초록 ▼

Fluoroelastomeric gel having the following properties: appearance: transparent gelatinous solid;water content between 10% and 90% by weight;a density between 1.1 and 2.1 g/cm3; said gel satisfies the following test: dried in a stove at 90° C. until a constant weight gives curable fluoroelastomers.

Fluoroelastomeric gel having the following properties: appearance: transparent gelatinous solid;water content between 10% and 90% by weight;a density between 1.1 and 2.1 g/cm3; said gel satisfies the following test: dried in a stove at 90° C. until a constant weight gives curable fluoroelastomers.

대표청구항 ▼

1. Fluoroelastomeric gel comprising a fluoroelastomeric latex, and having the following properties: appearance: transparent gelatinous solid;water content between 10% and 90% by weight; anddensity between 1.1 and 2.1 g/cm3,wherein said gel comprises a VDF-based fluoroelastomer mixed with at least on

1. Fluoroelastomeric gel comprising a fluoroelastomeric latex, and having the following properties: appearance: transparent gelatinous solid;water content between 10% and 90% by weight; anddensity between 1.1 and 2.1 g/cm3,wherein said gel comprises a VDF-based fluoroelastomer mixed with at least one (per)fluorinated comonomer having at least one ethylene-type unsaturation, wherein said (per)fluorinated comonomer is a fluorinated comonomer that is optionally perfluorinated,wherein said gel is not crosslinked in its uncured state,wherein when said gel is dried in a stove at 90° C. until it reaches a constant weight, it gives a curable fluoroelastomer, andwherein said gel is obtained by a process comprising the steps of combining a fluoroelastomeric latex with an aqueous solution at a temperature lower than or equal to the glass transition temperature of the fluoroelastomeric latex to form the fluoroelastomeric gel, wherein said aqueous solution comprises an electrolyte and one or more organic compounds, wherein said one or more organic compounds are soluble in the fluoroelastomeric latex and are capable of lowering the freezing point of the fluoroelastomeric latex, and wherein said one or more organic compounds are either the fluorinated comonomer or a different organic compound;and optionally washing the fluoroelastomeric gel with water. 2. Fluoroelastomeric gel according to claim 1, wherein the (per)fluorinated comonomer is selected from the following: CF2═CFORf (per)fluoroalkylvinylethers (PAVE), wherein Rf is a C1-C6 (per)fluoroalkyl;CF2═CFOX (per)fluoro-oxyalkylvinylethers, wherein X is a C1-C12 (per)fluorooxyalkyl, having one or more ether groups;(per)fluorodioxoles;(per)fluorovinylethers (MOVE) of formula CFXAI═CXAIOCF2ORAI wherein RAI is a C2-C6 linear, branched or C5-C6 cyclic perfluoroalkyl group, or a C2-C6 linear, branched perfluorooxyalkyl group containing from one to three oxygen atoms; RAI can optionally contain from 1 to 2 atoms, equal or different, selected from the following: Cl, Br, I; XAI═F;C2-C8 (per)fluoroolefins;C2-C8 fluoroolefins optionally containing one or more chlorine, bromine, or iodine atoms; and(per)fluorovinylethers containing hydrocyanic groups. 3. Fluoroelastomeric gel according to claim 1, wherein the monomeric compositions of the fluoroelastomers are the following, the sum of the comonomer per cent (by moles) being 100%: (a) VDF 45-85%, HFP 15-45%, TFE 0-30%;(b) VDF 50-80%, PAVE 5-50%, TFE 0-20%;(c) VDF 20-30%, OI 10-30%, HFP and/or PAVE 18-27%, TFE 10-30%;(d) TFE 45-65%, OI 20-55%, VDF 0-30%;(e) TEE 33-75%, PAVE 15-45%, VDF 5-30%;(f) VDF 45-85%, MOVE 1 5-50%, PAVE 0-50%; HFP 0-30%, TFE 0-30%;(g) VDF 45-85%, MOVE 2 5-50%, PAVE 0-50%; HFP 0-30%, TFE 0-30%;(h) VDF 45-85%, MOVE 2 5-50%, MOVE 1 5-50%, PAVE 0-50%; HFP 0-30%, TFE 0-30%. 