초록 ▼

A method for producing an optical fiber preform. Glass soot particles are formed by jetting and combusting a gaseous glass-forming material and a fuel gas from a burner in the presence of oxygen. The glass soot particles are deposited on a deposition rod while rotating the deposition rod about its a

A method for producing an optical fiber preform. Glass soot particles are formed by jetting and combusting a gaseous glass-forming material and a fuel gas from a burner in the presence of oxygen. The glass soot particles are deposited on a deposition rod while rotating the deposition rod about its axis and reciprocating the burner in parallel to the deposition rod so as to form the preform and varying at least one of the translation velocity of the burner and the rotation velocity of the rod so as to obtain a predetermined radial soot density distribution in the preform.

대표청구항 ▼

1. A method for producing an optical fiber preform, comprising: forming glass soot particles by jetting and combusting a glass-forming material and a fuel gas from a burner in the presence of oxygen;depositing in a plurality. of deposition passes. a plurality of deposition layers comprised of said g

1. A method for producing an optical fiber preform, comprising: forming glass soot particles by jetting and combusting a glass-forming material and a fuel gas from a burner in the presence of oxygen;depositing in a plurality. of deposition passes. a plurality of deposition layers comprised of said glass soot particles on a deposition rod having a longitudinal axis, each of said plurality of deposition layers being deposited by rotating said deposition rod about said longitudinal axis at a rotational velocity while translating said burner relative to said deposition rod in parallel to said longitudinal axis at a translation velocity; andproviding said preform with a density distribution that is substantially uniform in a radial direction such that each of said plurality of deposition layers has a density between about 0.4 g/cm3 and about 1.0 g/cm3, by varying at least one of said translation velocity and said rotational velocity, said varying at least one of said translation velocity and said rotational velocity occurring only between deposition passes,wherein the same translation velocity is used throughout deposition of each of the plurality of deposition layers. 2. A method for producing an optical fiber preform, comprising: forming glass soot particles by jetting and combusting a glass-forming material and a fuel gas from a burner in the presence of oxygen;depositing the glass soot particles on the deposition rod;depositing, in a plurality of deposition passes, a plurality of deposition layers comprised of said glass soot particles on a deposition rod having a longitudinal axis, each of said plurality of deposition layers being deposited by rotating said deposition rod about said longitudinal axis at a rotational velocity while translating said burner relative to said deposition rod in parallel to said longitudinal axis at a translation velocity; andproviding said preform with a density distribution that is substantially uniform in a radial direction, such that each of said plurality of deposition layers has a density between about 0.4 g/cm3 and about 1.0 g/cm3, by progressively increasing at least one of said translation velocity and said rotational velocity to a respective top value, said progressive increasing occurring only between deposition passes, and, thereafter, progressively decreasing said at least one of said translation velocity and said rotational velocity as a diameter of said preform grows with said depositing of said plurality of deposition layers, said progressive decreasing occurring only between deposition passes. 3. A method according to claim 2, comprising increasing both of said translation velocity and rotational velocity to a respective top value. 4. A method according to claim 2, comprising, after increasing at least one of said translation velocity and said rotational velocity to a respective top value, decreasing both of said translation velocity and rotational velocity so as to provide the preform with a density distribution that is substantially uniform in the radial direction. 5. A method according to claim 2, comprising increasing at least one of said translation velocity and said rotational velocity to a respective top value between depositing of deposition layers and, thereafter, decreasing at least one of said translation velocity and said rotational velocity between deposition passes so as to provide the preform with a density between about 0.4 g/cm3 and below about 1.0 g/cm3 in the radial direction in each of the plurality of deposition layers.