초록 ▼

In order to provide a method of manufacturing an aluminum flake pigment having a small mean particle size as well as high brightness, a method of manufacturing an aluminum flake pigment including a step of flaking aluminum powder in an organic solvent with a grinder having grinding media, which grin

In order to provide a method of manufacturing an aluminum flake pigment having a small mean particle size as well as high brightness, a method of manufacturing an aluminum flake pigment including a step of flaking aluminum powder in an organic solvent with a grinder having grinding media, which grinding media contain steel ball grinding media formed by spherical media consisting of a material including steel and having diameters in the range of 0.3 mm to 1.0 mm, is provided. The mean particle size (D50Al) of this aluminum powder is preferably in the range of 1.0 to 10.0 μm. Further, this grinder is preferably a ball mill.

대표청구항 ▼

1. A method of manufacturing an aluminum flake pigment including a step of flaking an aluminum powder to produce aluminum flakes as said aluminum flake pigment in an organic solvent with a grinder having grinding media, wherein said grinding media contain steel ball grinding media formed by spherica

1. A method of manufacturing an aluminum flake pigment including a step of flaking an aluminum powder to produce aluminum flakes as said aluminum flake pigment in an organic solvent with a grinder having grinding media, wherein said grinding media contain steel ball grinding media formed by spherical media comprising steel and having diameters in a range of 0.3 mm to 1.0 mm, wherein said aluminum powder has a mean particle size (D50Al) in a range of 1.0 μm to 4.6 μm, and a ratio (D50Al/DB) of said mean particle size (D50 Al) of said aluminum powder to an average diameter (DB) of said steel ball grinding media is in a range of 0.001 to 0.02 . 2. The method of manufacturing an aluminum flake pigment according to claim 1, wherein said ratio (D50Al/DB) of the mean particle size (D50Al) of said aluminum powder to the average diameter (DB) of said steel ball grinding media is in the range of 0.0015 to 0.008. 3. The method of manufacturing an aluminum flake pigment according to claim 1, wherein a ratio (WAl/Wsol) of the mass (WAl(kg)) of said aluminum powder to the volume (Wsol(L)) of said organic solvent is in a range of 0.1 to 0.3. 4. The method of manufacturing an aluminum flake pigment according to claim 1, wherein said grinder is a ball mill. 5. The method of manufacturing an aluminum flake pigment according to claim 4, further consprising operating said ball mill at a rotational frequency that is not more than 95% of the critical rotational frequency. 6. The method of manufacturing an aluminum flake pigment according to claim 1, wherein said step of flaking aluminum powder produces aluminum flakes comprising aluminum flake particles that include small flake particles having maximum dimensions of not more than 10 μm, wherein said small flake particles have a mean aspect ratio in a range of 8 to 20. 7. The method of manufacturing an aluminum flake pigment according to claim 1, wherein said ratio (D50A1/DB) of said mean particle size (D50A1) of said aluminum powder to said average diameter (DB) of said steel ball grinding media is less than 0.004. 8. The method of manufacturing an aluminum flake pigment according to claim 1, wherein said diameters of said spherical media are not more than 0.7 mm. 9. The method of manufacturing an aluminum flake pigment according to claim 1, wherein said step of flaking produces a slurry including said organic solvent and aluminum flakes produced by said flaking of said aluminum powder,further comprising, after said step of flaking, a step of separating said aluminum flakes out of said slurry and then preparing said aluminum flake pigment of said aluminum flakes. 10. The method of manufacturing an aluminum flake pigment according to claim 9, wherein said step of separating said aluminum flakes out of said slurry produces a cake of said aluminum flakes, and said step of preparing said aluminum flake pigment of said aluminum flakes comprises kneading said cake of said aluminum flakes to obtain said aluminum flake pigment. 11. The method of manufacturing an aluminum flake pigment according to claim 1, wherein said step of flaking said aluminum powder produces aluminum flakes used for said aluminum flake pigment, and wherein said aluminum flakes have a mean particle size in a range of 4.2μm to 13.1 μm.