초록 ▼

Inventive manufacture of CrB2—Al2O3 composites is based on pressureless sintering. According to typical inventive practice, CrB2 powder and Al2O3 powder are mixed together in selected volumetric proportions so that the volume of the CrB2 does not exceed 50% of the overall volume of the CrB2—Al2O3 mi

Inventive manufacture of CrB2—Al2O3 composites is based on pressureless sintering. According to typical inventive practice, CrB2 powder and Al2O3 powder are mixed together in selected volumetric proportions so that the volume of the CrB2 does not exceed 50% of the overall volume of the CrB2—Al2O3 mixture. The CrB2—Al2O3 mixture is shaped into a green body. The green body is pressureless sintered in a non-oxidizing atmosphere at a firing temperature in the approximate range between 1600° C. and 2050° C. The present invention succeeds in preparing, via pressureless sintering, a proportionality-associated range of compositions in the CrB2—Al2O3 system, which is a potentially “advanced” ceramic system. A typical inventively fabricated CrB2—Al2O3 composite is inventively configured in a complex shape, and has “advanced” material (e.g., mechanical) properties that are favorable for a contemplated application. Inventive manufacture of ceramic-ceramic composites is thus dually attributed, and uncommonly so, with complex shape-ability and advanced capability.

대표청구항 ▼

1. A method for making a chromium diborid-aluminum oxide two-phase ceramic composite body, the method comprising: mixing chromium diboride powder and aluminum oxide powder to produce a mixture, said mixture consisting of said chromium diboride and said aluminum oxide, wherein said chromium diboride

1. A method for making a chromium diborid-aluminum oxide two-phase ceramic composite body, the method comprising: mixing chromium diboride powder and aluminum oxide powder to produce a mixture, said mixture consisting of said chromium diboride and said aluminum oxide, wherein said chromium diboride constitutes a percentage by volume of said mixture in the range between 21% and 30%, and said aluminum oxide constitutes a percentage by volume of said mixture in the range between 70% and 79%;shaping said mixture to form a green body, said green body including said chromium diboride and said aluminum oxide;pressureless sintering said green body in a non-oxidizing atmosphere at a firing temperature in the range between 1600° C. and 1699° C., the pressureless sintered said green body including said chromium diboride and said aluminum oxide;wherein said pressureless sintering of said green body is performed to obtain a chromium diboride-aluminum oxide two-phase ceramic composite that is fully dense. 2. The method of claim 1 wherein the method further comprises milling said mixture prior to said shaping. 3. The method of claim 1 wherein said non-oxidizing atmosphere is one of a vacuum, an inert gas, and a reducing gas. 4. The method of claim 1 wherein said shaping includes using at least one shaping technique selected from the group consisting of die pressing, cold isostatic pressing, extrusion, slip casting, and injection molding. 5. The method of claim 1 wherein the method further comprises cooling the pressureless sintered said green body. 6. The method of claim 5 wherein the method further comprises at least one of: machining said green body prior to said pressureless sintering; andmachining the cooled pressureless sintered said green body. 7. The method of claim 1 wherein said chromium diboride constitutes a percentage by volume of said mixture in the range between 22% and 30%, and said aluminum oxide constitutes a percentage by volume of said mixture in the range between 70% and 78%. 8. The method of claim 1 wherein said chromium diboride constitutes a percentage by volume of said mixture in the range between 23% and 30%, and said aluminum oxide constitutes a percentage by volume of said mixture in the range between 70% and 77%. 9. A method for making a CrB2—Al2O3 two-phase ceramic composite article, the method comprising: preparing a blend of chromium diboride powder and aluminum oxide powder, said blend consisting of said chromium diboride and said aluminum oxide,wherein the prepared said blend of chromium diboride powder and aluminum oxide powder is in volumetric proportions in the range between 21% CrB2-79% Al2O3 and 30% CrB2-70% Al2O3;shaping said blend into a green body, said green body including said chromium diboride and said aluminum oxide;densifying said green body in the absence of applied pressure in a non-oxidizing atmosphere, said densifying of said green body including heating said green body in a furnace to a temperature in the range between 1600° C. and 1699° C., the densified said green body including said chromium diboride and said aluminum oxide;wherein said densifying of said green body is performed to obtain a chromium diboride-aluminum oxide two-phase ceramic composite that is fully dense. 10. The method of claim 9 wherein said shaping of said blend includes cold isostatic pressing. 11. The method of claim 9 wherein said non-oxidizing atmosphere is either a vacuous atmosphere or a gaseous atmosphere. 12. The method of claim 11 wherein said gaseous atmosphere is either an inert gaseous atmosphere or a reducing gaseous atmosphere. 13. The method of claim 9 wherein the method further comprises at least one of: machining said green body prior to said densifying of said green body; andmachining the densified said green body. 14. The method of claim 9 wherein the prepared said blend of chromium diboride powder and aluminum oxide powder is in volumetric proportions in the range between 22% CrB2-78% Al2O3 and 30% CrB2-70% Al2O3. 15. The method of claim 9 wherein the prepared said blend of chromium diboride powder and aluminum oxide powder is in volumetric proportions in the range between 23% CrB2-77% Al2O3 and 30% CrB2-70% Al2O3.