0.6 (2). 8. The microporous polypropylene film according to claim 6 or 7, wherein a Gurley air permeability is 10 sec/100 ml to 300 sec/100 ml. 9. The microporous polypropylene film according to claim 6 or 7, wherein the isotactic pentad fraction (mmmm) is 90% to 99.5%. 10. A microporous polypropylene film consisting essentially of not less than 97 wt % polypropylene with respect to a total amount of monomers of all polymers in the film, wherein formula (3) is satisfied in an in-plane intensity distribution profile scanned in a direction of an azimuthal angle for (−113) plane of the film in accordance with X-ray diffraction method, said film has β-crystal activity, a specific gravity of 0.2 to 0.4, a liquid paraffin permeating time of 0.1 seconds/25 μm to 60 seconds/29 μm and a heat shrinkage ratio at 105° C. in a longitudinal direction of the film of no greater than 5% 0.5≦I(MD)/I(TD)≦8 (3) (where, I (MD) is the integral intensity in the longitudinal direction and I (TD) is the integral intensity in the transverse direction. 11. The microporous polypropylene film according to claim 10, wherein a Gurley air permeability is 10 sec/100 ml to 300 sec/100 ml. 12. The microporous polypropylene film according to claim 1, wherein the polypropylene comprises 1) a mixture of a high molecular weight component or a polypropylene having a long chain branch with one or more common polypropylenes or 2) a copolymer or graft polymer of a propylene having a long chain branch and a common polypropylene.
Saito Jun (Sodegaurashi JPX) Kawazoe Shunji (Ichiharashi JPX) Kikukawa Shingo (Ichiharashi JPX), Polypropylene having a high melt-tensile strength, a process for producing the same and a molded product from the same.
Ikeda, Naoki; Sadamitsu, Kiyoshi; Hoki, Manabu; Nagata, Kenichiro; Kobayashi, Toshiaki, Porous polypropylene film, process for producing the same, and absorbent article employing the film.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.