초록 ▼

An antimony-free glass comprising TeO2 and/or Bi2O3 suitable for use in a frit for producing a hermetically sealed glass package is described. The hermetically sealed glass package, such as an OLED display device, is manufactured by providing a first glass substrate plate and a second glass substrat

An antimony-free glass comprising TeO2 and/or Bi2O3 suitable for use in a frit for producing a hermetically sealed glass package is described. The hermetically sealed glass package, such as an OLED display device, is manufactured by providing a first glass substrate plate and a second glass substrate plate and depositing the antimony-free frit onto the first substrate plate. OLEDs may be deposited on the second glass substrate plate. An irradiation source (e.g., laser, infrared light) is then used to heat the frit which melts and forms a hermetic seal that connects the first glass substrate plate to the second glass substrate plate and also protects the OLEDs disposed therein. The antimony-free glass has excellent aqueous durability, good flow, and low glass transition temperature.

대표청구항 ▼

1. An antimony-free glass comprising: V2O5 ≧30 and ≦60 mole %;P2O5 ≧5 mole % and ≦20 mole %;ZnO 0-10 mole %;Bi2O3 0-5 mole %;Fe2O3 ≧10 mole % and ≦25 mole %;TiO2 ≧5 mole % and ≦20 mole %;TeO2 ≧5 mole % and ≦20 mole %; and wherein TiO2+Fe2O3 is in a range from 20 mole % to 35 mole %. 2. The antimony-

1. An antimony-free glass comprising: V2O5 ≧30 and ≦60 mole %;P2O5 ≧5 mole % and ≦20 mole %;ZnO 0-10 mole %;Bi2O3 0-5 mole %;Fe2O3 ≧10 mole % and ≦25 mole %;TiO2 ≧5 mole % and ≦20 mole %;TeO2 ≧5 mole % and ≦20 mole %; and wherein TiO2+Fe2O3 is in a range from 20 mole % to 35 mole %. 2. The antimony-free glass according to claim 1, wherein: V2O5 ≧30 and ≦40 mole %; andP2O5 ≧5 mole % and ≦15 mole %. 3. The antimony-free glass according to claim 1, wherein: V2O5 ≧35 mole % and ≦40 mole %;P2O5 ≧8 mole % and ≦10 mole %; andZnO ≧3 mole % and ≦7 mole %. 4. The antimony-free glass according to claim 1, wherein the glass has the following composition: V2O5 40 mole %;P2O5 10 mole %;ZnO 5 mole %;Fe2O3 15 mole %;TiO2 15 mole %; andTeO2 15 mole %. 5. The antimony-free glass according claim 1, wherein the antimony-free glass has a Tg≦350° C. 6. The antimony-free glass according to claim 1, wherein the antimony-free glass comprises a glass frit. 7. The antimony-free glass according to claim 1, wherein the glass frit further comprises a CTE lowering filler. 8. A glass package comprising: a first glass plate;a second glass plate; anda frit that connects the first glass plate to the second glass plate and forms an hermetic seal therebetween, the frit including an antimony-free glass comprising: V2O5 ≧30 and ≦60 mole %;P2O5 ≧5 mole % and ≦20 mole %;ZnO ≧0 and ≦10 mole %;Bi2O3 ≧0 and ≦5 mole %;Fe2O3 ≧10 mole % and ≦25 mole %;TiO2 ≧5 mole % and ≦20 mole %;TeO2 ≧5 mole % and ≦20 mole %; and wherein TiO2+Fe2O3 is in a range from 20 mole % to 35 mole %. 9. The glass package according to claim 8, wherein: V2O5 ≧30 and ≦40 mole %; andP2O5 ≧5 mole % and ≦15 mole %. 10. The glass package according to claim 8, wherein: V2O5 ≧35 mole % and ≦40 mole %;P2O5 ≧8 mole % and ≦10 mole %; andZnO ≧3 mole % and ≦7 mole %. 11. The glass package according to claim 8, wherein the antimony-free glass has a Tg ≦350° C. 12. The glass package according to claim 8, wherein the frit comprises a CTE-lowering filler. 13. The glass package according to claim 8, further comprising an organic material disposed between the first and second glass plates. 14. The glass package according to claim 13, wherein the organic material comprises an organic light emitting diode. 15. A frit comprising: V2O5 ≧30 and ≦60 mole %;P2O5 ≧5 mole % and ≦20 mole %;ZnO ≧0 and ≦10 mole %;Bi2O3 ≧0 and ≦5 mole %;Fe2O3 ≧10 mole % and ≦25 mole %;TiO2 ≧5 mole % and ≦20 mole %;TeO2 ≧5 mole % and ≦20 mole %; and wherein TiO2+Fe2O3 is in a range from 20 mole % to 35 mole %. 16. The frit according to claim 15, wherein: V2O5 ≧30 and ≦40 mole %; andP2O5 ≧5 mole % and ≦15 mole %. 17. The frit according to claim 15, wherein: V2O5 ≧35 mole % and ≦40 mole %;P2O5 ≧8 mole % and ≦10 mole %; andZnO ≧3 mole % and ≦7 mole %. 18. The frit according to claim 15, wherein the frit comprises a CTE-lowering filler.