4. Fluoroelastomeric gel according to claim 1, wherein the fluoroelastomers comprise also monomeric units deriving from a bis-olefin of general formula: wherein: R1, R2, R3, R4, R5, R6, equal to or different from each other, are H or C1-C5 alkyls;Z is a C1-C18 linear or branched alkylene or cycloalkylene radical, optionally containing oxygen atoms or a (per)fluoropolyoxyalkylene radical. 5. Fluoroelastomeric gel according to claim 4, wherein, in formula (I), when Z is a C4-C12, perfluoroalkylene radical; R1, R2, R3, R4, R5, R6 are hydrogen;when Z is a (per)fluoropolyoxyalkylene radical, it comprises units selected from the following: —CF2CF2O—, —CF2CF(CF3)O—,—CF2CF2CF2O—, —CF2—CH2CH2O—,—CF(CF3)CF2O—, or —CFX1O—wherein X1 is selected from the group consisting of F and CF3. 6. Fluoroelastomeric gel according to claim 4, wherein Z has formula: -(Q)p-CF2O—(CF2CF2O)m(CF2O)n—CF2-(Q)p-  (II) wherein: Q is a C1-C10 alkylene or oxyalkylene radical; p is 0 or 1; m and n are numbers such that the m/n ratio is between 0.2 and 5 and the molecular weight of said (per)fluoropolyoxyalkylene radical is in the range 500-10,000. 7. Fluoroelastomeric gel according to claim 6 wherein Q is selected from: —CH2OCH2—; —CH2O(CH2CH2O)sCH2—, s being=1-3. 8. Fluoroelastomeric gel according to claim 4, wherein the unit amount in the chain deriving from the bis-olefins of formula (I) is from 0.01 to 1.0 moles per 100 moles of the other monomeric units constituting the basic fluoroelastomer structure. 9. Fluoroelastomeric gel according to claim 1, containing a semicrystalline (per)fluoropolymer, in an amount in per cent by weight referred to the total of dry weight fluoroelastomer+semicrystalline (per)fluoropolymer, from 0% to 70% by weight. 10. Fluoroelastomeric gel according to claim 9, wherein the semicrystalline (per)fluoropolymer is constituted by tetrafluoroethylene (TFE) homopolymers, or TFE copolymers with one or more monomers containing at least one unsaturation of ethylene type, in an amount from 0.01% to 10% by moles on the total of the monomer moles. 11. Fluoroelastomeric gel according to claim 10, wherein the comonomers having an ethylene unsaturation of the semicrystalline (per)fluoropolymer are both hydrogenated and fluorinated. 12. Fluoroelastomeric gel according to claim 11, wherein the hydrogenated comonomers having an ethylene unsaturation are selected from ethylene, propylene, acrylic monomers, selected from methylmethacrylate, (meth)acrylic acid, butylacrylate, hydroxyethylhexylacrylate, styrene monomers. 13. Fluoroelastomeric gel according to claim 11, wherein the fluorinated comonomers having an ethylene unsaturation are selected from the following: C3-C8 perfluoroolefins;C2-C8 hydrogenated fluoroolefins;C2-C8 chloro- and/or bromo- and/or iodo-fluoroolefins;CF2═CFORf (per)fluoroalkylvinylethers (PAVE), wherein Rf is a C1-C6 (per)fluoroalkyl;CF2═CFOX (per)fluoro-oxyalkylvinylethers, wherein X is: a C1-C12 alkyl, or a C1C12 oxyalkyl, or a C1-C12 (per)fluoro-oxyalkyl having one or more ether groups; (per)fluorodioxoles. 14. Fluoroelastomeric gel according to claim 10, wherein the comonomers of the semicrystalline (per)fluoropolymer are selected from PAVE and (per)fluorodioxoles. 15. Fluoroelastomeric gel according to claim 10, wherein the semicrystalline (per)fluoropolymer is coated by a shell of a semicrystalline (per)fluoropolymer containing bromine and/or iodine atoms in the chain deriving from brominated and/or iodinated comonomers, in an amount from 0.1% to 10% by moles referred to the total moles of the basic monomeric units of the semicrystalline (per)fluoropolymer core+shell, the semicrystalline (per)fluoropolymer in the core and in the shell can be of different composition. 16. Fluoroelastomeric gel according to claim 2, wherein the (per)fluorodioxoles are perfluorodioxoles. 