Method for manufacturing an elastomeric composition having a self-sealing property
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
C08J-003/20
C08L-009/00
B29C-073/16
B29D-030/06
B60C-019/12
C08J-003/22
C08L-007/00
C08K-003/00
C08K-005/01
C08L-057/02
출원번호
US-0576154
(2011-01-21)
등록번호
US-8957132
(2015-02-17)
우선권정보
FR-10 50596 (2010-01-28)
국제출원번호
PCT/EP2011/050857
(2011-01-21)
§371/§102 date
20121018
(20121018)
국제공개번호
WO2011/092123
(2011-08-04)
발명자
/ 주소
Voge, Bozena
Pelissier, Vincent
Merino Lopez, Jose
출원인 / 주소
Compagnie Generale des Establissements Michelin
대리인 / 주소
Cozen O'Connor
인용정보
피인용 횟수 :
3인용 특허 :
1
초록▼
Process for the manufacture of an elastomer composition having a self-sealing property which is based on at least (phr meaning parts by weight per 100 parts of solid elastomer): a blend of at least two solid elastomers, a polybutadiene or butadiene copolymer elastomer, referred to as “elastomer A”,
Process for the manufacture of an elastomer composition having a self-sealing property which is based on at least (phr meaning parts by weight per 100 parts of solid elastomer): a blend of at least two solid elastomers, a polybutadiene or butadiene copolymer elastomer, referred to as “elastomer A”, and a natural rubber or synthetic polyisoprene elastomer, referred to as “elastomer B”, the elastomer A:elastomer B ratio by weight being within a range from 10:90 to 90:10; between 30 and 90 phr of a hydrocarbon resin; from 0 to less than 30 phr of filler, in which, during a first stage or stage (a), a masterbatch comprising at least the elastomers A and B and between 30 and 90 phr of a hydrocarbon resin is prepared by mixing these various components in a mixer at a “hot compounding” temperature or up to a “hot compounding” temperature which is greater than the softening temperature of the hydrocarbon resin.
대표청구항▼
1. A process for the manufacture of an elastomer composition having a self-sealing property comprising (phr meaning parts by weight per 100 parts of solid elastomer): a blend of at least two solid elastomers, a polybutadiene or butadiene copolymer elastomer, referred to as “elastomer A”, and a natur
1. A process for the manufacture of an elastomer composition having a self-sealing property comprising (phr meaning parts by weight per 100 parts of solid elastomer): a blend of at least two solid elastomers, a polybutadiene or butadiene copolymer elastomer, referred to as “elastomer A”, and a natural rubber or synthetic polyisoprene elastomer, referred to as “elastomer B”, the elastomer A:elastomer B ratio by weight being within a range from 10:90 to 90:10;between 30 and 90 phr of a hydrocarbon resin;from 0 to less than 30 phr of a filler,wherein, during a first stage (a), a masterbatch comprising the elastomers A and B and between 30 and 90 phr of a hydrocarbon resin is prepared by mixing these various components in a mixer at a “hot compounding” temperature or up to a “hot compounding” temperature which is greater than the softening temperature of the hydrocarbon resin. 2. The process according to claim 1, wherein, during the first stage (a), the blend of at least two solid elastomers is brought into contact with the hydrocarbon resin in the solid state. 3. The process according to claim 1, wherein, during the first stage (a), the blend of at least two solid elastomers is brought into contact with the hydrocarbon resin in the liquid state. 4. The process according to claim 3, wherein the hydrocarbon resin is injected in the liquid state into the mixer. 5. The process according to claim 1, wherein the first stage (a) for the elastomers A and B is carried out with the exclusion of oxygen. 6. The process according to claim 1, wherein the hot compounding temperature is greater than 70° C. 7. The process according to claim 1, wherein the first stage (a) is carried out in a compounding screw extruder. 8. The process according to claim 1, wherein, during at least one subsequent stage (b), a crosslinking agent is incorporated in the masterbatch thus prepared, everything being mixed in the same mixer or in a different mixer. 9. The process according to claim 8, wherein stage (b) is carried out in a compounding screw extruder. 10. The process according to claim 8, wherein stage (b) is carried out on an external mixer of the two-roll open mill type. 11. The process according to claim 8, wherein the temperature during stage (b) is kept lower than the softening temperature of the hydrocarbon resin. 12. The process according to claim 8, wherein the temperature during stage (b) is kept lower than 130° C. 13. The process according to claim 12, wherein the temperature during stage (b) is kept lower than 50° C. 14. The process according to claim 1, wherein an intermediate stage of cooling the masterbatch is inserted between stages (a) and (b), in order to cool the masterbatch to a temperature lower than the softening temperature of the hydrocarbon resin. 