Novel silicoaluminophosphate molecular sieve compositions comprising SAPO-11 and SAPO-41 with at least about 5 wt % of in situ-produced amorphous portion. Such compositions can be uncalcined or calcined and novel processes for their preparation are described. These compositions, when loaded or impre
Novel silicoaluminophosphate molecular sieve compositions comprising SAPO-11 and SAPO-41 with at least about 5 wt % of in situ-produced amorphous portion. Such compositions can be uncalcined or calcined and novel processes for their preparation are described. These compositions, when loaded or impregnated with a catalytically active species such as a Group VIII noble metal are novel, and are excellent hydroisomerization catalysts.
1. A process for the production of a silicoaluminophosphate molecular sieve comprised at least of SAPO-11 and SAPO-41 in combination with an in situ-coproduced amorphous portion, which process comprises: I) forming a reaction mixture in an essentially alcohol-free single-phase liquid reaction medium
1. A process for the production of a silicoaluminophosphate molecular sieve comprised at least of SAPO-11 and SAPO-41 in combination with an in situ-coproduced amorphous portion, which process comprises: I) forming a reaction mixture in an essentially alcohol-free single-phase liquid reaction medium by bringing together, under agitation, the following components comprising (i) alumina, (ii) silica, (iii) P2O5 in the form of 85% (wt/wt) orthophosphoric acid or equivalent amount of H3PO4 in the form of other aqueous phosphoric acid solutions, (iv) templating agent for SAPO-11 and SAPO-41, (v) water, and (vi) surfactant, wherein the foregoing components are in substantially the following relative molar proportions: 0.6 to 1.4 moles of (i):0.05 to 0.7 moles of (ii):0.6 to 1.4 moles of (iii):0.5 to 2 moles of (iv):15 to 100 moles of (v):0.01 to 0.5 moles of (vi);II) ageing the reaction mixture for a period up to about 100 hours, with agitation at an energy input in the range of 0.05 to about 20 kW/m3, and at one or more temperatures in the range of about 10 to about 100° C., to form an aged mixture; andIII) heating the aged mixture at 160° C. to about 220° C. under autogenous pressures for 2 to 100 hours with agitation, to thereby produce in situ a silicoaluminophosphate molecular sieve comprised at least of SAPO-11 and SAPO-41 in combination with at least about 5 wt % of amorphous portion; wherein the silica in I) is selected from a) silica sols, b) colloidal silicas, c) silica gels, d) spray dried silica particles, e) fumed silicas, or f) any combination of a)-e). 2. A process as in claim 1 wherein: said relative molar proportions in I) are 0.8 to 1.2 moles of (i):0.1 to 0.5 moles of (ii):0.8 to 1.2 moles of (iii):0.8 to 1.2 moles of (iv):20 to 70 moles of (v):0.02 to 0.3 moles of (vi);said period of ageing in II) is 10 hours or less and said energy input for the agitation in II) is in the range of 0.1 to 10 kW/m3; andsaid aged mixture in III) is heated at 170° C. to about 210° C. under autogenous pressures for 10 to 70 hours. 3. A process as in claim 1 wherein: said relative molar proportions in I) are 0.9 to 1.1 moles of (i):0.2 to 0.4 moles of (ii):0.9 to 1.1 moles of (iii):0.9 to 1.1 moles of (iv):25 to 60 moles of (v):0.05 to 0.2 moles of (vi);said period of ageing in II) is 1 hour or less and said energy input for the agitation in II) is in the range of 0.5 to 3 kW/m3; andsaid aged mixture in III) is heated at 180 to 200° C. under autogenous pressures for 20 to 50 hours with agitation. 4. A process as in claim 1 wherein in conducting the heating of the aged mixture under the conditions specified therein, the rate or rates at which the temperature increase is accomplished are selected to be in the range of about 0.05° C./min to about 1500° C./min. 5. A process as in claim 1 further comprising IV) cooling the silicoaluminophosphate molecular sieve to below about 100° C. 6. A process as in claim 5 wherein said cooling is within one hour after completion of said heating. 7. A process as in claim 1 further comprising (i) recovering said silicoaluminophosphate molecular sieve by a solids/liquid separation procedure, to form a recovered product, and (ii) washing and drying said recovered product, the operations of (i) and (ii) being completed within about 5 hours after completion of said heating of the aged mixture. 8. A process as in claim 7 further comprising calcining said recovered product at one or more temperatures which are at least in the range of about 300° C. to about 550° C. 9. A process as in claim 1 wherein said components are brought together in a molar ratio which is substantially as follows: 1 mole of (i):0.3 mole of (ii):1 mole of (iii):1 mole of (iv):25 to 55 moles of (v):0.02 to 0.1 mole of (vi). 10. A process as in claim 1 wherein the heating is conducted at a temperature in the range of 180° C. to 200° C. for a period in the range of about 12 to about 40 hours. 11. A process as in claim 1 wherein the ageing is conducted at one or more temperatures in the range of about 30 to about 100° C. 12. A process as in claim 1 wherein the templating agent used is di-n-propylamine or isopropylamine. 13. A process as in claim 1 wherein the templating agent used is di-n-propylamine and the surfactant used is hexadecylamine. 14. A process as in claim 1 wherein said molecular sieve additionally comprises up to about 80 wt % of SAPO-41 molecular sieve. 15. A silicoaluminophosphate molecular sieve of comprising in situ-coproduced SAPO-11 and SAPO-41, and about 5 wt % or more of in situ-coproduced amorphous phase material, the SAPO-11 and SAPO-41 being physically or chemically inseparable from each other without perturbation. 16. A silicoaluminophosphate molecular sieve comprising about 5 wt % to about 80 wt % of SAPO-11, about 5 wt % to about 80 wt % of SAPO-41, and about 5 wt % to about 60 wt % of in situ-produced amorphous phase material, the SAPO-11 and SAPO-41 being physically or chemically inseparable from each other without perturbation. 17. A silicoaluminophosphate molecular sieve as in claim 16 comprising about 10 wt % to about 60 wt % of SAPO-11, from about 10 wt % to about 60 wt % of SAPO-41, and about 20 wt % to about 50 wt % of in situ-produced amorphous phase material. 18. A catalyst composition comprising a silicoaluminophosphate molecular sieve product of claim 15 which is loaded or impregnated with a catalytically active species of a Group VIII noble metal. 19. A catalyst composition as in claim 18 wherein said noble metal is platinum. 20. A catalyst composition as in claim 18 wherein said noble metal is up to about 10 wt % of said catalyst composition. 21. A catalyst composition as in claim 19 wherein said noble metal is up to about 10 wt % of said catalyst composition. 22. A catalyst composition as in claim 18 wherein up to about 60 wt % alumina is present in said catalyst composition. 23. A hydroisomerization process comprising contacting one or more linear or substantially linear hydrocarbons under hydroisomerization conditions with a catalyst composition of claim 18.