Break resistant and shock resistant sapphire plate
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
C04B-035/115
C04B-041/87
C23C-016/513
C23C-014/34
H05K-005/03
C04B-041/50
C04B-041/00
C23C-014/08
C23C-016/40
C30B-029/20
출원번호
US-0453102
(2014-08-06)
등록번호
US-9750150
(2017-08-29)
발명자
/ 주소
Beckmann, Rudolf
Nolker, Sabine
출원인 / 주소
APPLE INC.
대리인 / 주소
Brownstein Hyatt Farber Schreck, LLP
인용정보
피인용 횟수 :
0인용 특허 :
26
초록▼
A break resistant sapphire plate and a corresponding production process. The sapphire plate may include a planar sapphire substrate, and at least one shock absorbing layer arranged on a surface of the substrate. The shock absorbing layer may have a thickness of between 0.1% to 10% of the thickness o
A break resistant sapphire plate and a corresponding production process. The sapphire plate may include a planar sapphire substrate, and at least one shock absorbing layer arranged on a surface of the substrate. The shock absorbing layer may have a thickness of between 0.1% to 10% of the thickness of the substrate. The production process for producing the sapphire plate may include providing a planar sapphire substrate, and coating at least one surface of the substrate with a shock absorbing layer. The shock absorbing layer may include a layer thickness between 0.1% to 10% of the thickness of the substrate.
대표청구항▼
1. A sapphire plate, comprising: a planar sapphire substrate; andat least one shock absorbing layer selectively adhered to portions of a surface of the planar sapphire substrate, wherein the shock absorbing layer has:a layer thickness between 0.1% to 10% of a thickness of the substrate; andat least
1. A sapphire plate, comprising: a planar sapphire substrate; andat least one shock absorbing layer selectively adhered to portions of a surface of the planar sapphire substrate, wherein the shock absorbing layer has:a layer thickness between 0.1% to 10% of a thickness of the substrate; andat least 50 wt.-% of amorphous aluminum oxide (Al2O3). 2. The sapphire plate of claim 1, wherein the shock absorbing layer thickness is one of: 0.5% to 5%, 0.8% to 3%, 1% to 2%, or 1.2% to 1.5% of the thickness of the substrate. 3. The sapphire plate of claim 1, wherein the thickness of the sapphire substrate is one of: 200 μm to 2 mm, 300 μm to 1.5 mm, 500 μm to 1 mm or 600 μm to 800 μm. 4. The sapphire plate of claim 1, wherein the shock absorbing layer thickness is one of at least: 1 μm, 1.5 μm, 2 μm, 3 μm, 4 μm or 5 μm. 5. The sapphire plate of claim 1, further comprising a connection positioned between the sapphire substrate and the shock absorbing layer, perpendicular to an axis of the sapphire substrate, wherein the connection has a smaller tensile strength than at least one of the sapphire substrate or the shock absorbing layer. 6. The sapphire plate of claim 1, wherein the coated surface of the sapphire substrate substantially coincides with the crystalline A axis of sapphire. 7. The sapphire plate of claim 1, wherein the shock absorbing layer consists of aluminum oxide (Al2O3). 8. The sapphire plate of claim 1, wherein the shock absorbing layer comprises at least one of: 0 to 5 wt.-% of carbon, 0 to 10 wt.-% of hydrogen, and 0 to 5 wt.-% of nitrogen. 9. The sapphire plate of claim 1, wherein the coated surface of the sapphire substrate substantially coincides with the crystalline C axis of sapphire. 10. The sapphire plate of claim 1, wherein the shock absorbing layer is substantially transparent to electromagnetic radiation in a visible wavelength. 11. The sapphire plate of claim 1, wherein the sapphire substrate includes a first thermal expansion coefficient, and the shock absorbing layer includes a second thermal expansion coefficient, distinct from the first thermal expansion coefficient of the sapphire substrate. 12. A sapphire composite, comprising: a sapphire component exhibiting a first tensile strength; anda layer having a thickness of 0.1% to 10% of a thickness of the sapphire component and exhibiting a second tensile strength and coupled to the sapphire component along an interface defined between the sapphire component and the layer, wherein:a tensile strength of the composite at the interface is less than the first and second tensile strengths; andthe layer has at least 50 wt.-% of amorphous aluminum oxide (Al2O3). 13. The sapphire composite of claim 12, wherein the layer is configured to distribute force received at the layer away from the sapphire component. 14. The sapphire composite of claim 12, wherein: the sapphire component has a first hardness; andthe layer has a second hardness that differs from the first hardness. 15. The sapphire composite of claim 12, wherein the layer is coupled to the sapphire component via at least one of: a sputtering process; anda plasma-assisted CVD process. 16. A sapphire composite, comprising: a sapphire structure;a layer adhered directly to the sapphire structure and having at least 50 wt.-% of aluminum oxide (Al2O3) and a thickness between 0.1% to 10% of a thickness of the substrate;and an array of connections positioned along an interface between the sapphire structure and the layer, wherein the layer is affixed to the sapphire structure at the array of connections. 17. The sapphire composite of claim 16, wherein each of the array of connections defines a localized region of the layer that is affixed to the sapphire structure. 18. The sapphire composite of claim 16, wherein the layer is configured to deform. 19. The sapphire composite of claim 16, wherein the layer is separable from the sapphire structure in response to an impact force. 20. The sapphire composite of claim 16, wherein a thickness of the layer is at least 1% of a thickness of the sapphire substrate.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (26)
Kimock Fred M. (Macungie PA) Knapp Bradley J. (Allentown PA) Finke Steven J. (Kutztown PA) Galdieri John V. (New Tripoli PA), Abrasion wear resistant coated substrate product.
Buhay, Harry; Finley, James J.; Thiel, James P.; Lehan, John P., Coated articles having a protective coating and cathode targets for making the coated articles.
Buhay, Harry; Finley, James J.; Thiel, James P.; Lehan, John P., Method of making coated articles having an oxygen barrier coating and coated articles made thereby.
Buhay, Harry; Finley, James J.; Thiel, James P.; Lehan, John P., Methods of changing the visible light transmittance of coated articles and coated articles made thereby.
Klun, Thomas P.; Qiu, Zai-Ming; Hofmann, Gerald R.; Viner, Andrew S.; Benz, Oscar S.; Iyer, Suresh; Clark, Gregory D.; Burton, Craig A.; Pellerite, Mark J., Respirator, welding helmet, or face shield that has low surface energy hard-coat lens.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.