초록 ▼

The present invention relates to a back sheet for solar cell and a method of manufacturing the same. The back sheet for solar cell comprises a substrate and a fluoropolymer layer, wherein the components by weight of the fluoropolymer layer are as follows: 25˜45 parts of fluororesin; 1.5˜3 parts of m

The present invention relates to a back sheet for solar cell and a method of manufacturing the same. The back sheet for solar cell comprises a substrate and a fluoropolymer layer, wherein the components by weight of the fluoropolymer layer are as follows: 25˜45 parts of fluororesin; 1.5˜3 parts of modified resin; 0.5˜3 parts of polymeric filler; 0.1˜1 parts of inorganic filler; and 50˜70 parts of solvent. The back sheet for solar cell provided by the present invention has low cost and excellent performances, such as high peeling strength, good waterproof performance, and good weathering resistance. The method of manufacturing the back sheet for solar cell provided by the present invention is simple in process, and thus can achieve continuous industrial production.

대표청구항 ▼

1. A back sheet for solar cell comprising a substrate and a fluoropolymer layer, wherein components of a fluoropolymer liquid coating composition formulation for preparing the fluoropolymer layer by weight consist of: Fluororesin25~45parts;Modified resin1.5~3parts;Polymeric filler0.5~3parts;Inorgani

1. A back sheet for solar cell comprising a substrate and a fluoropolymer layer, wherein components of a fluoropolymer liquid coating composition formulation for preparing the fluoropolymer layer by weight consist of: Fluororesin25~45parts;Modified resin1.5~3parts;Polymeric filler0.5~3parts;Inorganic filler0.1~1part;Solvent50~70parts;wherein said modified resin is poly(vinylidene fluoride-tetrafluoroethylene-hexafluoropropylene) resin modified by a carboxylic group, a sulfonic group, an azacyclopropane group, an isocyanate group, an epoxy group, an amino group, a hydroxyl group, or an active methylene group. 2. The back sheet for solar cell according to claim 1, wherein said fluororesin is a homopolymer of vinylidene fluoride, tetrafluoroethylene, or hexafluoropropylene, or a copolymer thereof. 3. The back sheet for solar cell according to claim 1, wherein said inorganic fillers comprise one or more of the oxides of titanium, aluminum, tin, and silicon. 4. The back sheet for solar cell according to claim 2, wherein said inorganic fillers comprise one or more of the oxides of titanium, aluminum, tin, and silicon. 5. The back sheet for solar cell according to claim 1, wherein said solvent is one or more of toluene, methyl ethyl ketone, ethyl acetate, and butyl acetate. 6. The back sheet for solar cell according to claim 2, wherein said solvent is one or more of toluene, methyl ethyl ketone, ethyl acetate, and butyl acetate. 7. The back sheet for solar cell according to claim 1, wherein the thickness of said fluoropolymer layer is 25˜50 μm. 8. The back sheet for solar cell according to claim 2, wherein the thickness of said fluoropolymer layer is 25˜50 μm. 9. A method of manufacturing the back sheet for solar cell according to claim 1, wherein the fluoropolymer layer is coated on the surface of the substrate and cured to obtain the back sheet for solar cell. 10. The method of manufacturing the back sheet for solar cell according to claim 9, wherein the fluoropolymer layer is applied onto the substrate by immersion coating method, air blade coating method, blade coating method, gravure coating method, or slit coating method. 11. The method of manufacturing the back sheet for solar cell according to claim 9, wherein the fluoropolymer layer is cured by crosslinking the fluoropolymer layer through ultraviolet irradiation, or cured by crosslinking the fluoropolymers through high-energy radiation using X-ray, cobalt 60, an electrostatic accelerator, or a high-power electron linear accelerator as an irradiation source. 12. The method of manufacturing the back sheet for solar cell according to claim 9, wherein the thickness of said fluoropolymer layer on the substrate is 25˜50 μm after curing. 13. The method of manufacturing the back sheet for solar cell according to claim 10, wherein the thickness of said fluoropolymer layer on the substrate is 25˜50 μm after curing. 14. The method of manufacturing the back sheet for solar cell according to claim 11, wherein the thickness of said fluoropolymer layer on the substrate is 25˜50 μm after curing.