초록 ▼

Magnetic calcium phosphate particles are provided including particles comprising iron oxide and calcium phosphate. A chitosan coating is present on the particles, wherein the particles are less than or equal to 1,000 nm, are magnetic and exhibit a positive charge in the range of 1 mVolts to 60 mVolt

Magnetic calcium phosphate particles are provided including particles comprising iron oxide and calcium phosphate. A chitosan coating is present on the particles, wherein the particles are less than or equal to 1,000 nm, are magnetic and exhibit a positive charge in the range of 1 mVolts to 60 mVolts. The particles are provided by preparing a calcium hydroxide solution and filtering the calcium hydroxide solution in a membrane filter. An iron chloride solution is formed and combined with the filtered calcium hydroxide solution. In addition, the phosphoric acid solution is combined with the combined solutions of iron chloride and calcium hydroxide, forming a mixture including particles comprising iron oxide and calcium phosphate.

대표청구항 ▼

1. A method of forming a mixture of magnetic iron oxide and calcium phosphate particles, comprising: preparing a calcium hydroxide solution in water;filtering said calcium hydroxide solution through a filter;forming an iron chloride solution comprising a mixture of Fe(II) and Fe(III) in water;combin

1. A method of forming a mixture of magnetic iron oxide and calcium phosphate particles, comprising: preparing a calcium hydroxide solution in water;filtering said calcium hydroxide solution through a filter;forming an iron chloride solution comprising a mixture of Fe(II) and Fe(III) in water;combining said iron chloride solution with said filtered calcium hydroxide solution so as to form an homogeneous solution of iron chloride and calcium hydroxide; andtitrating said homogeneous solution of iron chloride and calcium hydroxide with a phosphoric acid solution to a pH of 5 to 7, wherein said phosphoric acid solution includes phosphoric acid dissolved in water and a polysaccharide, and the phosphoric acid solution is filtered prior to titration using a filter having a pore size of having a pore size of 0.45 μm or less; andstirring the titrated mixture so as to form a mixture of magnetic iron oxide nanoparticles of the formula Fe2O3 and Fe3O4 comprising polysaccharide, and calcium phosphate of the formula Cax(PO4)y wherein the ratio of x:y is in the range of 1 to 3; andcombining said mixture of magnetic nanoparticles with a solution of organic acid and chitosan and heating said mixture of magnetic nanoparticles and said solution of organic acid and chitosan to a temperature of 40° C. to 100° C. from 8 to 24 hours to coat the mixture of magnetic nanoparticles, said coated magnetic nanoparticles having an average particle size ranging from 200 nm to 400 nm with a polydispersity ranging from 0.01 to 0.5 and a zeta potential of 1 to 60 mV. 2. The method of claim 1, wherein said forming an iron chloride solution comprises dissolving FeCl2.4H2O to form an Fe(II) solution, dissolving FeCl3.6H2O to form an Fe(III), and combining said Fe(II) solution with Fe(III) solution. 3. The method of claim 1, wherein said filter for said calcium hydroxide solution exhibits a pore size of 0.45 μm or less. 4. The method of claim 1, further comprising agitating said combined solution of said chitosan and said organic acid and said magnetic nanoparticles. 5. The method of claim 1, further comprising washing said nanoparticles. 6. The method of claim 1, further comprising lyophilizing said nanoparticles. 7. The method of claim 1, wherein said calcium hydroxide solution is elevated to a temperature of 40° C. 8. The method of claim 1, wherein said phosphoric acid solution is added to said combined solutions of iron chloride and calcium hydroxide until the pH of said combined solutions is 5.0. 9. The method of claim 1, wherein said polysaccharide comprises chitosan. 10. The method of claim 1, wherein said organic acid comprises an aliphatic carboxylic acid.