초록 ▼

A slurry for manufacturing gypsum board comprises calcined gypsum, water, a foaming agent, and a coalescing agent. The foaming agent imparts a plurality of bubbles in the slurry. Typically, a foam is pre-generated with the foaming agent and the foam is used to form the slurry such that the foam impa

A slurry for manufacturing gypsum board comprises calcined gypsum, water, a foaming agent, and a coalescing agent. The foaming agent imparts a plurality of bubbles in the slurry. Typically, a foam is pre-generated with the foaming agent and the foam is used to form the slurry such that the foam imparts the plurality of bubbles in the slurry. The coalescing agent coalesces the plurality of bubbles imparted by the foam. Typically, the coalescing agent coalesces a plurality of small and partially joined bubbles imparted by the foam to create larger and more discrete bubbles. A gypsum board and method of forming the slurry and the gypsum board are also disclosed. The gypsum board comprises a gypsum layer formed from the slurry. The gypsum layer defines a plurality of bubbles dispersed therein, which are imparted by the foam and coalescing agent of the slurry.

대표청구항 ▼

1. A gypsum board comprising a cover sheet and a gypsum layer disposed on said cover sheet, said gypsum layer defining a plurality of bubbles dispersed therein and comprising the reaction product of: calcined gypsum; andwater;wherein an exothermic reaction occurs between said calcined gypsum and wat

