초록 ▼

A hydrated water-absorption polymer containing resin composition includes a liquid cross-link curable resin composition, and a water-absorption polymer dispersed in the liquid cross-link curable resin composition. The water-absorption polymer is preliminarily hydrated and swollen. The water-absorpti

A hydrated water-absorption polymer containing resin composition includes a liquid cross-link curable resin composition, and a water-absorption polymer dispersed in the liquid cross-link curable resin composition. The water-absorption polymer is preliminarily hydrated and swollen. The water-absorption polymer before being hydrated and swollen includes an average particle diameter of not more than 10 μm. The water-absorption polymer includes an amount of water absorption of 10 to 100 g/g.

대표청구항 ▼

1. A method of making an insulated wire, said method comprising: coating a perimeter of a conductor with a liquid crosslink-curable resin composition containing an aqueous absorbent polymer dispersed therein to provide an insulating layer around the conductor, the aqueous absorbent polymer comprisin

1. A method of making an insulated wire, said method comprising: coating a perimeter of a conductor with a liquid crosslink-curable resin composition containing an aqueous absorbent polymer dispersed therein to provide an insulating layer around the conductor, the aqueous absorbent polymer comprising a pre-absorbed water-swollen absorbent polymer;cross-linking the aqueous absorbent polymer-containing liquid crosslink-curable resin composition to provide a cured insulating layer; andheating the cured insulating layer to remove moisture in the aqueous absorbent polymer to faint voids in the insulating layer,wherein the aqueous absorbent polymer has an average particle diameter of 10 μm or less before swelling, an amount of water absorption of the aqueous absorbent polymer after swelling in a range from 10 g/g to 100 g/g, and the aqueous absorbent polymer-containing liquid crosslink-curable resin composition has a moisture content in a range from 25% to 65%, thereby a size and a shape of the voids in the insulated layer are controlled. 2. The method according to claim 1, wherein the aqueous absorbent polymer-containing liquid crosslink-curable resin composition is heated by a microwave. 3. The method according to claim 1, wherein an amount of the aqueous absorbent polymer is 0.1 parts by weight to 10 parts by weight in 100 parts by weight of the resin composition. 4. The method according to claim 1, wherein an amount of the aqueous absorbent polymer is 0.5 parts by weight to 3 parts by weight in 100 parts by weight of the resin composition. 5. The method according to claim 1, wherein the liquid crosslink-curable resin composition comprises an ultraviolet or a heat-curable liquid resin composition. 6. The method according to claim 1, wherein the insulating layer has a thickness of not more than 100 μm and a porosity of 20 to 60%. 7. The method according to claim 1, wherein each of the voids in the insulating layer is substantially circular in a cross section, has a maximum to minimum diameter ratio of not more than 2, and a diameter D in a thickness direction of D<½t, where t is a thickness of the insulating layer. 8. The method according to claim 1, wherein the size and the shape of the voids are adjusted by the average particle diameter and the amount of water absorption of the aqueous absorbent polymer. 9. The method according to claim 1, wherein said cross-linking comprises heating the insulating layer to form the cured insulating layer. 10. A method for making a porous material, the method comprising: dispersing a pre-absorbed water-swollen aqueous absorbent polymer into a liquid crosslink-curable resin composition to form a dispersed aqueous absorbent polymer-containing liquid crosslink-curable resin composition;coating the dispersed aqueous absorbent polymer-containing liquid crosslink-curable resin composition onto a sheet to provide an insulated layer around the sheet;crosslink-curing the dispersed aqueous absorbent polymer-containing liquid crosslink-curable resin composition to provide a cured aqueous absorbent polymer-containing resin composition; andsubsequently heating the cured aqueous absorbent polymer-containing resin composition to remove moisture in the aqueous absorbent polymer dispersed in the resin composition to form voids in the resin composition,wherein the aqueous absorbent polymer has an average particle diameter of 10 μm or less before swelling, an amount of water absorption of the aqueous absorbent polymer after swelling in a range from 10 g/g to 100 g/g, and the aqueous absorbent polymer-containing liquid crosslink-curable resin composition has a moisture content in a range from 25% to 65%, thereby a size and a shape of the voids in the insulated layer are controlled. 11. The method according to claim 10, wherein the liquid crosslink-curable resin composition comprises an ultraviolet or a heat-curable liquid resin composition. 12. The method according to claim 10, wherein the aqueous absorbent polymer-containing liquid crosslink-curable resin composition is heated by a microwave. 13. The method according to claim 10, wherein an amount of the aqueous absorbent polymer is 0.1 parts by weight to 10 parts by weight, relative to 100 parts by weight of the liquid crosslink-curable resin composition. 14. The method according to claim 10, wherein an amount of the aqueous absorbent polymer is 0.5 parts by weight to 3 parts by weight, relative to 100 parts by weight of the liquid crosslink-curable resin composition. 15. The method according to claim 10, wherein each of the voids in the insulating layer is substantially circular in a cross section, and has a diameter D in a thickness direction of D<½t, where t is a thickness of the resin composition.