초록
Fluoroelastomeric gel having the following properties: appearance: transparent gelatinous solid;water content between 10% and 90% by weight;density between 1.1 and 2.1 g/cm3; said gel satisfies the following test: dried in a stove at 90° C. until a constant weight gives curable fluoroelastomers.
대표청구항
▼
1. A process to form a fluoroelastomer gel having the following properties: appearance: transparent gelatinous solid; water content between 10 percent and 90 percent by weight; density between 1.1 and 2.1 g/cm3; said gel satisfies the following test: the gel subjected to drying in a stove at 90° C.
1. A process to form a fluoroelastomer gel having the following properties: appearance: transparent gelatinous solid; water content between 10 percent and 90 percent by weight; density between 1.1 and 2.1 g/cm3; said gel satisfies the following test: the gel subjected to drying in a stove at 90° C. until a constant weight gives a curable fluoroelastomer, said process comprising the following steps, starting from a fluoroelastomer polymerization latex:Ao. optionally, mixing of the fluoroelastomer latex with a semicrystalline (per)fluoropolymer latex, in an amount from 0 percent to 70 percent by weight, referred to the total of dry weight fluoroelastomer and semicrystalline (per)fluoropolymer;A. optionally, dilution with water of the polymerization latex of the fluoroelastomer, or of the mixture Ao, until obtaining a fluoroelastomer concentration, expressed in g polymer/kg latex, in the range 50-600;B. optionally, mixing of the polymerization latex Ao, or of the diluted latex A, or of the starting latex, with one or more organic compounds soluble in the latex aqueous phase, capable to lower the latex freezing point without causing the latex coagulation, said one or more organic compounds being such and/or in an amount such that the resulting mixture has the freezing point at a temperature lower than or equal to the glass transition temperature Tg (° C.) of the latex fluoroelastomer;C. preparation of an aqueous solution containing an electrolyte, optionally said solution being added with one or more organic compounds as defined in B, soluble in the latex aqueous phase, i.e. capable to lower the freezing point of the solution C, and such and/or in an amount such that the resulting solution C has a freezing point lower than or equal to the freezing point of the mixture prepared in B;D. cooling of the polymerization latex, or of the mixture Ao, or of the diluted latex A, or of the mixture B, until a temperature T1 lower than or equal to the glass transition temperature of the latex fluoroelastomer;E. cooling of the aqueous solution C at a temperature T2 lower than or equal to the glass transition temperature of the latex fluoroelastomer, or T2 being substantially equal to T1;F. formation of a gel by dripping of the mixture D into the solution E;G. optionally, washing with water of the gel obtained in F;H. optionally, gel drying and obtainment of the fluoroelastomer. 2. A process according to claim 1, wherein in step A the fluoroelastomer concentration in the latex, expressed in g polymer/kg of latex, is between 50 and 300. 3. A process according to claim 1, wherein step A is omitted when, after having carried out the optional step Ao, the fluoroelastomer concentration is, expressed in g polymer/kg latex, in the range 50-600. 4. A process according to claim 1, wherein the optional step A is carried out before the optional step Ao. 5. A process according to claim 1, wherein step B is optional when the fluoroelastomer has a glass transition temperature higher than 0° C. 6. A process according to claim 1, wherein organic compounds are used which lower the freezing point of at least 1°-2° C., with respect to the fluoroelastomer Tg. 7. A process according to claim 1, wherein the amount of the organic compounds as defined in B, in the mixtures prepared in B and in C, is from 5 percent to 70 percent, referred to the total weight of the mixture. 8. A process according to claim 1, wherein the organic compounds usable in steps B and C have a solubility in water higher than 1 percent w/w and are liquid at room temperature. 9. A process according to claim 8, wherein the organic compounds are selected from the group consisting of C1-C5 aliphatic alcohols, C3-C4 ketones, and diols selected between ethylene glycol and propylene glycol. 10. A process according to claim 1, wherein the electrolytes used in C are selected from the group consisting of inorganic salts, inorganic bases, and inorganic acids. 11. A process according to claim 1, wherein in step G the gel washing is carried out at temperatures between that used in step F and 800° C., and at the place of water, neutral and/or acid aqueous solutions having pH from 1 to 7 are optionally used. 12. A process according to claim 1, wherein at the end of step G the gel pH is brought to a value between 3 and 7. 13. A process according to claim 1, wherein in step H drying is carried out at temperatures in the range 60° C.-140° C., until a constant weight of the residue. 14. A process according to claim 1, which is carried out batchwise or continuously.