초록 ▼

A method for producing an activated carbon material includes forming an aqueous mixture of a natural, non-lignocellulosic carbon precursor and an inorganic compound, heating the mixture in an inert or reducing atmosphere, cooling the heated mixture to form a first carbon material, and removing the i

A method for producing an activated carbon material includes forming an aqueous mixture of a natural, non-lignocellulosic carbon precursor and an inorganic compound, heating the mixture in an inert or reducing atmosphere, cooling the heated mixture to form a first carbon material, and removing the inorganic compound to produce an activated carbon material. The activated carbon material is suitable to form improved carbon-based electrodes for use in high energy density devices.

대표청구항 ▼

1. A method for producing an activated carbon material comprising: forming an aqueous mixture consisting essentially of a natural, non-lignocellulosic carbon precursor selected from the group consisting of wheat flour, corn flour, rice flour and potato flour, and an inorganic compound;heating the aq

1. A method for producing an activated carbon material comprising: forming an aqueous mixture consisting essentially of a natural, non-lignocellulosic carbon precursor selected from the group consisting of wheat flour, corn flour, rice flour and potato flour, and an inorganic compound;heating the aqueous mixture in an inert or reducing atmosphere to form a first carbon material; andremoving the inorganic compound from the first carbon material to produce a powdered activated carbon material. 2. A method according to claim 1, wherein the inorganic compound is selected from the group consisting of an alkali hydroxide, alkali chloride, phosphoric acid, calcium chloride and zinc chloride. 3. A method according to claim 1, wherein the inorganic compound is selected from the group consisting of sodium hydroxide, potassium hydroxide, sodium chloride and potassium chloride. 4. A method according to claim 1, wherein a weight ratio of inorganic compound to non-lignocellulosic carbon precursor in the aqueous mixture is between about 5:1 and 1:5. 5. A method according to claim 1, wherein a weight ratio of inorganic compound to non-lignocellulosic carbon precursor in the aqueous mixture is greater than or equal to 1. 6. A method according to claim 1, further comprising aging the aqueous mixture for an aging time ranging from between about 0.5 to 8 hours prior to the step of heating. 7. A method according to claim 1, wherein the step of heating comprising heating the mixture at a temperature in the range of about 600° C. to 900° C. 8. A method according to claim 1, wherein the step of removing the inorganic compound comprises rinsing the first carbon material in a solvent. 9. A method according to claim 8, wherein the solvent is water. 10. The method according to claim 1, further comprising grinding the first carbon material after removing the inorganic compound to form the powdered activated carbon material. 11. A method for producing a carbon-based electrode comprising: forming an aqueous mixture consisting essentially of a natural, non-lignocellulosic carbon precursor selected from the group consisting of wheat flour, corn flour, rice flour and potato flour, and an inorganic compound;heating the aqueous mixture in an inert or reducing atmosphere to form a first carbon material;removing the inorganic compound from the first carbon material to produce an activated carbon material;mixing the activated carbon material with at least one of carbon black and PTFE to form an electrode mixture; andforming a carbon-based electrode from the electrode mixture. 12. A method according to claim 11, wherein the activated carbon material is dried to form a powder prior to forming the carbon-based electrode. 13. A method according to claim 11, further comprising incorporating the carbon-based electrode into a high energy density device. 14. A method according to claim 13, wherein the high energy density device is an ultracapacitor. 15. A method according to claim 14, wherein the ultracapacitor has a design selected from the group consisting of a jelly roll design, a prismatic design, and a honeycomb design. 16. A method for producing an activated carbon material comprising: heating a natural, non-lignocellulosic carbon precursor selected from the group consisting of wheat flour, corn flour, rice flour and potato flour in an inert or reducing atmosphere to form a first carbon material;mixing the first carbon material with an inorganic compound to form a mixture that consists essentially of the first carbon material and the inorganic compound;heating the mixture in an inert or reducing atmosphere to incorporate the inorganic compound into the first carbon material; andremoving the inorganic compound from the first carbon material to produce an activated carbon material. 17. A method according to claim 16, wherein the mixture comprises an aqueous mixture of the inorganic compound. 18. A method according to claim 17, further comprising aging the mixture for an aging time ranging from between about 0.5 to 8 hours prior to the step of heating. 19. A method according to claim 16, wherein the step of heating the mixture comprising heating at a temperature in the range of about 300° C. to 850° C. 20. A method for producing a carbon-based electrode comprising: heating a natural, non-lignocellulosic carbon precursor selected from the group consisting of wheat flour, corn flour, rice flour and potato flour in an inert or reducing atmosphere to form a first carbon material;mixing the first carbon material with an inorganic compound to form a mixture that consists essentially of the first carbon material and the inorganic compound;heating the mixture in an inert or reducing atmosphere to incorporate the inorganic compound into the first carbon material;removing the inorganic compound from the first carbon material to produce an activated carbon material; andforming a carbon-based electrode from the activated carbon material. 21. A method for producing a carbon-based electrode comprising: heating a natural, non-lignocellulosic carbon precursor selected from the group consisting of wheat flour, corn flour, rice flour and potato flour in an inert or reducing atmosphere to form an intermediate carbon material that consists essentially of the natural, non-lignocellulosic carbon precursor;heating the intermediate carbon material in an oxidizing atmosphere to produce an activated carbon material powder; andforming a carbon-based electrode from the activated carbon material powder.