15. The process according to claim 1, wherein an intermediate stage of cooling the masterbatch is inserted between stages (a) and (b), in order to cool the masterbatch to a temperature lower than 130° C. 16. The process according to claim 1, wherein the elastomer A is a polybutadiene. 17. The process according to claim 16, wherein the elastomer A is a polybutadiene having a content (mol %) of cis-1,4-bonds of greater than 90%. 18. The process according to claim 1, wherein the elastomer B is natural rubber or a synthetic cis-1,4 polyisoprene. 19. The process according to claim 1, wherein the elastomer A:elastomer B ratio by weight is within a range from 20:80 to 80:20. 20. The process according to claim 1, wherein the total content of elastomer A and elastomer B is greater than 50 phr. 21. The process according to claim 1, wherein the blend of elastomers A and B constitutes the only solid elastomer of the composition. 22. The process according to claim 1, wherein the number-average molar mass Mn of each of the elastomers A and B is between 100,000 and 5,000,000 g/mol. 23. The process according to claim 1, wherein the content of hydrocarbon resin is within a range from 45 to 75 phr. 24. The process according to claim 1, wherein the hydrocarbon resin exhibits a glass transition temperature (Tg) of greater than 0° C. 25. The process according to claim 1, wherein the number-average molar mass Mn of the hydrocarbon resin is between 400 and 2000 g/mol. 26. The process according to claim 1, wherein the hydrocarbon resin is selected from the group consisting of cyclopentadiene (CPD) homopolymer or copolymer resins, dicyclopentadiene (DCPD) homopolymer or copolymer resins, terpene homopolymer or copolymer resins, terpene phenol homopolymer or copolymer resins, C5 fraction homopolymer or copolymer resins, C9 fraction homopolymer or copolymer resins, cc-methylstirene homopolymer or copolymer resins, and the mixtures of these resins. 27. The process according to claim 1, wherein the filler is introduced during a stage subsequent to stage (a). 28. The process according to claim 1, wherein the content of the filler is between 0 and 30 phr. 29. The process according to claim 1, wherein the filler is carbon black. 30. The process according to claim 29, wherein the content of carbon black is less than 5 phr. 31. The process according to claim 30, wherein the content of carbon black is between 005 and 2 phr. 32. The process according to claim 8, wherein the crosslinking agent comprises sulphur or a sulphur donor. 33. The process according to claim 32, wherein the crosslinking agent comprises sulphur and a guanidine derivative. 34. The process according to claim 32, wherein the sulphur donor is a thiuram polysulphide, preferably tetrabenzylthiuram disulphide (TBzTD). 35. The process according to claim 1, wherein a liquid plasticizer having a glass transition temperature (Tg) of less than −20° C. is additionally incorporated in the composition. 36. The process according to claim 35, wherein the content of liquid plasticizer is less than 60 phr. 37. The process according to claim 36, wherein the content of liquid plasticizer is within a range from 5 to 40 phr. 38. The process according to claim 35, wherein the liquid plasticizer is selected from the group consisting of liquid elastomers, polyolefin oils, naphthenic oils, paraffinic oils, DAE oils, MES oils, TDAE oils, mineral oils, vegetable oils, ether plasticizers, ester plasticizers, phosphate plasticizers, sulphonate plasticizers and the mixtures of these compounds. 39. The process according to claim 38, wherein the liquid plasticizer is selected from the group consisting of liquid elastomers, polyolefin oils, vegetable oils and the mixtures of these compounds. 40. The process according to claim 35, wherein the number-average molar mass Mn of the liquid plasticizer is between 400 and 90,000 g/mol. 41. The process according to claim 35, wherein the liquid plasticizer is incorporated in the masterbatch during stage (a). 42. The process according to claim 35, wherein the liquid plasticizer is incorporated during stage (b). 43. The process according to claim 35, wherein the liquid plasticizer is incorporated during a stage (c) subsequent to stage (b), in the same mixer or a different mixer from that of stage (b). 44. The process according to claim 43, wherein stage (c) is carried out in a compounding screw extruder. 45. The process according to claim 43, wherein stage (c) is carried, out on an external mixer of the two-roll open mill type.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (1)
Pialot, Frederic; Fombelle, Damien; Voge, Bozena; Merino Lopez, Jose, Process for manufacturing a self-sealing composition.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.