Cement composition containing an additive of a pozzolan and a strength retrogression inhibitor
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
C09K-008/467
C04B-014/00
E21B-033/13
출원번호
US-0273297
(2014-05-08)
등록번호
US-8895487
(2014-11-25)
발명자
/ 주소
Patil, Rahul C.
Muthusamy, Ramesh
Singh, Sheetal
Deshpande, Abhimanyu
출원인 / 주소
Halliburton Energy Services, Inc.
대리인 / 주소
Roddy, Craig W.
인용정보
피인용 횟수 :
2인용 특허 :
16
초록▼
A cement composition comprises: cement; water; and an additive, wherein the additive is a pozzolan and a strength-retrogression inhibitor, and wherein a mixture consisting essentially of: the additive; water; and a source of calcium develops a compressive strength of at least 500 psi at a time of 24
A cement composition comprises: cement; water; and an additive, wherein the additive is a pozzolan and a strength-retrogression inhibitor, and wherein a mixture consisting essentially of: the additive; water; and a source of calcium develops a compressive strength of at least 500 psi at a time of 24 hours, a temperature of 190° F., and a pressure of 3,000 psi. A method of cementing in a subterranean formation comprises: introducing the cement composition into the subterranean formation and allowing the cement composition to set. The compressive strength of the test cement composition consisting essentially of: the cement; the water; and the additive at a final time of 72 hours has a percent change greater than −5% from the compressive strength of the test cement composition at an initial time of 24 hours when tested at a temperature of 300° F. and a pressure of 3,000 psi.
대표청구항▼
1. A cement composition comprising: cement;water; andan additive, wherein the additive is a pozzolan and a strength-retrogression inhibitor,wherein the additive is a red brick powder and comprises at least the compounds silicon dioxide (SiO2), iron III oxide (Fe2O3), and aluminum oxide (Al2O3), wher
1. A cement composition comprising: cement;water; andan additive, wherein the additive is a pozzolan and a strength-retrogression inhibitor,wherein the additive is a red brick powder and comprises at least the compounds silicon dioxide (SiO2), iron III oxide (Fe2O3), and aluminum oxide (Al2O3), wherein the SiO2 is in a concentration in the range of about 40% to about 60% of the total chemical composition of the additive; the Fe2O3 is in a concentration in the range of about 15% to about 25% of the total chemical composition of the additive; andthe Al2O3 is in a concentration in the range of about 5% to about 15% of the total chemical composition of the additive, andwherein a mixture consisting essentially of: the additive; water; and a source of calcium develops a compressive strength of at least 500 psi (3.4 MPa) at a time of 24 hours, a temperature of 190° F. (88° C.), and a pressure of 3,000 psi (20.7 MPa). 2. The composition according to claim 1, wherein the cement is selected from the group consisting of Portland cements, gypsum cements, high alumina content cements, slag cements, high magnesia content cements, and combinations thereof. 3. The composition according to claim 1, wherein the water is selected from the group consisting of freshwater, brackish water, saltwater, and any combination thereof. 4. The composition according to claim 1, wherein the SiO2, Fe2O3, and Al2O3 comprise at least 70% of the total chemical composition of the additive. 5. The composition according to claim 1, wherein the concentration of the SiO2, Fe2O3, and Al2O3 is a percentage such that the additive is a pozzolan and a strength retrogression inhibitor. 6. The composition according to claim 1, wherein the ratio of SiO2 to Fe2O3 to Al2O3 is in the range of 1:0.2:0.2 to 1:0.35:0.3. 7. The composition according to claim 1, wherein the ratio of SiO2 to Fe2O3 to Al2O3 is a ratio such that the additive is a pozzolan and a strength retrogression inhibitor. 8. The composition according to claim 1, wherein the particle size of the additive is selected such that the mixture develops a compressive strength of at least 500 psi (3.4 MPa) at a time of 24 hours, a temperature of 190° F. (88° C.), and a pressure of 3,000 psi (20.7 MPa). 9. The composition according to claim 1, wherein the particle size of the additive is selected such that the cement composition develops a compressive strength of at least 2,000 psi (13.8 MPa) at a time of 24 hours, a temperature of 190° F. (88° C.), and a pressure of 3,000 psi (20.7 MPa). 10. The composition according to claim 1, wherein the additive has a particle size distribution such that at least 90% of the additive has a particle size in the range of about 30 microns to 75 microns. 11. The composition according to claim 1, wherein the cement composition has a compressive strength of −20% to +20% compared to a control cement composition consisting of cement and water at any time, a temperature of 300° F. (149° C.), and a pressure of 3,000 psi (20.7 MPa). 12. The composition according to claim 1, wherein the compressive strength of a test cement composition consisting of the cement, the water, and the additive, at a final time of 72 hours has a percent change greater than 20% from the compressive strength of the test cement composition at an initial time of 6 hours when tested at a temperature of 300° F. (149° C.) and a pressure of 3,000 psi (20.7 MPa). 13. The composition according to claim 1, wherein the concentration of the additive is selected such that a percent change of the compressive strength of a test cement composition consisting of the cement, the water, and the additive or the cement composition is greater than −5% at a final time of 72 hours and an initial time of 24 hours. 14. The composition according to claim 13, wherein the percent change is greater than +2%. 15. The composition according to claim 1, wherein the additive is in a concentration in the range of about 2% to about 70% by weight of the cement. 16. The composition according to claim 1, wherein the cement composition is in a pumpable state prior to and during introduction into a subterranean formation. 17. A cement composition comprising: cement;water; andan additive, wherein the additive is a pozzolan and a strength-retrogression inhibitor,wherein the additive is a red brick powder and comprises at least the compounds silicon dioxide (SiO2), iron III oxide (Fe2O3), and aluminum oxide (Al2O3), wherein the ratio of SiO2 to Fe2O3 to Al2O3 is in the range of 1:0.2:0.2 to 1:0.35:0.3, and wherein a mixture consisting essentially of: the additive; water; and a source of calcium develops a compressive strength of at least 500 psi (3.4 MPa) at a time of 24 hours, a temperature of 190° F. (88° C.), and a pressure of 3,000 psi (20.7 MPa).
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (16)
Roddy,Craig W.; Chatterji,Jiten; Brenneis,D. Chad; King,Bobby J., Cement compositions comprising high alumina cement and cement kiln dust.
Roddy,Craig W.; Chatterji,Jiten; Brenneis,D. Chad; King,Bobby J., Methods of using cement compositions comprising high alumina cement and cement kiln dust.
Ravi, Krishna M.; Patil, Rahul C.; Patil, Sandip P.; Joseph, Trissa; Duffy, Marcus, Pozzolan for use in a cement composition having a low heat of hydration.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.