Repellent coating composition and coating, method for making and uses thereof
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
C08G-077/22
C09D-005/16
C09D-183/04
F28F-019/04
B05D-005/08
C08G-077/16
C08K-005/5419
C08K-005/5455
F24J-002/46
출원번호
US-0997402
(2011-12-20)
등록번호
US-9029491
(2015-05-12)
우선권정보
DK-2010 70577 (2010-12-22)
국제출원번호
PCT/DK2011/050517
(2011-12-20)
§371/§102 date
20130809
(20130809)
국제공개번호
WO2012/083970
(2012-06-28)
발명자
/ 주소
Bischoff, Claus
Holberg, Stefan
출원인 / 주소
Teknologisk Institut
대리인 / 주소
Wray, James Creighton
인용정보
피인용 횟수 :
0인용 특허 :
14
초록▼
A cross-linkable coating composition comprises (i) one or more silanes having either at least three hydrolysable groups, or at least two hydrolysable groups and at least one organofunctional group capable of forming chemical bonds upon curing, wherein (i.a) the sum of said silanes constitutes at lea
A cross-linkable coating composition comprises (i) one or more silanes having either at least three hydrolysable groups, or at least two hydrolysable groups and at least one organofunctional group capable of forming chemical bonds upon curing, wherein (i.a) the sum of said silanes constitutes at least 20% of the total mass of the coating compositions combined solids and silanes, and (i.b) said silanes are possibly partly or completely hydrolyzed and possibly partly condensed, and (ii) at least one low surface energy additive, wherein (ii.a) said low surface energy additive comprises polydimethylsiloxane chemically bonded to at least one functional group, (ii.b) said functional group is configured for the polydimethylsiloxane moiety to cross-link with said coating composition, (ii.c) said polydimethylsiloxane constitutes 0.01% to 15% of the mass of said cured coating, when said coating composition is cured, and (ii.d) said polydimethylsiloxane moiety has a molecular weight of more than 1600 g/mol.
대표청구항▼
1. A cross-linkable coating composition comprising: (i) methyltriethoxysilane,(ii) a polysilane obtainable by reacting (3-aminopropyl) methyldiethoxysilane with a further component selected from the group consisting of 4,4′-methylene bis(cyclohexylisocyanate) and a homopolymer of 1,6-hexamethylene d
1. A cross-linkable coating composition comprising: (i) methyltriethoxysilane,(ii) a polysilane obtainable by reacting (3-aminopropyl) methyldiethoxysilane with a further component selected from the group consisting of 4,4′-methylene bis(cyclohexylisocyanate) and a homopolymer of 1,6-hexamethylene diisocyanate, and where the sum of said silanes constitutes at least 20% of the total mass of the coating composition's combined solids and silanes, and where said silanes are optionally partly or completely hydrolysed and optionally partly condensed; and(iii) at least one low surface energy additive defined by a surface providing a static water contact angle above 90°, wherein(iii.a) the low surface energy additive is obtainable by reacting (3-aminopropyl) methyldiethoxysilane with a silanol terminated polydimethylsiloxane and a further component selected from the group consisting of 4,4′-methylene bis(cyclohexylisocyanate) in the presence of ethanol and 2-propanol as solvents or a composition comprising a homopolymer of 1,6-hexamethylene diisocyanate in the presence of ethanol, ethylacetate and 2-propanol as solvents,(iii.b) said polydimethylsiloxane has in the composition a concentration that upon curing results in 0.01% to 15% of the mass of said cured coating, and(iii.c) said polydimethylsiloxane moiety has a molecular weight of more than 1600 g/mol. 2. Method of making a cross-linkable coating composition comprising: (i) one or more silanes comprising either of the following two options: at least three hydrolysable groups orat least two hydrolysable groups and at least one organofunctional group capable of forming chemical bonds upon curing,and where the sum of said silanes constitutes at least 20% of the total mass of the coating compositions combined solids and silanes, where said silanes being optionally partly or completely hydrolysed and optionally partly condensed; and(ii) at least one low surface energy additive defined by a surface providing a static water contact angle above 90°,(ii.a) said low surface energy additive comprising polydimethylsiloxane chemically bonded to at least one functional group,(ii.b) said functional group configuring the polydimethylsiloxane moiety to cross-link with said coating composition, andcuring the composition wherein the method comprises the step of obtaining at least one low surface energy additive by reacting 1 molar part silanol terminated polydimethylsiloxane with an excess of at least 3 molar parts of a silane having at least two hydrolysable groups and at least one amino-group, said amino group being in a further step converted to an urea or an amide group, and wheresaid polydimethylsiloxane moiety has a molecular weight of more than 1600 g/mol, and where the method comprises providing said polydimethylsiloxane in a concentration in the composition which, when said coating composition is cured, results in 0.01% to 15% of the mass of said cured coating. 3. Method of making a coating composition according to claim 2, wherein said method contains at least one step during preparation that adjusts the amount of silicon (Si) and carbon (C) being added to ensure that said coating composition, when cured, has a silicon (Si) content between 4% and 44% and a carbon (C) content between 17% and 86% by weight. 4. Method of making a coating composition according to claim 2 wherein the method comprises the usage of a silane with one methyl group bonded to silicon and three hydrolysable groups, said silane constitutes at least 10% of the total mass of the coating compositions combined solids and silanes. 