1. A gypsum board comprising a cover sheet and a gypsum layer disposed on said cover sheet, said gypsum layer defining a plurality of bubbles dispersed therein and comprising the reaction product of: calcined gypsum; andwater;wherein an exothermic reaction occurs between said calcined gypsum and water, with said reaction product having a temperature ranging from an initial temperature (T1) to a peak temperature (T2) during formation; in the presence of a foaming agent comprising a surfactant for creating a foam to impart a plurality of bubbles in said reaction product; anda coalescing agent comprising an ethylene oxide-propylene oxide (EO/PO) block copolymer and/or a reverse EO/PO block copolymer, with said coalescing agent having a cloud point (TCP) of from about 16.0 to about 60.0° C. according to ASTM D2024 and that is between the initial temperature (T1) and the peak temperature (T2) of said reaction product, such that said coalescing agent coalesces the plurality of bubbles imparted by the foam thereby establishing the plurality of bubbles in said gypsum layer. 2. A gypsum board as set forth in claim 1 wherein said foaming agent and said coalescing agent are present in a weight ratio of from about 20:1 to about 3:1. 3. A gypsum board as set forth in claim 1 wherein said coalescing agent has a cloud point (TCP) of from about 18.0 to about 60.0° C. according to ASTM D2024. 4. A gypsum board as set forth in claim 1 wherein said ethylene oxide-propylene oxide (EO/PO) block copolymer and/or said reverse EO/PO block copolymer has an ethylene oxide (EO) weight percent of from about 10 to about 50 based on 100 parts by weight of said EO/PO block copolymer. 5. A gypsum board as set forth in claim 1 wherein said coalescing agent is said reverse EO/PO block copolymer. 6. A gypsum board as set forth in claim 1 wherein said coalescing agent is present in an amount of from about 0.01 to about 1.0 lbs per 1000 square feet (msf) of said gypsum board. 7. A gypsum board as set forth in claim 1 wherein said surfactant of said foaming agent comprises a sulfate or a sulfonate. 8. A gypsum board as set forth in claim 1 wherein said surfactant of said foaming agent comprises an ammonium ether sulfate. 9. A gypsum board as set forth in claim 1 wherein said surfactant of said foaming agent comprises an ammonium ether sulfate and said coalescing agent is a reverse EO/PO block copolymer, with said reverse EO/PO block copolymer having an ethylene oxide (EO) weight percent of from about 10 to about 50 based on 100 parts by weight of said reverse EO/PO block copolymer. 10. A gypsum board as set forth in claim 9 wherein said foaming agent and said coalescing agent are present in a weight ratio of from about 7.5:1 to about 5:1. 11. A gypsum board as set forth in claim 9 wherein said foaming agent is present in an amount of from about 0.1 to about 2.0 lbs per 1000 square feet (msf) of said gypsum board and said coalescing agent is present in an amount of from about 0.05 to about 1.0 lbs per 1000 square feet (msf) of said gypsum board. 12. A gypsum board as set forth in claim 1 wherein said foaming agent is present in an amount of from about 0.1 to about 2.0 lbs per 1000 square feet (msf) of said gypsum board. 13. A gypsum board as set forth in claim 1 formed in yet the further presence of an additive component comprising at least one of a starch, an accelerator, glass fibers, potash, a thickening agent, boric acid, or a combination thereof. 14. A gypsum board as set forth in claim 1 wherein said water and said calcined gypsum are reacted in a weight ratio of from about 0.5 to about 1.5. 15. A gypsum board as set forth in claim 1 wherein the plurality of bubbles have an average diameter of from about 200 to about 800 microns. 16. A gypsum board as set forth in claim 1 having a weight of less than about 1500 lbs per 1000 square feet (msf). 17. A gypsum board as set forth in claim 1 further comprising a second cover sheet spaced from said cover sheet with said gypsum layer sandwiched between said cover sheets. 18. A gypsum board as set forth in claim 1 wherein said coalescing agent is said ethylene oxide-propylene oxide (EO/PO) block copolymer. 19. A method of forming a gypsum board comprising a cover sheet and a gypsum layer disposed on the cover sheet, the gypsum layer defining a plurality of bubbles dispersed therein and comprising the reaction product of calcined gypsum and water, wherein an exothermic reaction occurs between the calcined gypsum and water, with the reaction product having a temperature ranging from an initial temperature (T1) to a peak temperature (T2) during formation in the presence of a foaming agent comprising a surfactant for creating a foam to impart a plurality of bubbles in the reaction product and a coalescing agent comprising an ethylene oxide-propylene oxide (EO/PO) block copolymer and/or a reverse EO/PO block copolymer, with the coalescing agent having a cloud point (TCP) of from about 16.0 to about 60.0° C. according to ASTM D2024 and that is between the initial temperature (T1) and the peak temperature (T2) of the reaction product, such that the coalescing agent coalesces the plurality of bubbles imparted by the foam thereby establishing the plurality of bubbles in the gypsum layer, said method comprising the steps of: providing the calcined gypsum;providing the water;providing the foaming agent;providing the coalescing agent; andmixing the calcined gypsum, water, foaming agent, and coalescing agent to form the slurry;disposing the slurry on the cover sheet; andallowing the slurry to set to form the reaction product, gypsum layer, and the gypsum board. 20. A method as set forth in claim 19 wherein the foaming agent and the coalescing agent are present in a weight ratio of from about 10:1 to about 5:1. 21. A method as set forth in claim 19 wherein the coalescing agent has a cloud point (TCP) of from about 18.0 to about 60.0° C. according to ASTM D2024. 22. A method as set forth in claim 19 wherein the ethylene oxide-propylene oxide (EO/PO) block copolymer and/or the reverse EO/PO block copolymer has an ethylene oxide (EO) weight percent of from about 10 to about 50 based on 100 parts by weight of the EO/PO block copolymer. 23. A method as set forth in claim 19 wherein the coalescing agent is the reverse EO/PO block copolymer. 24. A method as set forth in claim 19 wherein the coalescing agent is present in an amount of from about 0.05 to about 1.0 lbs per 1000 square feet (msf) of the slurry. 25. A method as set forth in claim 19 wherein the surfactant of the foaming agent comprises a sulfate or a sulfonate. 26. A method as set forth in claim 19 wherein the surfactant of the foaming agent comprises an ammonium ether sulfate. 27. A method as set forth in claim 19 wherein the surfactant of the foaming agent comprises an ammonium ether sulfate and the coalescing agent is a reverse EO/PO block copolymer, with the reverse EO/PO block copolymer having an ethylene oxide (EO) weight percent of from about 10 to about 50 based on 100 parts by weight of the reverse EO/PO block copolymer. 28. A method as set forth in claim 19 wherein the foaming agent and the coalescing agent are present in the slurry a weight ratio of from about 7.5:1 to about 5:1. 29. A method as set forth in claim 19 wherein the foaming agent is present in an amount of from about 0.5 to about 2.0 lbs per 1000 square feet (msf) of the slurry and the coalescing agent is present in an amount of from about 0.05 to about 1.0 lbs per 1000 square feet (msf) of the slurry. 30. A method as set forth in claim 19 wherein the foaming agent is present in an amount of from about 0.5 to about 2.0 lbs per 1000 square feet (msf) of the slurry. 31. A method as set forth in claim 19 further comprising the step of premixing a portion of the water and the foaming agent separate from the calcined gypsum prior to the step of mixing. 32. A method as set forth in claim 19 further comprising the step of premixing a portion of the water and the coalescing agent separate from the calcined gypsum prior to the step of mixing. 33. A method as set forth in claim 19 further comprising the step of providing an additive component such that the step of mixing is further defined as mixing the calcined gypsum, water, foaming agent, coalescing agent, and the additive component to form a slurry. 34. A method as set forth in claim 33 wherein the additive component comprises a starch, an accelerator, glass fibers, potash, a thickening agent, boric acid, or a combination thereof. 35. A method as set forth in claim 19 further comprising the steps of providing a second cover sheet and applying the second cover sheet to the gypsum layer opposite the cover sheet such that the gypsum layer is sandwiched between the cover sheets. 36. A method as set forth in claim 19 further comprising the step of applying heat to the gypsum board to remove residual water from the gypsum layer.