Dental ceramic article, process of production and use thereof
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
C04B-035/48
A61C-013/00
A61C-008/00
A61C-005/10
A61K-006/00
A61K-006/02
C04B-035/486
C04B-035/632
C04B-035/634
C04B-041/00
C04B-041/50
C04B-041/85
A61C-005/77
C04B-111/00
C04B-111/82
출원번호
US-0003409
(2012-03-16)
등록번호
US-9758435
(2017-09-12)
우선권정보
EP-11158584 (2011-03-17)
국제출원번호
PCT/US2012/029333
(2012-03-16)
§371/§102 date
20130905
(20130905)
국제공개번호
WO2012/125885
(2012-09-20)
발명자
/ 주소
Schechner, Gallus
Hauptmann, Holger
Dittmann, Rainer K.
Schnagl, Hans R.
출원인 / 주소
3M Innovative Properties Company
인용정보
피인용 횟수 :
0인용 특허 :
73
초록▼
The present disclosure relates to a dental ceramic article comprising ceramic components, the ceramic components having ZrO2 and Al2O3 and at least one component comprising Mn, Er or mixtures thereof, Al2O3 being present in an amount below about 0.15 wt.-% with respect to the weight of the ceramic a
The present disclosure relates to a dental ceramic article comprising ceramic components, the ceramic components having ZrO2 and Al2O3 and at least one component comprising Mn, Er or mixtures thereof, Al2O3 being present in an amount below about 0.15 wt.-% with respect to the weight of the ceramic article. The present disclosure relates also to kit of parts comprising a ceramic article and a coloring solution and processes for producing a dental ceramic article.
대표청구항▼
1. A pre-sintered dental ceramic article comprising ceramic components, the ceramic components comprising ZrO2 and Al2O3 and colouring components comprising ions or oxides of Mn, Er, or mixtures thereof, wherein the pre-sintered dental ceramic article has: Al2O3: from 0.01 to about 0.12 wt.-%;Er2O3:
1. A pre-sintered dental ceramic article comprising ceramic components, the ceramic components comprising ZrO2 and Al2O3 and colouring components comprising ions or oxides of Mn, Er, or mixtures thereof, wherein the pre-sintered dental ceramic article has: Al2O3: from 0.01 to about 0.12 wt.-%;Er2O3: from about 0.010 wt.-% to about 1.5 wt.-%;Pr6O11: from about 0 wt.-% to about 0.1 wt.-%;MnO2: from about 0.001 wt.-% to about 0.01 wt.-%; andFe2O3: 0 wt.-% to about 0.1 wt.-%, wherein wt.-% is with respect to the weight of the ceramic article. 2. The dental ceramic article of claim 1, comprising a stabilizer selected from oxides of Y, Mg, Ca, Ce, La and mixtures thereof. 3. The dental ceramic article of claim 1, wherein the ceramic article has the shape of a dental support structure, a dental crown, a dental bridge, a dental facing, an inlay, an inlay, a mill blank, an implant or an abutment. 4. The dental ceramic article of claim 1, wherein the dental ceramic is contained in a frame or a holding device. 5. The dental ceramic article of claim 1 being characterized by at least one of the following features: density: from about 2.4 to about 3.7 g/cm3; orporosity: from about 40 to about 60 vol.-%. 6. The dental ceramic article according to claim 1, wherein the dental ceramic article comprises pores having diameters from about 50 nm to about 150 nm. 7. The dental ceramic article according to claim 1, wherein Al2O3 is present in an amount below about 0.1 wt.-% with respect to the weight of the ceramic components. 8. A sintered dental ceramic article comprising ceramic components, the ceramic components comprising ZrO2 and Al2O3 and colouring components comprising ions or oxides of Mn, Er, or mixtures thereof, wherein Al2O3 is present in an amount from about 0.01 to about 0.15 wt. % with respect to the weight of the ceramic components and wherein the sintered dental ceramic article has: ZrO2+HfO2: from about 80 wt.-% to about 98 wt.-%;Al2O3: from 0.01 to about 0.12 wt.-%;Er2O3: from about 0.010 wt.-% to about 1.5 wt.-%;Pr6O11: from about 0 wt.-% to about 0.1 wt.-%;MnO2: from about 0.001 wt.-% to about 0.01 wt.-%; andFe2O3: 0 wt.-% to about 0.1 wt.-%,wherein wt.-% is with respect to the weight of the sintered dental ceramic article and the sintered dental ceramic article has at least one of the following features:breaking resistance: at least about 400 MPa;density: from about 5.9 to about 6.1 g/cm3 orfluorescence emission in the region of the visible light. 9. A process for producing a dental ceramic article, the process comprising the step of treating a ceramic article with a colouring solution, wherein the ceramic article comprises ZrO2 and Al2O3, and the colouring solution comprises at least one colouring component comprising ions selected from Er, Mn and mixtures thereof and sintering the treated ceramic article such that the sintered dental ceramic article has:ZrO2+HfO2: from about 80 wt.-% to about 98 wt.-%;Al2O3: from 0.01 to about 0.12 wt.-%;Er2O3: from about 0.010 wt.-% to about 1.5 wt.-%;Pr6O11: from about 0 wt.-% to about 0.1 wt.-%;MnO2: from about 0.001 wt.-% to about 0.01 wt.-%; andFe2O3: 0 wt.-% to about 0.1 wt.-%,wherein wt.-% is with respect to the weight of the sintered dental ceramic article. 10. The process of claim 9 wherein the step of sintering the ceramic article after treatment with the colouring solution is at a temperature within a range from about 1300° C. to about 1550° C., optionally with a dwell time from about 0 to about 10 h. 11. A process for producing a dental ceramic article, the process comprising the steps of mixing at least one colouring component with ceramic components thereby obtaining a mixture, the at least one colouring component comprising ions or oxides selected from Er, Mn and mixtures thereof, the ceramic components comprising ZrO2 and Al2O3, shaping the mixture to form a ceramic article and optionally sintering the ceramic articlewherein the ceramic article has:ZrO2+HfO2: from about 80 wt.-% to about 98 wt.-%;Er2O3: from about 0.010 wt.-% to about 1.5 wt.-%;Pr6O11: from about 0 wt.-% to about 0.1 wt.-%;MnO2: from about 0.001 wt.-% to about 0.01 wt.-%; andFe2O3: 0 wt.-% to about 0.1 wt.-%,wherein wt.-% is with respect to the weight of the dental ceramic article.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (73)
Kreis Gerhard (Munich DEX) Wegehaupt Karl-Heinrich (Burghausen DEX), Addition of Si-bonded hydrogen to an aliphatic multiple bond.