5. Method of making a coating composition according to claim 2 wherein at least 5% of the total mass of the coating compositions combined solids and silanes is a silane obtainable by reacting (3-aminopropyl)methyldiethoxysilane with a further component selected from the group consisting of 4,4′-methylene bis(cyclohexylisocyanate) in the presence of ethanol and 2-propanol as solvents and a homopolymer of 1,6-hexamethylene diisocyanate in the presence of ethanol, ethylacetate and 2-propanol as solvents. 6. Method of making a coating composition according to claim 2 comprising at least one step of adding a combination of monopodal silanes and polysilanes, wherein said monopodal silanes have one silicon atom with two or three hydrolysable groups, said monopodal silanes constitute about 15% to 85% of the total mass of the coating compositions combined solids and silanes andsaid polysilanes having at least two silicon atoms, each with two or three hydrolysable groups, and an organic structure connecting the silicon atoms through a silicon-carbon bond and where said polysilane comprises at least one group of thiourethane or urea linkage and where said polysilanes constitute about 15% to 85% of the total mass of the coating compositions combined solids and silanes. 7. Method of making a coating composition according to claim 2, comprising hydrolysing the coating compositions prior to application. 8. Method of making a coating composition according to claim 7 including a step where the hydrolysis is performed prior to application with a molar ratio of water to silicon-bonded hydrolysable groups of at least 0.1. 9. Method of making a coating composition according to claim 2 where the hydrolysis of the coating composition is performed prior to application with a molar ratio of water to hydrolysable groups bonded to silicon of at least 0.2. 10. Method of making a coating composition according to claim 2 including a step of providing a polysilane, where said polysilane comprises at least one, preferably at least two linkages from the group of thiourethane or urea. 11. A method of making a coating based on a coating composition made according to claim 2, wherein said coating composition further comprises a binder, a hardener, a colorant, a filler, a catalyst, a UV-stabilizer, a solvent, an anti-bacterial agent or a combination thereof. 12. A method comprising using on a structure the coating composition made according to claim 2, further comprising spreading the coating composition on at least part of a surface of a structure and protecting said structure from oil derived fouling or to repel oil or said fouling from the surface of the structure. 13. A method comprising using on a structure the coating composition made according to claim 2, further comprising spreading the coating composition on at least part of a surface of a structure and protecting said structure from crude oil derived fouling or to repel crude oil or said fouling from the surface of the structure. 14. A method comprising using on a structure the coating composition made according to claim 2, further comprising spreading the coating composition to reduce or repel material accumulation on surfaces of the structure, where said accumulation of material can be due to fouling, scaling, or corrosion. 15. A method comprising using on a structure the coating composition made according to claim 2, further comprising spreading the coating composition on a maritime structure and preventing or reducing accumulation of material on or to repel material from on structures used in maritime or off-shore environments. 16. A method comprising using on a structure the coating composition made according to claim 2, further comprising spreading the coating composition on an energy converter structure and preventing or reducing accumulation of material on or to repel material from structures used in energy converters such as power plants, where said energy converters include turbines, blades on wind turbines and solar converters. 17. A method comprising using on a structure the coating composition made according to claim 2, further comprising spreading the coating composition on a heat exchanger structure and preventing or reducing to prevent or reduce accumulation of material on or to repel material from structures used in heat exchangers. 18. A method comprising using on a structure the coating composition made according to claim 2, further comprising spreading the coating composition on tubular structures, channels or valves and preventing or reducing to prevent or reduce accumulation of material on or to repel material from structures used in pipes, tubes, channels or valves. 19. The coating composition according to claim 1, where content of said polydimethylsiloxane with a molecular weight of more than 1600 g/mol is between 0.7 and 1.1% based on weight of combined solids and silanes.
Cifuentes Martin E. (Midland MI) Brady William P. (Midland MI) Fenton William N. (Midland MI) Schmidt Randall G. (Midland MI) Strong Michael R. (Midland MI) Stickles David L. (Midland MI) VanWert Ber, Moisture-curable compositions containing aminoalkoxy-functional silicone.
Baumann, Martin; Fritsche, Klaus Dieter; Korbelarz, Dagmar; Ludwig, Stephan; Poth, Lutz, Self-cleaning paint coating and a method and agent for producing the same.
Baumann, Martin; Fritsche, Klaus-Dieter; Korbelarz, Dagmar; Ludwig, Stephan; Poth, Lutz, Substrates with a self-cleaning surface, a process for their production and their use.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.