초록 ▼

Ceramic materials with a matrix which contains at least one carbide, at least one carbide-forming element and carbon, and which furthermore contain a dispersed phase of carbon particles with spherical shape and an average diameter of 0.2 μm to 800 μm, a process for their production and their use for

Ceramic materials with a matrix which contains at least one carbide, at least one carbide-forming element and carbon, and which furthermore contain a dispersed phase of carbon particles with spherical shape and an average diameter of 0.2 μm to 800 μm, a process for their production and their use for thermal insulation, as a protective layer in ceramic armoring against mechanical action, or as a friction layer in brake disks or clutch disks.

대표청구항 ▼

1. Process for producing ceramic materials, comprising in sequence: preparing a mixture containing carbon particles with a spherical shape and an average diameter of 0.2 μm to 800 μm, and a binder selected from artificial resins and pitches and optionally fibers of carbon with a diameter from 4 μm t

1. Process for producing ceramic materials, comprising in sequence: preparing a mixture containing carbon particles with a spherical shape and an average diameter of 0.2 μm to 800 μm, and a binder selected from artificial resins and pitches and optionally fibers of carbon with a diameter from 4 μm to 12 μm and a length from 0.1 mm to 48 mm;compacting the mixture into an essentially pore-free body;carbonizing the body by heating to a temperature from 750° C. to 1300° C. into a porous carbon body; andconverting the porous carbon body with a carbide-forming element or a mixture of several carbide-forming elements at a temperature in the range of the melting point of the carbide-forming element or a mixture of these several carbide-forming elements to a temperature of 500 K above the indicated melting point, at least 10% of the mass of the carbon in the carbon body being reacted into carbide. 2. The process according to claim 1, wherein the mixture of the compacting step additionally contains silicon powder with a grain size from 0.05 mm to 2 mm. 3. The process according to claim 2, wherein the silicon is used as a carbide-forming element. 4. The process according to claim 1, wherein silicon is used as a carbide-forming element. 5. The process according to claim 1, wherein the volumetric proportion of the dispersed carbon particles is 5% to 73% of the volume of the ceramic materials. 6. The process according to claim 1, wherein the carbon particles have been obtained by carbonization of polymerizates which can be produced by bead polymerization. 7. The process according to claim 1, wherein the carbon particles have been obtained by carbonization of ion exchanger materials in spherical form. 8. The process according to claim 7, wherein the ion exchanger materials with cations are selected from the group of cations consisting of sodium, potassium, magnesium, calcium, strontium, aluminum, lead, titanium, zirconium, and hafnium, or with anions selected from borates, aluminates, silicates, titanates, and phosphates. 9. The process according to claim 1, wherein the carbon particles have a bimodal size distribution. 10. The process according to claim 9, wherein the bimodal size distribution comprises large carbon particles and small carbon particles, wherein the large carbon particles have an average particle diameter of from 100 μm to 150 μm, and wherein the small particles fit into a wedge formed between adjacent large particles. 11. The process according to claim 1, wherein the carbon particles with a spherical shape are characterized in that each one of the carbon particles can be circumscribed by an outer ellipsoid and inscribed by an inner ellipsoid, wherein the outer ellipsoid is the smallest triaxial ellipsoid that can be circumscribed around any one of the carbon particles and has semiaxes that do not differ in length by more than 20%; the inner ellipsoid is the largest triaxial ellipsoid that can be inscribed within any one of the carbon particles and has semiaxes that do not differ in length by more than 20%; the centers of the outer ellipsoid and the inner ellipsoid are at a distance from one another that is no more than 25% of the length of the largest semiaxis of the outer ellipsoid; and the lengths of the corresponding semiaxes of the inner and outer ellipsoids differ by no more than 25% of the respective greater length.