17. Fluoroelastomeric gel according to claim 2, wherein the (per)fluorovinylethers (MOVE) of formula CFXAI═CXAIOCF2ORAI are selected from (MOVE 1) CF2═CFOCF2OCF2CF3 and (MOVE 2) CF2═CFOCF2OCF2CF2OCF3. 18. Fluoroelastomeric gel according to claim 2, wherein the C2-C3 (per)fluoroolefins are selected from tetrafluoroethylene, hexafluoropropene, hydropentafluoropropene, and vinyl fluoride. 19. Fluoroelastomeric gel according to claim 4, wherein when Z a C1-C18 linear or branched alkylene or cycloalkylene radical, Z is at least partially fluorinated. 20. Fluoroelastomeric gel according to claim 5, wherein, in formula (I), when Z is a C4-C8 perfluoroalkylene radical; R1, R2, R3, R4, R5, R6 are hydrogen. 21. Fluoroelastomeric gel according to claim 6, wherein the molecular weight of said (per)fluoropolyoxyalkylene radical is in the range 700-2,000. 22. Fluoroelastomeric gel according to claim 8, wherein the unit amount in the chain deriving from the bis-olefins of formula (I) is from 0.03 to 0.5 moles per 100 moles of the other monomeric units constituting the basic fluoroelastomer structure. 23. Fluoroelastomeric gel according to claim 22, wherein the unit amount in the chain deriving from the bis-olefins of formula (I) is from 0.05 to 0.2 moles per 100 moles of the other monomeric units constituting the basic fluoroelastomer structure. 24. Fluoroelastomeric gel according to claim 9, containing a semicrystalline (per)fluoropolymer, in an amount in per cent by weight referred to the total of dry weight fluoroelastomer semicrystalline perfluoropolymer, from 0% to 50% by weight. 25. Fluoroelastomeric gel according to claim 24, containing a semicrystalline (per)fluoropolymer, in an amount in per cent by weight referred to the total of dry weight fluoroelastomer+semicrystalline perfluoropolymer, from 2% to 30% by weight. 26. Fluoroelastomeric gel according to claim 10, wherein the semicrystalline (per)fluoropolymer is constituted by tetrafluoroethylene (TFE) homopolymers, or TFE copolymers with one or more monomers containing at least one unsaturation of ethylene type, in an amount from 0.05% to 7% by moles on the total of the monomer moles. 27. Fluoroelastomeric gel according to claim 13, wherein the C3-C8 perfluoroolefins are selected from hexafluoropropene (HFP) and hexafluoroisobutene. 28. Fluoroelastomeric gel according to claim 13, wherein the C2-C8 hydrogenated fluoroolefins are selected from vinyl fluoride (VF), vinylidene fluoride (VDF), trifluoro-ethylene, and CH2═CH—Rf perfluoroalkylethylene, wherein Rf is a C1-C6 perfluoroalkyl. 29. Fluoroelastomeric gel according to claim 13, wherein the C2-C8 chloro-fluoroolefins are chlorotrifluoroethylene (CTFE). 30. Fluoroelastomeric gel according to claim 13, wherein Rf is a C1-C6 (per)fluoroalkyl selected from CF3, C2F5, and C3F7. 31. Fluoroelastomeric gel according to claim 13, wherein the (per)fluorodioxoles are perfluorodioxoles. 32. Fluoroelastomeric gel according to claim 14, wherein PAVE is selected from perfluoromethyl-, perfluoroethyl-, and perfluoropropylvinylether. 33. Fluoroelastomeric gel according to claim 14, wherein (per)fluorodioxoles are perfluorodioxoles. 34. Curable fluoroelastomers obtained from the fluoroelastomeric gel of claim 1. 35. Cured fluoroelastomers obtained by crosslinking the fluoroelastomers according to claim 34. 36. Cured fluoroelastomers obtained by crosslinking the fluoroelastomers according to claim 34, wherein crosslinking is of peroxidic type. 37. Cured fluoroelastomers obtained by crosslinking the fluoroelastomers according to claim 34, wherein crosslinking is of ionic type, optionally ionic-peroxidic type. 38. Manufactured articles comprising the cured fluoroelastomers according to claim 35.