Nakabayashi Nobuo (Chiba JPX) Honda Narimichi (Yamaguchi JPX) Nakamura Mitsuo (Tokyo JPX) Sakashita Takeshi (Yamaguchi JPX), Adhesive for ceramics and processes for the bonding of ceramics using same.
Fox ; Frederick J. ; Noren ; Richard W. ; Krankkala ; George E., Catalyst for condensation of hydrolyzable silanes and storage stable compositions thereof.
Fitch, John; Moritz, Jan; Sargeant, Steven J.; Shimizu, Yuji; Nishigaki, Yasuo, Coated film with exceptional embossing characteristics and method for producing it.
Elsbernd, Cheryl L. S.; Terrazas, Michael S.; Martin, Steven J.; Pellerite, Mark J., Compositions comprising fluorinated silanes and compressed fluid CO2.
Liu Junkang Jacob ; Leir Charles M. ; Moore George G. I. ; Sherman Audrey A. ; Everaerts Albert I. ; Boulos Marie A., Cure-on-demand, moisture-curable compositions having reactive silane functionality.
Joel D. Oxman ; Larry D. Boardman, Hydrosilation reaction utilizing a (cyclopentadiene)(sigma-aliphatic) platinum complex and a free radical photoinitiator.
Yoshida Masahiro (Hidaka JPX) Kimura Nobuo (Kanagawa JPX) Okamura Hiromichi (Ibaraki JPX), Ivory-colored zirconia sintered body, process for its production and its use.
Yoshida Masahiro (Hidaka JPX) Kimura Nobuo (Oiso JPX) Okamura Hiromichi (Fujishiro JPX), Ivory-colored zirconia sintered body, process for its production and its use.
Yamana Masayuki,JPX ; Nakamae Yasushi,JPX ; Sakashita Hirotoshi,JPX ; Kashiwagi Masato,JPX, Mold release agent, cured film obtained from said mold release agent, and molding method using said mold release agent.
Sato Shinichi (Annaka JPX) Oohasi Morio (Annaka JPX) Inomata Hiroshi (Annaka JPX), Mold releasing resin composition and molding of curable resin using the same.
Sadoun Michael (3 avenue Sverine 92400 Courbevoie FRX) Decker Alain (113 ; avenue Gabriel Pri 91700 Ste Genevieve des Bois FRX), Orthodontic bracket made from zirconium oxide.
Boldridge ; Jr. Austin (Freehold NJ) Buell Scott (Harpers Ferry WV) Graham James M. (Westminster MD), Parallel encoded piezoelectric keyboard switch and array.
Merrill, William W.; Jonza, James M.; Benson, Jr., Olester; Ouderkirk, Andrew J.; Weber, Michael F., Post-formable multilayer optical films and methods of forming.
Tyszblat Michle (3 avenue Sverine 92400 Courbevoie FRX), Process for the preparation of a dental prosthesis and the prosthesis produced by said process.
Tyszblat Michle (3 avenue Sverine 92400 Courbevoie FRX), Process for the preparation of a dental prosthesis by slight solid phase fritting of a metal oxide based infrastructure.
Hechler Wolfgang (Lautertal DEX) Dietz Johann (Bickenbach DEX) Weigand Manfred (Weiterstadt DEX) Osterried Karl (Dieburg DEX), Process for the production of a coated system.
Mazurek Mieczyslaw H. (St. Paul MN) Kantner Steven S. (St. Paul MN) Leir Charles M. (St. Paul MN) Bogaert Yvan A. (Gent MN BEX) Galkiewicz Robert K. (St. Paul MN) Sherman Audrey A. (St. Paul MN), Radiation-curable silicone elastomers and pressure sensitive adhesives.
Breen, Tricia L.; Kosbar, Laura L.; Mastro, Michael P.; Nunes, Ronald W., Vapor phase surface modification of composite substrates to form a molecularly thin release layer.
Nakayama Susumu (Okayama JPX) Ichimori Terumitsu (Saitama JPX) Mino Tadahiro (Okayama JPX) Ayuzawa Nobuo (Hyogo JPX), Zirconia-based sinter, process for producing the same, gringing part material, and bracket material for dental correctio.
Yoshihiro Kobayashi JP; Nobuhiko Matsushita JP, Zirconium ceramic material, optical fiber connector member using the same, and method of producing the same.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.