초록 ▼

A wear resistant multilayer nitride hard coating for substrates. The hard coating includes a first layer of titanium aluminum nitride and a second layer comprising a plurality of sublayer groups. Each sublayer group includes a first sublayer of titanium silicon nitride and a second sublayer of titan

A wear resistant multilayer nitride hard coating for substrates. The hard coating includes a first layer of titanium aluminum nitride and a second layer comprising a plurality of sublayer groups. Each sublayer group includes a first sublayer of titanium silicon nitride and a second sublayer of titanium aluminum nitride. The composition of the titanium aluminum nitride, both in the first layer and in the sublayer groups, is (TixAl1-x)N, wherein 0.4≦x≦0.6. The composition of the titanium silicon nitride sublayers is (TiySi1-y)N, wherein 0.85≦y≦0.98, and all of the silicon is in solid solution in the titanium silicon nitride such that no silicon phase or silicon nitride phase exists in this sublayer. The combined amount of aluminum and silicon present in the sublayer groups being narrowly controlled such that the sum of x and y is in the range of 1.38 to 1.46.

대표청구항 ▼

1. A hard coating for a substrate comprising: a first layer deposited by physical vapor deposition comprising (TizAl1-z)N, wherein 0.4≦z≦0.6; anda second layer deposited by physical vapor deposition having a plurality of sublayer groups, a sublayer group comprising a first sublayer of (TiySi1-y)N, w

1. A hard coating for a substrate comprising: a first layer deposited by physical vapor deposition comprising (TizAl1-z)N, wherein 0.4≦z≦0.6; anda second layer deposited by physical vapor deposition having a plurality of sublayer groups, a sublayer group comprising a first sublayer of (TiySi1-y)N, wherein 0.85≦y≦0.98, and a second sublayer of (TixAl1-x)N, wherein 0.4≦x≦0.6;wherein neither a pure silicon phase nor a pure silicon nitride phase is present in the first sublayer and the sum or x and y is in the range of 1.38 to 1.46. 2. The hard coating of claim 1, wherein the first layer accounts for 20 to 60 percent of the overall coating thickness. 3. The hard coating of claim 1, wherein the thickness of the sublayer group is in the range of 3 to 20 nm. 4. The hard coating of claim 1, wherein the sublayer groups are adjacently stacked. 5. The hard coating of claim 1, wherein x and z are substantially equal in value. 6. The hard coating of claim 1, wherein x and z are different in value. 7. The hard coating of claim 1, wherein the (TizAl1-z)N of the first layer Comprises hexagonal close-packed phase in addition to face-centered cubic phase. 8. The hard coating of claim 1, wherein the (TixAl1-x)N of at least one second sublayer comprises hexagonal close-packed phase in addition to face-centered cubic phase. 9. The hard coating of claim 1, wherein a sublayer group has a ratio of thickness of the first sublayer to thickness of the second sublayer in a range of 0.2 to 2.0. 10. The hard coating of claim 1, wherein the sum of x and y is in the range of 1.39 to 1.45. 11. The hard coating of claim 1, having a thickness of 2 to 6 μm. 12. The hard coating of claim 1, wherein the first layer and the second layer are adjacent to one another. 13. The hard coating of claim 1 further comprising one or more additional layers comprising TiN or CrN. 14. The hard coating of claim 13 wherein a TiN layer is interposed between the substrate and the first layer. 15. The hard coating of claim 1 further comprising one or more additional layers selected from the group consisting of TiAlCrN, AlCrN, TiAlSiN, AlCrSiN and TiAlCrSiN. 16. The hard coating of claim 1 having a hardness according to ISO 14577 of 30.8 GPa to 33.6 GPa. 17. A hard coated article comprising: an article having a surface; anda hard coating covering at least a portion of the surface, the hard coating comprising:a first layer deposited by physical vapor deposition comprising (TizAl1-z)N, wherein 0.4≦z≦0.6; anda second layer deposited by physical vapor deposition having a plurality of sublayer groups, a sublayer group comprising a first sublayer of (TiySi1-y)N, wherein 0.85≦y≦0.98, and a second sublayer of (TixAl1-x)N, wherein 0.4≦x≦0.6;wherein neither a pure silicon phase nor a pure silicon nitride phase is present in the first sublayer and the sum or x and y is in the range of 1.38 to 1.46. 18. The hard coated article of claim 17, wherein the first layer accounts for 20 to 60 percent of the overall coating thickness. 19. The hard coated article of claim 17, wherein the thickness of the sublayer group is in the range of 3 to 20 nm. 20. The hard coated article of claim 17, wherein the sublayer groups are adjacently stacked. 21. The hard coated article of claim 17, wherein x and z are substantially equal in value. 22. The hard coated article of claim 17, wherein x and z are different in value. 23. The hard coated article of claim 17, wherein the (TizAl1-z)N of the first layer comprises hexagonal close-packed phase in addition to face-centered cubic phase. 24. The hard coated article of claim 17, wherein the (TixAl1-x)N of at least one second sublayer comprises hexagonal close-packed phase in addition to face-centered cubic phase. 25. The hard coated article of claim 17, wherein a sublayer group has a ratio of thickness of the first sublayer to thickness of the second sublayer in a range of 0.2 to 2.0. 26. The hard coated article of claim 17, wherein the sum of x and y is in the range of 1.39 to 1.45. 27. The hard coated article of claim 17, wherein the first layer and the second layer are adjacent to one another. 28. The hard coated article of claim 17 further comprising one or more additional layers comprising TiN or CrN. 29. The hard coated article of claim 17 further comprising one or more additional layers selected from the group consisting of TiAlCrN, AlCrN, TiAlSiN, AlCrSiN and TiAlCrSiN. 30. The hard coated article of claim 17, wherein the article is selected from the group consisting of a cutting tool and a wear component. 31. The hard coated article of claim 30, wherein the article is selected from the group consisting of drills, end mills and indexable cutting inserts. 32. The hard coated article of claim 17, wherein the article comprises cemented carbide, cermet, steel, cubic boron nitride, polycrystalline diamond, silicon nitride, alumina or titanium aluminum nitride.