초록 ▼

Catalyst articles comprising substantially only a palladium precious metal component in a first catalytic layer and a rhodium component in a second catalytic layer and related methods of preparation and use are disclosed. Also disclosed is a catalyst article comprising a first layer formed on a carr

Catalyst articles comprising substantially only a palladium precious metal component in a first catalytic layer and a rhodium component in a second catalytic layer and related methods of preparation and use are disclosed. Also disclosed is a catalyst article comprising a first layer formed on a carrier substrate, wherein the first layer comprises a refractory metal oxide and has a surface that is substantially uniform; a second layer formed on the first layer, wherein the second layer comprises i) an oxygen storage component that is about 50-90% by weight of the second layer and ii) a palladium component in an amount of about 2-5% by weight of the second layer, wherein the palladium component is substantially the only platinum group metal component, and a palladium-free third layer comprising a rhodium component supported on a thermostable oxygen storage component which is about 80-99% by weight of the second layer. One or more improved properties are exhibited by the catalyst article.

대표청구항 ▼

1. A catalyst article for use in a small engine comprising: a first catalytic layer formed on a carrier, the first catalytic layer comprising i) an oxygen storage component that is about 50-90% by weight of the first catalytic layer and ii) a palladium component in an amount of about 2-5% by weight

1. A catalyst article for use in a small engine comprising: a first catalytic layer formed on a carrier, the first catalytic layer comprising i) an oxygen storage component that is about 50-90% by weight of the first catalytic layer and ii) a palladium component in an amount of about 2-5% by weight of the first catalytic layer, wherein the palladium component is substantially the only platinum group metal component in the first catalytic layer, and;a second catalytic layer formed on the first catalytic layer, the second catalytic layer comprising a rhodium component in an amount of about 0.2-1% by weight of the second catalytic layer, wherein the second catalytic layer does not contain palladium and the rhodium component is associated with a thermostable oxygen storage component. 2. The catalyst article of claim 1 wherein the palladium component is present at about 3-4% by weight of the first catalytic layer. 3. The catalyst article of claim 1 wherein the rhodium component is present at about 0.3-0.9% by weight of the second catalytic layer. 4. The catalyst article of claim 1 further comprising a refractory metal oxide undercoat on the carrier. 5. The catalyst article of claim 1 wherein the oxygen storage component in the second catalytic layer is present in an amount of 80-99% by weight of the second catalytic layer. 6. The catalyst article of claim 5 wherein the oxygen storage component in the second catalytic layer is ceria-zirconia. 7. The catalyst article of claim 1 wherein the carrier is selected from the group consisting of metal carriers, ceramic carriers and wire mesh. 8. The catalyst article of claim 1 comprising about 20-100 g/ft3 of platinum group metals. 9. The catalyst article of claim 8 comprising about 25-75 g/ft3 platinum group metals. 10. The catalyst article of claim 1 wherein the first catalytic layer further comprises about 0-0.5% by weight of a platinum component and the second catalytic layer further comprises about 0.2-1% by weight of a platinum component. 11. The catalyst article of claim 10 wherein the first catalytic layer comprises about 0.04-0.08% by weight of the platinum component and the second catalytic layer comprises about 0.5-1% by weight of the platinum component. 12. A method of treating exhaust from a small engine comprising hydrocarbons and nitrogen oxides comprising: contacting the exhaust with a catalyst article, wherein the catalyst article comprisesi) a first catalytic layer coated on a carrier, wherein the first catalytic layer comprises an oxygen storage component that is about 50-90% by weight of the first catalytic layer, and a palladium component in an amount of about 2-5% by weight of the first catalytic layer, wherein the palladium component is substantially the only platinum group metal component in the first catalytic layer, and;ii) a second catalytic layer coated on the first catalytic layer, the second catalytic layer comprising a rhodium component in an amount of about 0.2-1% by weight of the second catalytic layer, wherein the second catalytic layer does not contain palladium and the rhodium component is associated with a thermostable oxygen storage component support. 13. The method of claim 12 wherein the exhaust is contacted with a catalyst article comprising about 80-99% by weight of the oxygen storage component in the second catalytic layer. 14. The method of claim 12 wherein the exhaust is contacted with a catalyst article comprising about 25-75 g/ft3 of platinum group metals. 15. The method of claim 12 wherein the exhaust is contacted with a catalyst article comprising an oxygen storage component in the second catalytic layer selected from the group consisting of ceria-zirconia and ceria. 16. The method of claim 12 wherein the exhaust is contacted with a catalyst article comprising an oxygen storage component in the first catalytic layer selected from ceria, praseodymium, neodymium, and mixed oxides of any one or more of cerium, neodymium and praseodymium. 17. The method of claim 12 wherein the exhaust is contacted with a catalyst article further comprising a refractory metal oxide undercoat. 18. The method of claim 12 wherein the exhaust is contacted with a catalyst article further comprising 0-0.5% by weight of a platinum component in the first catalytic layer and 0.2-1% by weight of a platinum component in the second catalytic layer. 19. A method of making a catalyst article comprising: forming a first catalytic layer on a carrier by depositing a slurry on the carrier or, optionally, on a refractory metal oxide undercoat adhered to the carrier, the slurry comprising an oxygen storage component that provides about 50-90% by weight of the oxygen storage component in the first catalytic layer and a palladium component, wherein the palladium component is substantially the only platinum group metal component in the first catalytic layer, and wherein the palladium component is present in an amount sufficient to provide about 2-5% by weight of the palladium component in the first catalytic layer;drying the first catalytic layer;forming a second catalytic layer on the first catalytic layer by depositing a slurry on the first catalytic layer, the slurry comprising a rhodium component associated with a thermostable oxygen storage component support, wherein the rhodium component is present in an amount sufficient to provide about 0.2-1% by weight of the rhodium component in the second catalytic layer, and;drying the second catalytic layer. 20. A small engine system comprising a two stroke engine, wherein the system comprises an exhaust gas outlet for discharging exhaust gas and a catalytic article in accordance with claim 1 proximate to the exhaust gas outlet.