초록 ▼

A method for shielding a metal substrate surface during the application of heat to the surroundings of the substrate which comprises. A liquid maskant composition is formed which comprises: a) at least one of a polycarbonate urethane diacrylate oligomer, a polycarbonate urethane dimethacrylate oligo

A method for shielding a metal substrate surface during the application of heat to the surroundings of the substrate which comprises. A liquid maskant composition is formed which comprises: a) at least one of a polycarbonate urethane diacrylate oligomer, a polycarbonate urethane dimethacrylate oligomer, a polycarbonate caprolactone urethane diacrylate oligomer, or a polycarbonate caprolactone urethane dimethacrylate oligomer; b) a reactive diluent capable of free radical polymerization; and c) a photoinitiator capable of generating free radicals when exposed to actinic radiation. The maskant composition is applied onto a surface of the substrate. The maskant composition is then exposed to sufficient actinic radiation to polymerize or crosslink the composition into a dried maskant. In use the dried maskant is heated on the substrate to a temperature of from about 400° F. to about 600° F. for from about 20 minutes to about 30 minutes, and then the maskant is removed.

대표청구항 ▼

1. A method for shielding a metal substrate surface during the application of heat to the surroundings of the substrate which comprises: I) providing a liquid maskant composition which comprises:a) at least one of a polycarbonate caprolactone urethane diacrylate oligomer, or a polycarbonate caprolac

1. A method for shielding a metal substrate surface during the application of heat to the surroundings of the substrate which comprises: I) providing a liquid maskant composition which comprises:a) at least one of a polycarbonate caprolactone urethane diacrylate oligomer, or a polycarbonate caprolactone urethane dimethacrylate oligomer;wherein the polycarbonate caprolactone urethane diacrylate oligomer or polycarbonate caprolactone urethane dimethacrylate oligomer has a formula: C-DX-DnCwherein:n=1-30D=a diisocyanate residueC=a residue of a hydroxy functional methacrylate or hydroxy functional acrylate capping agentY=a residue of a polycarbonate caprolactone diol with formula k=1-30m=1-20R═C2 to C8 alkyl group;R′═C2 to C8 alkyl group;b) a reactive diluent capable of free radical polymerization;c) a photoinitiator capable of generating free radicals when exposed to actinic radiation;II) applying the liquid maskant composition onto a surface of the substrate;III) exposing said liquid maskant composition to sufficient actinic radiation to polymerize or crosslink the composition into a dried maskant. 2. The method of claim 1 wherein the liquid maskant composition comprises the polycarbonate caprolactone urethane diacrylate oligomer. 3. The method of claim 1 wherein the liquid maskant composition comprises the polycarbonate caprolactone urethane dimethacrylate oligomer. 4. The method of claim 1 wherein the liquid maskant composition comprises from about 15 to about 85% of the polycarbonate caprolactone urethane diacrylate oligomer, or polycarbonate caprolactone urethane dimethacrylate oligomer. 5. The method of claim 1 wherein the liquid maskant composition comprises from about 20% by weight to about 50% by weight of the reactive diluent capable of free radical polymerization. 6. The method of claim 1 wherein the liquid maskant composition comprises from about 1% by weight to about 10% by weight of the photoinitiator. 7. The method of claim 1 wherein the liquid maskant composition further comprises up to about 15% by weight of a thickening agent. 8. The method of claim 1 wherein the liquid maskant composition further comprises up to about 5% by weight of one or more of heat stabilizers, UV-light stabilizers, free-radical scavengers, hindered amine light stabilizer compounds, dyes, pigments, surfactants, plasticizers, opacity-modifying agents, and combinations thereof. 9. The method of claim 1 wherein the reactive diluent capable of free radical polymerization comprises a vinyl containing monomer. 10. The method of claim 1 wherein the maskant composition is applied at a thickness of from about 0.005 inch to about 0.060 inch. 11. The method of claim 1 further comprising the subsequent step IV) of heating the substrate to a temperature of from about 400° F. to about 600° F. for from about 20 minutes to about 30 minutes. 12. The method of claim 11 further comprising the subsequent step V) of removing the dried maskant. 13. The method of claim 12 wherein the step V) of removing the dried maskant is conducted by peeling the dried maskant from the surface of the substrate. 14. The method of claim 12 wherein the step V) of removing the dried maskant is conducted by burning the dried maskant from the surface of the substrate. 15. A liquid maskant composition which comprises a) a polycarbonate caprolactone urethane diacrylate oligomer or polycarbonate caprolactone urethane dimethacrylate oligomer a having the formula: C-DX-DnCwherein:n=1-30D=a diisocyanate residueC=a residue of a hydroxy functional methacrylate or hydroxy functional acrylate capping agentY=a residue of a polycarbonate caprolactone diol with formula k=1-30m=1-20R═C2 to C8 alkyl group;R′═C2 to C8 alkyl group;b) a reactive diluent capable of free radical polymerization; andc) a photoinitiator capable of generating free radicals when exposed to actinic radiation. 16. The liquid maskant composition of claim 15 comprising the polycarbonate caprolactone urethane diacrylate oligomer. 17. The liquid maskant composition of claim 15 comprising the polycarbonate caprolactone urethane dimethacrylate oligomer.