초록 ▼

A method for regenerating a solid filter containing iodine in the form of silver iodide and/or iodate and possibly molecular iodine physisorbed, in a solid filter containing silver in the form of nitrate. The iodine is extracted from the filter by putting the filter into contact with a basic aqueous

A method for regenerating a solid filter containing iodine in the form of silver iodide and/or iodate and possibly molecular iodine physisorbed, in a solid filter containing silver in the form of nitrate. The iodine is extracted from the filter by putting the filter into contact with a basic aqueous solution containing a reducing agent. The extraction is achieved at room temperature, and then the filter is separated from this basic aqueous solution. Next, silver is extracted from the filter by putting the filter into contact with an acid aqueous solution. The filter is then separated from the acid aqueous solution. Finally, the filter is impregnated with silver by putting the filter into contact with a silver nitrate solution and then drying the filter. This method can be used in nuclear installations, notably factories for reprocessing used nuclear fuels.

대표청구항 ▼

1. A method for regenerating a solid filter containing iodine in the form of silver iodide and/or iodate and possibly molecular iodine physisorbed, in a solid filter containing silver in the form of nitrate, which comprises the following steps: a) extracting the iodine contained in the filter by put

1. A method for regenerating a solid filter containing iodine in the form of silver iodide and/or iodate and possibly molecular iodine physisorbed, in a solid filter containing silver in the form of nitrate, which comprises the following steps: a) extracting the iodine contained in the filter by putting the filter into contact with a basic aqueous solution containing a reducing agent, at room temperature, and then separating the filter from the basic aqueous solution;b) extracting the silver contained in the filter obtained in step a) by putting the filter into contact with an acid aqueous solution, and then separating the filter from the acid aqueous solution; andc) impregnating the filter obtained in step b) with silver by putting the filter into contact with a silver nitrate solution, and then drying the filter. 2. The method according to claim 1, wherein the reducing agent used in step a) is ascorbic acid or a salt thereof. 3. The method according to claim 1, wherein the basis aqueous solution used in step a) comprises from 0.5 to 2 mol/L of ascorbic acid or of a salt thereof and has a pH from 10 to 14. 4. The method according to claim 1, wherein the acid aqueous solution used in step b) is a nitric acid solution having a nitric acid concentration from 0.2 to 6 mol/L. 5. The method according to claim 1, wherein step b) further comprises, after separating the filter from the acid aqueous solution, drying the filter for 5 to 24 hours, in air in an oven or under a partial vacuum at a temperature below 120° C., and then optionally under an inert gas at a temperature from 120 to 500° C. 6. The method according to claim 1, wherein the silver nitrate solution used in step c) is the acid aqueous solution obtained at the end of step b), after adjusting, if necessary, the silver content and/or the acidity of said acid aqueous solution. 7. The method according to claim 1, wherein the silver nitrate solution used in step c) has a silver concentration from 20 to 200 g/L. 8. The method according to claim 1, wherein the drying of the filter provided in step c) is carried out at a temperature below 120° C., at atmospheric pressure or under a partial vacuum. 9. The method according to claim 1, wherein the filter contains 12% by mass of elementary silver in the form of nitrate at the end of step c). 10. The method according to claim 1, wherein the filter comprises a porous mineral solid support selected from the group consisting of porous silica or alumina beads.