초록 ▼

A composite structure includes a substrate with pores of a first mean pore size and a coating on at least one surface of that substrate. This coating has pores of a second mean pore size where the first mean pore size is equal to or greater than said second mean pore size. When the pore size of the

A composite structure includes a substrate with pores of a first mean pore size and a coating on at least one surface of that substrate. This coating has pores of a second mean pore size where the first mean pore size is equal to or greater than said second mean pore size. When the pore size of the coating is effective to capture particulate greater than 0.2 micron, the composite may be formed into a filter effective to remove microbes from a fluid medium. One method to form the porous coating on the substrate includes: (1) forming a suspension of sinterable particles in a carrier fluid and containing the suspension in a reservoir; (2) maintaining the suspension by agitation; (3) transferring the suspension to an ultrasonic spray nozzle; (4) applying a first coating of the suspension to the substrate; and (5) sintering the sinterable particles to the substrate.

대표청구항 ▼

1. A method for forming a porous coating on a porous substrate, comprising the steps of: (a) forming a suspension of sinterable particles in a carrier fluid and containing said suspension in a reservoir;(b) maintaining said suspension by agitation in said reservoir;(c) transferring said suspension f

1. A method for forming a porous coating on a porous substrate, comprising the steps of: (a) forming a suspension of sinterable particles in a carrier fluid and containing said suspension in a reservoir;(b) maintaining said suspension by agitation in said reservoir;(c) transferring said suspension from said reservoir to a first non-cavitating in-line ultrasonic agitator that agitates said suspension without cavitation;(d) transferring said suspension from said first non-cavitating ultrasonic in-line agitator to a selector valve;(e) selectively transferring said suspension from said selector valve to either an ultrasonic spray nozzle or back to said reservoir;(f) heating said porous substrate;(g) when said suspension is transferred to said ultrasonic spray nozzle, applying a first coating of said suspension to said heated porous substrate;(h) subsequent to completion of step (g), selectively transferring said suspension from said selector valve back to said reservoir and sintering said sinterable particles to said substrate thereby forming a coated porous substrate. 2. The method of claim 1 including interposing a pump between said reservoir and said first non-cavitating in-line ultrasonic agitator and interposing a second non-cavitating ultrasonic inline agitator that agitates said suspension without cavitation between said reservoir and said pump. 3. The method of claim 2 including adjusting a space between an orifice of said ultrasonic spray nozzle and said substrate to be from one inch to three inches. 4. The method of claim 2 wherein said pump is effective to dispense a precise volume of fluid per shaft revolution between said first ultrasonic inline agitator and said ultrasonic spray nozzle. 5. The method of claim 4 wherein said sinterable particles are selected to have an average particle size of from 50 nanometers to 350 nanometers. 6. The method of claim 5 wherein said suspension is formed with from 10 grams per liter to 200 grams per liter of sinterable particles in a carrier fluid. 7. The method of claim 5 wherein said sinterable particles are selected to be stainless steel. 8. The method of claim 7 wherein said coated substrate is effective to remove microbes from a fluid medium. 9. The method of claim 1 including heating said substrate to a temperature of from 120° F. to 220° F. immediately prior to said applying step. 10. The method of claim 9 including selecting said carrier fluid to be water, isopropanol or a mixture thereof and maintaining said substrate at a temperature of between 100° F. and 150° F. during said applying step. 11. The method of claim 10 wherein a heat source is adjacent a first side of said substrate while said first coating is applied to an opposing second side of said substrate. 12. A method for forming a porous coating on a tubular porous substrate having an interior bore, comprising the steps of: (a) forming a suspension of sinterable particles in a carrier fluid and containing said suspension in a reservoir;(b) maintaining said suspension by agitation in said reservoir;(c) transferring said suspension from said reservoir to a selector valve;(d) selectively transferring said suspension from said selector, valve to either a spray nozzle or back to said reservoir;(e) when said suspension is transferred to said spray nozzle, including interposing a non-cavitating ultrasonic in-line agitator that agitates said suspension without cavitation between said reservoir and said spray nozzle, applying a first coating of said suspension to said porous substrate that has been heated to a temperature of from 100° F. and 200° F. immediately prior to said applying step; and(f) sintering said sinterable particles to said porous substrate thereby forming a coated substrate. 13. The method of claim 12 including applying a vacuum to said interior bore during said applying step. 14. The method of claim 13 including rotating said tube about a longitudinal axis thereof during said applying step. 15. The method of claim 14 including shuttling said spray nozzle along a longitudinal axis of said tube during said applying step until outside surfaces of said tube are covered with said porous coating. 16. The method of claim 13 including shuttling said spray nozzle along a longitudinal axis of said tube during said applying step. 17. The method of claim 14 including selecting said carrier fluid to be water, isopropanol or a mixture thereof. 18. The method of claim 17 including shuttling said spray nozzle along a longitudinal axis of said tube during said applying step until outside surfaces of said tube are covered with said porous coating.