초록 ▼

The present invention provides a metal-graphite composite material favorable to two-dimensional diffusion of heat and having a high thermal conductivity in two axial directions, and a production method therefor. The metal-graphite composite material of the present invention includes: 20 to 80% by vo

The present invention provides a metal-graphite composite material favorable to two-dimensional diffusion of heat and having a high thermal conductivity in two axial directions, and a production method therefor. The metal-graphite composite material of the present invention includes: 20 to 80% by volume of a scaly graphite powder; and a matrix selected from the group consisting of copper, aluminum and alloys thereof, wherein the scaly graphite powder in which a normal vector to a scaly surface thereof is tilted at 20° or higher with respect to a normal vector to a readily heat-conducting surface of the metal-graphite composite material is 15% or less relative to a whole amount of the scaly graphite powder, and the metal-graphite composite material has a relative density of 95% or higher.

대표청구항 ▼

1. A metal-graphite two-dimensionally thermally-conductive composite material comprising: 20 to 80% by volume of a scaly graphite powder; and a matrix selected from the group consisting of copper, aluminium and alloys thereof, wherein the scaly graphite powder in which a normal vector to a scaly sur

1. A metal-graphite two-dimensionally thermally-conductive composite material comprising: 20 to 80% by volume of a scaly graphite powder; and a matrix selected from the group consisting of copper, aluminium and alloys thereof, wherein the scaly graphite powder in which a normal vector to a scaly surface is tilted at 20° or higher with respect to a normal vector to a readily heat-conducting surface of the metal-graphite two-dimensionally thermally-conductive composite material is 12% or less relative to a whole amount of the scaly graphite powder,the scaly graphite powder in which a normal vector to a scaly surface is tilted at 10° or less with respect to a normal vector to the readily heat-conducting surface is 55% or more relative to a whole amount of the scaly graphite powder, andthe metal-graphite two-dimensionally thermally-conductive composite material has a relative density of 95% or higher. 2. The metal-graphite two-dimensionally thermally-conductive composite material according to claim 1, wherein the scaly graphite powder has a d002 value of a graphite crystal in a range of 0.3345 nm to 0.3360 nm as measured by X-ray diffraction. 3. The metal-graphite two-dimensionally thermally-conductive composite material according to claim 1, wherein the scaly graphite powder has an average aspect ratio of 10 to 100. 4. The metal-graphite two-dimensionally thermally-conductive composite material according to claim 1, wherein the scaly graphite powder has an average particle size of 50 μm to 1000 μm. 5. The metal-graphite two-dimensionally thermally-conductive composite material according to claim 1, further comprising any one of a carbon fiber and a carbon nanofiber. 6. A production method for a metal-graphite two-dimensionally thermally-conductive composite material, comprising the steps of: (1) obtaining a powder mixture by mixing a scaly graphite powder with a scaly powder of a matrix selected from the group consisting of copper, aluminium and alloys thereof;(2) forming a sintering precursor by use of the powder mixture; and(3) sintering the sintering precursor with uniaxial pressing being performed, whereinstep (3) is carried out by a method selected from the group consisting of a hot pressing method, a pulse electric current sintering method, and a hot isostatic pressing sintering method in combination with a mold stretchable in a uniaxial direction;the scaly graphite powder accounts for 20 to 80% by volume of the metal-graphite two-dimensionally thermally-conductive composite material,the metal-graphite two-dimensionally thermally-conductive composite material has a relative density of 95% or higher, anda ratio of the scaly graphite powder in which a normal vector to a scaly surface is tilted at 20° or higher with respect to a direction vector of the uniaxial pressing in step (3) is 12% or less relative to a whole amount of the scaly graphite powder, andthe scaly graphite powder in which a normal vector to a scaly surface is tilted at 10° or less with respect to a normal vector to the readily heat-conducting surface is 55% or more relative to a whole amount of the scaly graphite powder. 7. The production method for a metal-graphite two-dimensionally thermally-conductive composite material according to claim 6, wherein the scaly graphite powder has a d002 value of a graphite crystal in a range of 0.3345 nm to 0.3360 nm as measured by X-ray diffraction. 8. The production method for a metal-graphite two-dimensionally thermally-conductive composite material according to claim 6, wherein the scaly graphite powder has an average aspect ratio of 10 to 100, andthe scaly powder of the matrix has an average aspect ratio of 10 to 100. 9. The production method for a metal-graphite two-dimensionally thermally-conductive composite material according to claim 6, wherein the scaly graphite powder has an average particle size of 50 μm to 1000 μm. 10. The production method for a metal-graphite two-dimensionally thermally-conductive composite material according to claim 6, further comprising the step of adding any one of a carbon fiber and a carbon nanofiber to the powder mixture. 11. The production method for a metal-graphite two-dimensionally thermally-conductive composite material according to claim 6, wherein step (2) is performed by repeating, one or more times, steps of:(2a) filling the powder mixture into a mold; and(2b) uniaxially pressing the powder mixture thus filled, anda thickness, in a direction of the uniaxial pressing in step (2b), of the sintering precursor obtained by a single sequence of steps (2a) and (2b) is 5 mm or smaller. 12. The production method for a metal-graphite two-dimensionally thermally-conductive composite material according to claim 6, wherein step (2) is performed by steps of:(2c) forming a slurry by mixing the powder mixture with a liquid medium;(2d) spreading the slurry on a substrate by a doctor blade method; and(2e) removing the liquid medium therefrom, anda thickness of a sintering precursor obtained through steps (2c) to (2e) is 5 mm or smaller. 13. A metal-graphite two-dimensionally thermally-conductive composite material produced by the production method according to claim 6. 14. A metal-graphite two-dimensionally thermally-conductive composite material produced by the production method according to claim 7. 15. A metal-graphite two-dimensionally thermally-conductive composite material produced by the production method according to claim 8. 16. A metal-graphite two-dimensionally thermally-conductive composite material produced by the production method according to claim 9. 17. A metal-graphite two-dimensionally thermally-conductive composite material produced by the production method according to claim 10. 18. A metal-graphite two-dimensionally thermally-conductive composite material produced by the production method according to claim 11. 19. A metal-graphite two-dimensionally thermally-conductive composite material produced by the production method according to claim 12.